US4019920A
Expired / Lapsed
US
⏱️ 0.0 years remaining
Gypsum set accelerator
Assignee: National Gypsum Co
•
Filing: 1975-05-23
•
Granted: 1977-04-26
•
Expires: 1995-05-23
Abstract
Abstract A gypsum set accelerator, produced by compression milling a mixture of ground gypsum rock and starch, and the addition thereof to an aqueous slurry of settable calcined gypsum such as in the forming of paper-covered gypsum wallboard.
Inventors
- 👤 Edward A. Burkard
- 👤 Donald A. Kossuth
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-05 19:09
CPC Classifications
C; C04; C04B; C04B28/00; C04B28/14; C04B20/00; C04B20/02; C04B20/026; C04B28/145; C04B2111/00; C04B2111/00474; C04B2111/00612; C04B2111/0062
Claims Analysis
Total Claims: 3
Claim 1
Independent Claim
170 words
The method of making gypsum wallboard comprising the steps of compression milling a mixture of from about 1:3 to about 3:1 parts by weight of calcium sulfate dihydrate and starch for a period of time sufficient to reduce the particle size to provide a surface area of about 10,000 to about 20,000 cm 2 /gm as measured by a Fisher Sub-Sieve Sizer, mixing said milled mixture into an aqueous slurry comprising the wallboard forming ingredients including a major portion of calcined gypsum and a minor portion water of hydration, fiber reinforcement and density reducing agent, said slurry also including excess water whereby the slurry can be suitably formed, said milled mixture being only separate additive for accelerating the setting and for providing the necessary additional bonding strength needed by the settable gypsum to bond itself to paper cover sheets, disposing said slurry onto paper cover sheets, forming said wallboards of said slurry and paper cover sheets, maintaining said wallboard form while said slurry sets and hardens, and drying said wallboard.
Claim 2
Independent Claim
170 words
The method of making gypsum wallboard comprising the steps of compression milling a mixture of from about 1:3 to about 3:1 parts by weight of calcium sulfate dihydrate and starch for a period of time sufficient to reduce the particle size to provide a surface area of about 10,000 to about 20,000 cm 2 /gm as measured by a Fisher Sub-Sieve Sizer, mixing said milled mixture into an aqueous slurry comprising the wallboard forming ingredients including a major portion of calcined gypsum and a minor portion water of hydration, fiber reinforcement and density reducing agent, said slurry also including excess water whereby the slurry can be suitably formed, said milled mixture being only separate additive for accelerating the setting and for providing the necessary additional bonding strength needed by the settable gypsum to bond itself to paper cover sheets, disposing said slurry onto paper cover sheets, forming said wallboards of said slurry and paper cover sheets, maintaining said wallboard form while said slurry sets and hardens, and drying said wallboard.
Claim 3
Dependent Claim
39 words
The method of claim 1 wherein about 5 lbs. of said milled mixture of about 25 to 75% land plaster and about 25 to 75% starch is added to said aqueous slurry per 1650 lbs. of wallboard core produced.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1980-04-25 | 1980-10-25 | 1981-04-26 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1984-04-25 | 1984-10-25 | 1985-04-26 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1988-04-25 | 1988-10-25 | 1989-04-26 | $7700.00 | Window Closed / Lapsed |