Method of manufacturing α-alumina
Assignee: Robert Bosch GmbH
•
Filing: 1974-06-24
•
Granted: 1977-04-26
•
Expires: 1994-06-24
Abstract
Abstract A method of manufacturing α-alumina with a degree of purity of at least 98% which has a high sintering activity. The α-alumina contains at least 98% α-Al 2 O 3 and not more than 0.1% Na (calculated as Na 2 O), and not more than 0.1% Ti (calculated as TiO 2 ). The α-alumina also contains between 0.03% and 2% of Fe 2 O 3 and/or Cr 2 O 3 . The α-alumina is formed by first fine grinding and then calcining, preferably at a temperature between about 1120° C and 1350° C, an aluminum hydroxide and/or hydrated aluminum oxide. The α-alumina is then cooled and finely ground to provide an α-alumina having excellent sintering activity.
Inventors
- 👤 Friedrich Esper
- 👤 Karin Bethge
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-27 04:01
CPC Classifications
C; C04; C04B; C04B35/00; C04B35/01; C04B35/10; C04B35/111; C01; C01F; C01F7/00; C01F7/02; C01F7/44; C01F7/441; C01F7/442; C01P; C01P2006/00; C01P2006/10
Claims Analysis
Total Claims: 10
Claim 1
Independent Claim
205 words
A process for preparing a finely ground α-alumina with a degree of purity of at least 98% consisting of a. grinding a mixture of (i) at least one alumina source material selected from the group consisting of aluminum hydroxide and hydrated alumina oxide, and (ii) at least one calcination auxilary agent selected from the group consisting of Fe 2 O 3 and Cr 2 O 3 in an amount of between 0.03% and 2% by weight based on the total Al 2 O 3 , to produce an admixture of said alumina souce material and said calcination auxiliary agent ground to a grain size of not more than 0.4 μm which corresponds to a specific surface of at least 5 m 2 /g, said alumina source material containing not more than 0.1% Na, calculated as Na 2 O and not more than 0.1% Ti, calculated as TiO 2 , b. calcining said admixture at a temperature of between about 1120° C and 1350° C until said alumina source material is converted into α-alumina with a degree of purity of at least 98%, and c. cooling said calcined α-alumina and then finely grinding said calcined α-alumina to produce a finely ground α-alumina having excellent sintering activity.
Claim 2
Dependent Claim
205 words
A process for preparing a finely ground α-alumina with a degree of purity of at least 98% consisting of a. grinding a mixture of (i) at least one alumina source material selected from the group consisting of aluminum hydroxide and hydrated alumina oxide, and (ii) at least one calcination auxilary agent selected from the group consisting of Fe 2 O 3 and Cr 2 O 3 in an amount of between 0.03% and 2% by weight based on the total Al 2 O 3 , to produce an admixture of said alumina souce material and said calcination auxiliary agent ground to a grain size of not more than 0.4 μm which corresponds to a specific surface of at least 5 m 2 /g, said alumina source material containing not more than 0.1% Na, calculated as Na 2 O and not more than 0.1% Ti, calculated as TiO 2 , b. calcining said admixture at a temperature of between about 1120° C and 1350° C until said alumina source material is converted into α-alumina with a degree of purity of at least 98%, and c. cooling said calcined α-alumina and then finely grinding said calcined α-alumina to produce a finely ground α-alumina having excellent sintering activity.
Claim 3
Dependent Claim
34 words
The process of claim 1 wherein the said admixture is ground to a grain size of not more than 0.2 μm which corresponds to a specific surface of at least 10 m 2 /g.
Claim 4
Dependent Claim
38 words
The process of claim 1 wherein the said admixture contains a total of said calcination auxiliary agent in an amount between 0.05 and 0.2% and wherein the α-alumina product having excellent sintering activity contains at least 98% α-alumina.
Claim 5
Dependent Claim
17 words
The process of claim 3 wherein said admixture also contains MgO in an amount up to 0.5%.
Claim 6
Dependent Claim
34 words
The process of claim 4, wherein said admixture is prepared by mixing said alumina oxide source material with said MgO and said calcination auxiliary agent and then finely grinding to form a homogeneous admixture.
Claim 7
Dependent Claim
17 words
The process of claim 1 wherein said admixture also contains MgO in an amount up to 0.5%.
Claim 8
Dependent Claim
29 words
The process of claim 1 wherein said admixture is prepared by mixing said source material with said calcination auixiliary agent and then finely grinding to form a homogeneous admixture.
Claim 9
Dependent Claim
97 words
The process of claim 1 wherein said admixture is prepared by finely grinding the said source material which also contains at least one compound selected from the group consisting of Fe 2 O 3 and Cr 2 O 3 in an amount up to about 2%, sufficiently so that said Fe 2 O 3 or Cr 2 O 3 can become effective as said calcination auxiliary agent during said calcination, the grain size to be obtained by grinding being not more than 0.4 μm which corresponds to a specific surface of at least 5 m 2 /g.
Claim 10
Dependent Claim
32 words
The process of claim 8 wherein the grain size to be obtained by grinding is not more than 0.2 μm, corresponding to a specific surface of at least 10 m 2 /g.
References Cited (Backward Citations)
US3238049A
Cited
US3377176A
Cited
US3615775A
Cited
US3637406A
Cited
US3772416A
Cited
US3854965A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1980-04-25 | 1980-10-25 | 1981-04-26 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1984-04-25 | 1984-10-25 | 1985-04-26 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1988-04-25 | 1988-10-25 | 1989-04-26 | $7700.00 | Window Closed / Lapsed |