US4019969A
Expired / Lapsed
US
⏱️ 0.0 years remaining
Method of manufacturing catalytic tubes with wall-supported catalyst, particularly for steam reforming of hydrocarbons and methanation
Assignee: Instytut Nawozow Sztucznych
•
Filing: 1975-11-17
•
Granted: 1977-04-26
•
Expires: 1995-11-17
Abstract
Abstract This invention relates to a method of manufacturing catalytic tubes with wall-supported catalyst particularly for steam reforming of hydrocarbons and methanation, wherein at first a porous layer of metal sponge is laid on the tube surface by the known method of electrolysis, wherein said tube is permanently filled with electrolyte and a shield mounted on the anode is raised step by step or in continuous manner during electrolysis. Said tube constitutes a cathode during electrolysis, and a metal bar placed in the axis of the tube forms an anode. The tube is roasted at a temperature of 800 DEG -1200 DEG C, then salts are introduced into the sponge, which after roasting yield metal oxides irreducible in the presence of a hydrogen and salts, which yield reducible metal oxides, and coating the layer with salts is performed by known methods using aqueous solutions of salts, and after coating the roasting is carried out.
Inventors
- 👤 Andrzej Golebiowski
- 👤 Stanislawa Paluch
- 👤 Zdzislaw Janecki
- 👤 Alfred Polanski
- 👤 Waclaw Hennel
- 👤 Jerzy Zielinski
- 👤 Cezary Warzec
- 👤 Wojciech Lisowski
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-24 20:44
CPC Classifications
B; B01; B01J; B01J37/00; B01J37/02; B01J37/0215; B01J37/0225; B01J37/024; B01J37/34; B01J37/348; C; C01; C01B; C01B3/00; C01B3/02; C01B3/32; C01B3/34; C01B3/38; C01B3/384; C01B3/40; C07; C07C; C07C1/00; C07C1/02; C07C1/04; C07C1/0425; C07C1/0445; C25; C25D; C25D7/00; C25D7/04; C01B2203/00; C01B2203/10; C01B2203/1005; C01B2203/1035; C01B2203/1041; C01B2203/1047; C01B2203/1052; C01B2203/1064; C07C2523/00; C07C2523/70; C07C2523/74; C07C2523/755; Y; Y02; Y02P; Y02P20/00; Y02P20/50; Y02P20/52
Claims Analysis
Total Claims: 18
Claim 1
Independent Claim
76 words
A method of manufacturing a catalytic tube with wall-supported catalyst particularly for steam reforming of hydrocarbons and methanation, comprising depositing a porous coating of metal sponge on the tube surface by electrolysis, impregnating the sponge with aqueous solutions of salts which after roasting yield metal oxides irreducible in the presence of hydrogen and of salts, which yield reducible metal oxides, and roasting the impregnated sponge coated tube to form metal oxides deposited in said metal sponge.
Claim 2
Independent Claim
76 words
A method of manufacturing a catalytic tube with wall-supported catalyst particularly for steam reforming of hydrocarbons and methanation, comprising depositing a porous coating of metal sponge on the tube surface by electrolysis, impregnating the sponge with aqueous solutions of salts which after roasting yield metal oxides irreducible in the presence of hydrogen and of salts, which yield reducible metal oxides, and roasting the impregnated sponge coated tube to form metal oxides deposited in said metal sponge.
Claim 3
Dependent Claim
55 words
The method of claim 1, in which the tube constitutes the cathode during electrolysis, and a metal bar placed in the axis of the tube constitutes the anode, wherein said tube is permanently filled with electrolyte and a shield mounted on the anode is raised step by step or in a continuous manner during electrolysis.
Claim 4
Dependent Claim
24 words
The method of claim 1, wherein the electrolyte circulates between a thermostabilizing tank and the tube on which the porous metal sponge is deposited.
Claim 5
Dependent Claim
32 words
The method of claim 1, wherein nickel is the metal from which the sponge layer is prepared, and the electrolysis is performed in the range of temperatures from 15° to 20° C.
Claim 6
Dependent Claim
50 words
The method of claim 1, in which the tube constitutes the cathode during electrolysis, and a metal bar placed in the axis of the tube constitutes the anode, wherein the tube as well as said bar are arranged vertically or obliquely, and the electrolyte level is raised progressively during electrolysis.
Claim 7
Dependent Claim
48 words
The method of claim 1, wherein during preparation of the first portion of the sponge layer, directly adherent to the wall, such conditions of electrolysis are used as to obtain a sponge of higher density than the sponge obtained when preparing the remaining portion of the sponge layer.
Claim 8
Dependent Claim
28 words
The method of claim 1, wherein the tube is roasted at a temperature of 800°-1200° C after preparing the metal sponge but before introducing salts into this sponge.
Claim 9
Dependent Claim
20 words
The method of claim 1, wherein the electrolysis proceeds with current densities ranging from 10 to 60 A/dcm 2 .
Claim 10
Dependent Claim
18 words
The method of claim 1, wherein the electrolyte pH-value is kept at a level of 2.2-6.8 during electrolysis.
Claim 11
Dependent Claim
79 words
The method of claim 2 wherein the electrolyte circulates between a thermostabilizing tank and the tube; the tube and the bar are arranged vertically or obliquely; the electrolysis conditions are selected so as to obtain a first portion of sponge layer directly adherent to the wall of higher density than remaining portion of the sponge layer; the current density ranges from 10 to 60 A/dcm 2 ; and the pH is maintained at a level of 2.2-6.8 during electrolysis.
Claim 12
Dependent Claim
28 words
The method of claim 10, wherein the tube is roasted at a temperature of 800°-1200° C after preparing the metal sponge but before introducing salts into this sponge.
Claim 13
Dependent Claim
32 words
The method of claim 10, wherein nickel is the metal from which the sponge layer is prepared, and the electrolysis is performed in the range of temperatures from 15° to 20° C.
Claim 14
Dependent Claim
32 words
The method of claim 11, wherein nickel is the metal from which the sponge layer is prepared, and the electrolysis is performed in the range of temperatures from 15° to 20° C.
Claim 15
Dependent Claim
10 words
The catalytic tube obtained by the method of claim 1.
Claim 16
Dependent Claim
10 words
The catalytic tube obtained by the method of claim 4.
Claim 17
Dependent Claim
10 words
The catalytic tube obtained by the method of claim 10.
Claim 18
Dependent Claim
10 words
The catalytic tube obtained by the method of claim 11.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1980-04-25 | 1980-10-25 | 1981-04-26 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1984-04-25 | 1984-10-25 | 1985-04-26 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1988-04-25 | 1988-10-25 | 1989-04-26 | $7700.00 | Window Closed / Lapsed |