Morpholino-modified polysiloxane-polyoxyalkylene copolymers and their use as foam stabilizers in polyurethanes

Claim 2

An organosilicone composition which comprises a polysiloxane-polyoxyalkylene copolymer containing monofunctional siloxy units and difunctional siloxy units, an average of between about 2 and about 30 silicon-bonded polyoxyalkylene blocks for every two moles of monofunctional units, and an average of from about 2 to about 100 silicon-bonded morpholino-bearing groups for every two moles of monofunctional units, wherein: i. said polyoxyalkylene blocks have the average composition, --(R°).sub.r-- (OC.sub.a H.sub.2a).sub.b-- OG

Claim 3

where r is zero or one, R° comprises a bivalent alkylene group a carbon atom of which is bonded to silicon, --(OC a H 2a ) b-- is a polyoxyalkylene chain where a has a value from 2 to 4 and b has an average value from about 3 to about 100, and G is an organic cap; ii. said morpholino-bearing groups have the formula, ##STR38## wherein p is zero or has an average value from about one to about four, q is zero or one provided q is one when p has a value of more than one, R' is bivalent alkylene having from two to four carbon atoms, R" is bivalent alkylene having from two to six carbon atoms, and R 1 , R 2 , R 3 and R 4 are independently hydrogen or alkyl of one to four carbon atoms; and iii. the monofunctional units of the copolymer have at least two alkyls of one to ten carbon atoms bonded to the respective silicon atoms thereof and the difunctional units have at least one alkyl of one to ten carbon atoms bonded to the respective silicon atoms thereof, the remaining organic group bonded to silicon of the respective monofunctional and difunctional siloxy units being alkyl of one to ten carbon atoms, said morpholino-bearing group or said polyoxyalkylene block, provided the average number of said morpholino-bearing groups and said polyoxyalkylene blocks contained in the copolymer is as aforesaid.

Claim 4

where r is zero or one, R° comprises a bivalent alkylene group a carbon atom of which is bonded to silicon, --(OC a H 2a ) b-- is a polyoxyalkylene chain where a has a value from 2 to 4 and b has an average value from about 3 to about 100, and G is an organic cap; ii. said morpholino-bearing groups have the formula, ##STR38## wherein p is zero or has an average value from about one to about four, q is zero or one provided q is one when p has a value of more than one, R' is bivalent alkylene having from two to four carbon atoms, R" is bivalent alkylene having from two to six carbon atoms, and R 1 , R 2 , R 3 and R 4 are independently hydrogen or alkyl of one to four carbon atoms; and iii. the monofunctional units of the copolymer have at least two alkyls of one to ten carbon atoms bonded to the respective silicon atoms thereof and the difunctional units have at least one alkyl of one to ten carbon atoms bonded to the respective silicon atoms thereof, the remaining organic group bonded to silicon of the respective monofunctional and difunctional siloxy units being alkyl of one to ten carbon atoms, said morpholino-bearing group or said polyoxyalkylene block, provided the average number of said morpholino-bearing groups and said polyoxyalkylene blocks contained in the copolymer is as aforesaid.

Claim 5

An organosilicone composition as defined in claim 1 in which the polysiloxane-polyoxyalkylene copolymer contains, for every two moles of monofunctional units, an average of up to about 200 moles of said difunctional siloxy units wherein the remaining organic group bonded to the respective silicon atoms thereof is said alkyl of one to ten carbon atoms.

Claim 6

An organosilicone composition which comprises a polysiloxane-polyoxyalkylene copolymer containing monofunctional trialkylsiloxy units, (R) 3 SiO 1/2 , where R has from one to ten carbon atoms, and, for every two moles of monofunctional units, an average of from about 10 to about 200 dialkylsiloxy units having the unit formula, (R) 2 SiO 2/2 , where R has from one to ten carbon atoms, an average of from about 2 to about 100 difunctional morpholino-bearing alkylsiloxy units having the unit formula, ##STR39## where R is alkyl of one to ten carbon atoms, p is zero or has an average value from about one to about four, q is zero or one provided q is one when p has a value of more than one, c has a value from two to four and d has a value from two to six. and an average of from about 2 to about 30 difunctional siloxy units having the unit formula, (R)(E)SiO.sub. 2/2, where R is alkyl of one to ten carbon atoms and E is a polyoxyalkylene block having the average composition, --(R°).sub.r -(OC.sub.a H.sub.2a).sub.b-- OG wherein r is zero or one, R° comprises a bivalent alkylene group a carbon atom of which is bonded to silicon, --(OC a H 2a ) b-- is a polyoxyalkylene chain where a has a value from 2 to 4 provided the average polyoxyalkylene content of --(OC a H 2a ) b-- is constituted of from about 20 to about 75 weight percent of oxyethylene, and wherein b has an average value from about 3 to about 100, and G is R°°--, R°°C(O)-- or R°°NHC(O)-- where R°° is a monovalent hydrocarbon group having from 1 to 12 carbon atoms.

Claim 7

An organosilicone composition which comprises a polysiloxane-polyoxyalkylene copolymer containing monofunctional trialkylsiloxy units, (R) 3 SiO 1/2 , where R has from one to ten carbon atoms, and, for every two moles of monofunctional units, an average of from about 10 to about 200 dialkylsiloxy units having the unit formula, (R) 2 SiO 2/2 , where R has from one to ten carbon atoms, an average of from about 2 to about 100 difunctional morpholino-bearing alkylsiloxy units having the unit formula, ##STR39## where R is alkyl of one to ten carbon atoms, p is zero or has an average value from about one to about four, q is zero or one provided q is one when p has a value of more than one, c has a value from two to four and d has a value from two to six. and an average of from about 2 to about 30 difunctional siloxy units having the unit formula, (R)(E)SiO.sub. 2/2, where R is alkyl of one to ten carbon atoms and E is a polyoxyalkylene block having the average composition, --(R°).sub.r -(OC.sub.a H.sub.2a).sub.b-- OG wherein r is zero or one, R° comprises a bivalent alkylene group a carbon atom of which is bonded to silicon, --(OC a H 2a ) b-- is a polyoxyalkylene chain where a has a value from 2 to 4 provided the average polyoxyalkylene content of --(OC a H 2a ) b-- is constituted of from about 20 to about 75 weight percent of oxyethylene, and wherein b has an average value from about 3 to about 100, and G is R°°--, R°°C(O)-- or R°°NHC(O)-- where R°° is a monovalent hydrocarbon group having from 1 to 12 carbon atoms.

Claim 8

An organosilicone composition as defined in claim 3 in which the said copolymer contains an average of from about 20 to about 100 of said dialkylsiloxy units, an average of from about 2 to about 30 of said difunctional morpholino-bearing alkylsiloxy units and an average of from about 2 to about 10 of said difunctional siloxy units having the unit formula, (R)(E)SiO 2/2 .

Claim 9

An organosilicone composition which comprises a polysiloxane-polyoxyalkylene copolymer containing monofunctional trialkylsiloxy units, (R) 3 SiO 1/2 , where R has from one to ten carbon atoms, and, for every two moles of monofunctional units, zero or an average of up to about 20 dialkylsiloxy units having the unit formula, (R) 2 SiO 2/2 , where R has from one to ten carbon atoms, an average of from about 2 to about 20 difunctional morpholino-bearing alkylsiloxy units having the unit formula, ##STR40## where R is alkyl of one to ten carbon atoms, p is zero or has an average value from about one to about four, q is zero or one provided q is one when p has a value of more than one, c has a value from two to four and d has a value from two to six, and an average of from about 2 to about 30 difunctional siloxy units having the unit formula, (R)(E)SiO 2/2 , where R is alkyl of one to ten carbon atoms and E is a polyoxyalkylene block having the average composition, --(R°).sub.r-- (OC.sub.a H.sub.2a).sub.b-- OG wherein r is zero or one, R° comprises a bivalent alkylene group a carbon atom of which is bonded to silicon, --(OC a H 2a ) b-- is a polyoxyalkylene chain where a has a value from 2 to 4 provided the average polyoxyalkylene content of --(OC a H 2a ) b-- is constituted of at least 75 weight percent of oxyethylene, and wherein b has an average value from about 3 to about 100, and G is R°°--, R°°C(O)-- or R°°NHC(O)-- where R°° is a monovalent hydrocarbon group having from 1 to 12 carbon atoms.

Claim 10

An organosilicone composition which comprises a polysiloxane-polyoxyalkylene copolymer containing monofunctional trialkylsiloxy units, (R) 3 SiO 1/2 , where R has from one to ten carbon atoms, and, for every two moles of monofunctional units, zero or an average of up to about 20 dialkylsiloxy units having the unit formula, (R) 2 SiO 2/2 , where R has from one to ten carbon atoms, an average of from about 2 to about 20 difunctional morpholino-bearing alkylsiloxy units having the unit formula, ##STR40## where R is alkyl of one to ten carbon atoms, p is zero or has an average value from about one to about four, q is zero or one provided q is one when p has a value of more than one, c has a value from two to four and d has a value from two to six, and an average of from about 2 to about 30 difunctional siloxy units having the unit formula, (R)(E)SiO 2/2 , where R is alkyl of one to ten carbon atoms and E is a polyoxyalkylene block having the average composition, --(R°).sub.r-- (OC.sub.a H.sub.2a).sub.b-- OG wherein r is zero or one, R° comprises a bivalent alkylene group a carbon atom of which is bonded to silicon, --(OC a H 2a ) b-- is a polyoxyalkylene chain where a has a value from 2 to 4 provided the average polyoxyalkylene content of --(OC a H 2a ) b-- is constituted of at least 75 weight percent of oxyethylene, and wherein b has an average value from about 3 to about 100, and G is R°°--, R°°C(O)-- or R°°NHC(O)-- where R°° is a monovalent hydrocarbon group having from 1 to 12 carbon atoms.

Claim 11

An organosilicone composition as defined in claim 5 in which the said copolymer contains an average of no more than about 10 of said dialkylsiloxy units, an average of no more than about 10 of said difunctional morpholino-bearing alkylsiloxy units, and an average of no more than about 15 of said difunctional siloxy units having the unit formula, (R)(E)SiO 2/2 .

Claim 12

An organosilicone composition which comprises a polysiloxane-polyoxyalkylene copolymer having the average composition, ##STR41## wherein: R is alkyl of one to four carbon atoms; G is an organic cap; p is zero or one; c has a value from two to four; d has a value from two to six; r is zero or one; e has a value from two to six; b has an average value from about 3 to about 100; a has a value from two to four provided at least 20 weight percent of --(OC a H 2a ) b-- is constituted of oxyethylene; x is zero or a positive number having an average value of up to about 200; y has an average value from about 2 to about 100; and z has an average value from about 2 to about 30.

Claim 13

An organosilicone composition which comprises a polysiloxane-polyoxyalkylene copolymer having the average composition, ##STR41## wherein: R is alkyl of one to four carbon atoms; G is an organic cap; p is zero or one; c has a value from two to four; d has a value from two to six; r is zero or one; e has a value from two to six; b has an average value from about 3 to about 100; a has a value from two to four provided at least 20 weight percent of --(OC a H 2a ) b-- is constituted of oxyethylene; x is zero or a positive number having an average value of up to about 200; y has an average value from about 2 to about 100; and z has an average value from about 2 to about 30.

Claim 14

An organosilicone composition as defined in claim 7 in which x of said copolymer has an average value of at least about 10, and the average polyoxyalkylene content of --(OC a H 2a ) b -- is constituted of from about 20 to about 65 weight percent of oxyethylene.

Claim 15

An organosilicone composition as defined in claim 7 in which x of said copolymer is a positive number having an average value of no more than about 20, y has an average value of no more than about 20, b has an average value no more than about 30, and the polyoxyalkylene content of --(OC a H 2a ) b -- is constituted on the average of at least 75 weight percent oxyethylene.

Claim 16

An organosilicone composition as defined in claim 7 in which the R groups of said copolymer are methyl.

Claim 17

An organosilicone composition as defined in claim 7 in which r of said copolymer is zero.

Claim 18

An organosilicone composition as defined in claim 7 in which r of said copolymer is one and e has a value of no more than four.

Claim 19

An organosilicone composition as defined in claim 7 in which p of said copolymer is one.

Claim 20

An organosilicone composition as defined in claim 7 in which p of said copolymer is zero.

Claim 21

An organosilicone composition as defined in claim 7 in which G of said copolymer is a monovalent hydrocarbon group having from 1 to 12 carbon atoms.

Claim 22

A composition as defined in claim 15 in which G is alkyl of one to four carbon atoms.

Claim 23

A composition as defined in claim 15 in which G is aryl.

Claim 24

A composition as defined in claim 15 in which G is aralkyl.

Claim 25

An organosilicone composition as defined in claim 7 in which G is R°°C(O)-- where R°° is a monovalent hydrocarbon group having from 1 to 12 carbon atoms.

Claim 26

An organosilicone composition as defined in claim 7 in which G is R°°NHC (O)-- where R°° is a monovalent hydrocarbon group having from 1 to 12 carbon atoms.

Claim 27

An organosilicone composition which comprises a polysiloxane-polyoxyalkylene copolymer having the average composition, ##STR42## wherein: Me is methyl; G is an organic cap; e has a value from 2 to 6; d has a value from 2 to 6; x has an average value from about 10 to about 200; y has an average value from about 2 to about 100; z has an average value from about 2 to about 30; a has a value from two to four provided an average of from about 20 to about 75 weight percent of --(OC a H 2a ) b -- is constituted of oxyethylene units; and b has an average value such that the average molecular weight of --(OC a H 2a ) b -- is from about 1000 to about 6000.

Claim 28

An organosilicone composition which comprises a polysiloxane-polyoxyalkylene copolymer having the average composition, ##STR42## wherein: Me is methyl; G is an organic cap; e has a value from 2 to 6; d has a value from 2 to 6; x has an average value from about 10 to about 200; y has an average value from about 2 to about 100; z has an average value from about 2 to about 30; a has a value from two to four provided an average of from about 20 to about 75 weight percent of --(OC a H 2a ) b -- is constituted of oxyethylene units; and b has an average value such that the average molecular weight of --(OC a H 2a ) b -- is from about 1000 to about 6000.

Claim 29

An organosilicone composition which comprises a polysiloxane-polyoxyalkylene copolymer having the average composition, ##STR43## wherein: Me is methyl; R°° is a monovalent hydrocarbon group having one to twelve carbon atoms; x has an average value from about 20 to about 100; y has an average value from about 2 to about 30; z has an average value from about 2 to about 10; and m and n are positive numbers the average values of which are such that the average molecular weight of the chain, --(OC 2 H 4 ) n (OC 3 H 6 ) m --, is from about 1000 to about 6000 and the average oxyethylene content of said chain is from about 20 to about 65 weight percent.

Claim 30

An organosilicone composition which comprises a polysiloxane-polyoxyalkylene copolymer having the average composition, ##STR43## wherein: Me is methyl; R°° is a monovalent hydrocarbon group having one to twelve carbon atoms; x has an average value from about 20 to about 100; y has an average value from about 2 to about 30; z has an average value from about 2 to about 10; and m and n are positive numbers the average values of which are such that the average molecular weight of the chain, --(OC 2 H 4 ) n (OC 3 H 6 ) m --, is from about 1000 to about 6000 and the average oxyethylene content of said chain is from about 20 to about 65 weight percent.

Claim 31

A composition as defined in claim 22 in which R°° of said copolymer is alkyl of one to four carbon atoms.

Claim 32

A composition as defined in claim 23 in which R°° is methyl.

Claim 33

An organosilicone composition which comprises a polysiloxane-polyoxyalkylene copolymer having the average composition, ##STR44## wherein: Me is methyl; G is an organic cap; e has a value from 2 to 6; d has a value from 2 to 6; x is zero or a positive number having an average value no more than about 20; y has an average value from about 2 to about 20; z has an average value from about 2 to about 30; b has an average value from about 3 to about 30; and a has a value from 2 to 4 provided an average of at least 75 weight percent of the polyoxyalkylene chain, --(OC a H 2a ) b --, is constituted of oxyethylene units.

Claim 34

An organosilicone composition which comprises a polysiloxane-polyoxyalkylene copolymer having the average composition, ##STR44## wherein: Me is methyl; G is an organic cap; e has a value from 2 to 6; d has a value from 2 to 6; x is zero or a positive number having an average value no more than about 20; y has an average value from about 2 to about 20; z has an average value from about 2 to about 30; b has an average value from about 3 to about 30; and a has a value from 2 to 4 provided an average of at least 75 weight percent of the polyoxyalkylene chain, --(OC a H 2a ) b --, is constituted of oxyethylene units.

Claim 35

An organosilicone composition which comprises a polysiloxane-polyoxyalkylene copolymer having the average composition, ##STR45## wherein: Me is methyl; R°° is a monovalent hydrocarbon group having from one to twelve carbon atoms; x is zero or a positive number having an average value no more than about 10; y has an average value from about 2 to about 10; z has an average value from about 2 to about 15; and b has an average value from about 4 to about 15.

Claim 36

An organosilicone composition which comprises a polysiloxane-polyoxyalkylene copolymer having the average composition, ##STR45## wherein: Me is methyl; R°° is a monovalent hydrocarbon group having from one to twelve carbon atoms; x is zero or a positive number having an average value no more than about 10; y has an average value from about 2 to about 10; z has an average value from about 2 to about 15; and b has an average value from about 4 to about 15.

Claim 37

An organosilicone composition as defined in claim 26 in which x of said copolymer is a positive number.

Claim 38

An organosilicone composition as defined in claim 26 in which x is zero.

Claim 39

An organosilicone composition as defined in claim 26 in which R°° of said copolymer is alkyl of one to four carbon atoms.

Claim 40

An organosilicone composition as defined in claim 29 in which R°° is methyl.

Claim 41

A flame-retarded polyether-based urethane foam which comprises the product formed by simultaneously reacting and foaming a reaction mixture containing: (a) a polyether polyol reactant containing an average of at least two hydroxyl groups per molecule; (b) an organic polyisocyanate reactant containing at least two isocyanato groups per molecule; (c) water as a source of blowing action; (d) a catalyst comprising a tertiary-amine; (e) a flame-retarding agent; and (f) a foam stabilizer comprising a polysiloxane-poly(oxyethylene-oxypropylene) copolymer having the average composition, ##STR46## wherein: R is alkyl having from one to four carbon atoms; R' is bivalent alkylene of 2 to 4 carbon atoms; R" is bivalent alkylene of 2 to 6 carbon atoms; R° comprises a bivalent alkylene group of from 2 to 6 carbon atoms a carbon atom of which is bonded to silicon; G is an organic cap; r is zero or one; p is zero or one; x has an average value from about 10 to about 200, y has an average value from about 2 to about 100, and z has an average value from about 2 to about 30, provided an average of from about 50 to about 85 weight percent of said copolymer is constituted of said --(R°) r (OC 2 H 4 ) n (OC 3 H 6 ) m OG blocks; and m and n are numbers such that the average molecular weight of the chain, --(OC 2 H 4 ) n (OC 3 H 6 ) m --, is from about 1000 to about 6000 and from about 20 to about 65 weight percent of the chain is constituted of oxyethylene.

Claim 42

A flame-retarded polyether-based urethane foam which comprises the product formed by simultaneously reacting and foaming a reaction mixture containing: (a) a polyether polyol reactant containing an average of at least two hydroxyl groups per molecule; (b) an organic polyisocyanate reactant containing at least two isocyanato groups per molecule; (c) water as a source of blowing action; (d) a catalyst comprising a tertiary-amine; (e) a flame-retarding agent; and (f) a foam stabilizer comprising a polysiloxane-poly(oxyethylene-oxypropylene) copolymer having the average composition, ##STR46## wherein: R is alkyl having from one to four carbon atoms; R' is bivalent alkylene of 2 to 4 carbon atoms; R" is bivalent alkylene of 2 to 6 carbon atoms; R° comprises a bivalent alkylene group of from 2 to 6 carbon atoms a carbon atom of which is bonded to silicon; G is an organic cap; r is zero or one; p is zero or one; x has an average value from about 10 to about 200, y has an average value from about 2 to about 100, and z has an average value from about 2 to about 30, provided an average of from about 50 to about 85 weight percent of said copolymer is constituted of said --(R°) r (OC 2 H 4 ) n (OC 3 H 6 ) m OG blocks; and m and n are numbers such that the average molecular weight of the chain, --(OC 2 H 4 ) n (OC 3 H 6 ) m --, is from about 1000 to about 6000 and from about 20 to about 65 weight percent of the chain is constituted of oxyethylene.

Claim 43

A flame-retarded polyether-based urethane foam which comprises the product formed by simultaneously reacting and foaming a reaction mixture containing: (a) a polyether polyol reactant containing an average of at least two hydroxyl groups per molecule; (b) an organic polyisocyanate reactant containing at least two isocyanato groups per molecule; (c) water as a source of blowing action; (d) a catalyst comprising a tertiary-amine; (e) a flame-retarding agent; and (f) a foam stabilizer comprising polysiloxane-poly(oxyethylene-oxypropylene) copolymers having the average composition, ##STR47## wherein: Me is methyl, R°° is a monovalent hydrocarbon group having from 1 to 12 carbon atoms; x has an average value from about 20 to about 100, y has an average value from about 2 to about 30, and z has an average value from about 2 to about 10, provided the average weight of said copolymers attributable to said --C 3 H 6 (OC 2 H 4 ) n (OC 3 H 6 ) m OR°° groupings is from about 50 to about 85 weight percent; and m and n are numbers such that the average molecular weight of the chain, --(OC 2 H 4 ) n (OC 3 H 6 ) m --, is from about 1000 to about 6000 and from about 20 to about 65 weight percent of said chain is constituted of oxyethylene.

Claim 44

A flame-retarded polyether-based urethane foam which comprises the product formed by simultaneously reacting and foaming a reaction mixture containing: (a) a polyether polyol reactant containing an average of at least two hydroxyl groups per molecule; (b) an organic polyisocyanate reactant containing at least two isocyanato groups per molecule; (c) water as a source of blowing action; (d) a catalyst comprising a tertiary-amine; (e) a flame-retarding agent; and (f) a foam stabilizer comprising polysiloxane-poly(oxyethylene-oxypropylene) copolymers having the average composition, ##STR47## wherein: Me is methyl, R°° is a monovalent hydrocarbon group having from 1 to 12 carbon atoms; x has an average value from about 20 to about 100, y has an average value from about 2 to about 30, and z has an average value from about 2 to about 10, provided the average weight of said copolymers attributable to said --C 3 H 6 (OC 2 H 4 ) n (OC 3 H 6 ) m OR°° groupings is from about 50 to about 85 weight percent; and m and n are numbers such that the average molecular weight of the chain, --(OC 2 H 4 ) n (OC 3 H 6 ) m --, is from about 1000 to about 6000 and from about 20 to about 65 weight percent of said chain is constituted of oxyethylene.

Claim 45

A flame-retardant polyester-based urethane foam which comprises the product formed by simultaneously reacting and foaming a reaction mixture containing: (a) a polyester polyol reactant containing an average of at least two hydroxyl groups per molecule; (b) an organic polyisocyanate reactant containing at least two isocyanato groups per molecule; (c) water as a source of blowing action; (d) a catalyst comprising a tertiary-amine; (e) a flame-retarding agent; and (f) a foam stabilizer comprising a polysiloxane-polyoxyethylene copolymer having the average composition, ##STR48## wherein: Me is methyl; R°° is a monovalent hydrocarbon group having from 1 to 12 carbon atoms; b has an average value from about 3 to about 30; x is zero or a positive number having an average value up to about 20, y has an average value from about 2 to about 20, and z has an average value from about 2 to about 30, provided the average weight of said copolymer attributable to --C 3 H 6 (OC 2 H 4 ) b OR°° is from about 50 to about 85 weight percent.

Claim 46

A flame-retardant polyester-based urethane foam which comprises the product formed by simultaneously reacting and foaming a reaction mixture containing: (a) a polyester polyol reactant containing an average of at least two hydroxyl groups per molecule; (b) an organic polyisocyanate reactant containing at least two isocyanato groups per molecule; (c) water as a source of blowing action; (d) a catalyst comprising a tertiary-amine; (e) a flame-retarding agent; and (f) a foam stabilizer comprising a polysiloxane-polyoxyethylene copolymer having the average composition, ##STR48## wherein: Me is methyl; R°° is a monovalent hydrocarbon group having from 1 to 12 carbon atoms; b has an average value from about 3 to about 30; x is zero or a positive number having an average value up to about 20, y has an average value from about 2 to about 20, and z has an average value from about 2 to about 30, provided the average weight of said copolymer attributable to --C 3 H 6 (OC 2 H 4 ) b OR°° is from about 50 to about 85 weight percent.

Claim 47

A flame-retarded polyester-based urethane foam as defined in claim 33 in which x of said copolymer is a positive number.

Claim 48

A process for producing flexible polyurethane foam which comprises simultaneously reacting and foaming a reaction mixture containing: (a) a polyether polyol or a polyester polyol reactant having an average of at least two hydroxyl groups per molecule; (b) a polyisocyanate reactant having at least two isocyanato groups per molecule; (c) a blowing agent; (d) a catalyst comprising an amine; and (e) a foam stabilizer comprising a polysiloxane-polyoxyalkylene copolymer having the average composition, ##STR49## wherein: R is alkyl having from one to ten carbon atoms; t, u, v, w, the sum t+u and the sum v+w are independently zero or one, and each of the sums t+w and u+v is independently zero, one or two; E is a polyoxyalkylene block having the average composition, --(R°).sub.r --(OC.sub.a H.sub.2a).sub.b --OG wherein r is zero or one, R° comprises a bivalent alkylene group a carbon atom of which is bonded to silicon, --(OC a H 2a ) b -- is a polyoxyalkylene chain where a has a value from 2 to 4 and b has an average value from about 3 to about 100, and G is an organic cap; and Q is a morpholino-bearing group having the formula, ##STR50## where p is zero or has an average value from about one to about four, q is zero or one provided q is one when p has a value of more than one, R' is bivalent alkylene having from two to four carbon atoms, R" is bivalent alkylene having from two to six carbon atoms, and R 1 , R 2 , R 3 and R 4 are independently hydrogen or alkyl having from one to four carbon atoms; and, when reactant (a) is a polyether polyol, x has an average value from about 10 to about 200, y has an average value from about 2 to about 100 and z has an average value from about 2 to about 30, provided an average of from about 50 to about 85 weight percent of said copolymer is constituted of E; and the average polyoxyalkylene content of --(C a H 2a O) b -- of E is constituted of from about 20 to about 75 weight percent of oxyethylene; and when reactant (a) is a polyester polyol, x is zero or a positive number having an average value up to about 20, y has an average value from about 2 to about 20 and z has an average value from about 2 to about 30, provided an average of from about 50 to about 85 weight percent of said copolymer is constituted of E; and the average polyoxyalkylene content of --(C a H 2a O) b -- of E is constituted of at least 75 weight percent of oxyethylene.

Claim 49

A process for producing flexible polyurethane foam which comprises simultaneously reacting and foaming a reaction mixture containing: (a) a polyether polyol or a polyester polyol reactant having an average of at least two hydroxyl groups per molecule; (b) a polyisocyanate reactant having at least two isocyanato groups per molecule; (c) a blowing agent; (d) a catalyst comprising an amine; and (e) a foam stabilizer comprising a polysiloxane-polyoxyalkylene copolymer having the average composition, ##STR49## wherein: R is alkyl having from one to ten carbon atoms; t, u, v, w, the sum t+u and the sum v+w are independently zero or one, and each of the sums t+w and u+v is independently zero, one or two; E is a polyoxyalkylene block having the average composition, --(R°).sub.r --(OC.sub.a H.sub.2a).sub.b --OG wherein r is zero or one, R° comprises a bivalent alkylene group a carbon atom of which is bonded to silicon, --(OC a H 2a ) b -- is a polyoxyalkylene chain where a has a value from 2 to 4 and b has an average value from about 3 to about 100, and G is an organic cap; and Q is a morpholino-bearing group having the formula, ##STR50## where p is zero or has an average value from about one to about four, q is zero or one provided q is one when p has a value of more than one, R' is bivalent alkylene having from two to four carbon atoms, R" is bivalent alkylene having from two to six carbon atoms, and R 1 , R 2 , R 3 and R 4 are independently hydrogen or alkyl having from one to four carbon atoms; and, when reactant (a) is a polyether polyol, x has an average value from about 10 to about 200, y has an average value from about 2 to about 100 and z has an average value from about 2 to about 30, provided an average of from about 50 to about 85 weight percent of said copolymer is constituted of E; and the average polyoxyalkylene content of --(C a H 2a O) b -- of E is constituted of from about 20 to about 75 weight percent of oxyethylene; and when reactant (a) is a polyester polyol, x is zero or a positive number having an average value up to about 20, y has an average value from about 2 to about 20 and z has an average value from about 2 to about 30, provided an average of from about 50 to about 85 weight percent of said copolymer is constituted of E; and the average polyoxyalkylene content of --(C a H 2a O) b -- of E is constituted of at least 75 weight percent of oxyethylene.

Claim 50

A process as defined in claim 35 in which said reaction mixture contains a flame-retardant as an additional component thereof.

Claim 51

A flame-retarded flexible polyurethane foam produced by the process of claim 36.

Claim 52

A process as defined in claim 35 in which the flame-retardant contains phosphorus or halogen, both phosphorus and halogen, or phosphorus and nitrogen.

Claim 53

A process as defined in claim 35 in which the flame-retardant is present in the reaction mixture in an amount from about 1 to about 30 parts by weight per 100 parts by weight of polyol reactant (a).

Claim 54

A flame-retardant polyester-based urethane foam which comprises the product formed by simultaneously reacting and foaming a reaction mixture containing: (a) a polyester polyol reactant containing an average of at least two hydroxyl groups per molecule; (b) an organic polyisocyanate reactant containing at least two isocyanato groups per molecule; (c) water as a source of blowing action; (d) a catalyst comprising a tertiary-amine; (e) a flame-retarding agent; and (f) a foam stabilizer comprising a polysiloxane-polyoxyethylene copolymer having the average composition, ##STR51## wherein: R is alkyl having from one to four carbon atoms; R' is bivalent alkylene of 2 to 4 carbon atoms; R" is bivalent alkylene of 2 to 6 carbon atoms; R° comprises a bivalent alkylene group of from 2 to 6 carbon atoms a carbon atom of which is bonded to silicon; G is an organic cap; r is zero or one; p is zero or one; b has an average value from about 3 to about 30; x is zero or a positive number having an average value up to about 20, y has an average value from about 2 to about 20, and z has an average value from about 2 to about 30, provided the average weight of said copolymer attributable to --(R°) r (OC 2 H 4 ) b OG is from about 50 to about 85 weight percent.

Claim 55

A flame-retardant polyester-based urethane foam which comprises the product formed by simultaneously reacting and foaming a reaction mixture containing: (a) a polyester polyol reactant containing an average of at least two hydroxyl groups per molecule; (b) an organic polyisocyanate reactant containing at least two isocyanato groups per molecule; (c) water as a source of blowing action; (d) a catalyst comprising a tertiary-amine; (e) a flame-retarding agent; and (f) a foam stabilizer comprising a polysiloxane-polyoxyethylene copolymer having the average composition, ##STR51## wherein: R is alkyl having from one to four carbon atoms; R' is bivalent alkylene of 2 to 4 carbon atoms; R" is bivalent alkylene of 2 to 6 carbon atoms; R° comprises a bivalent alkylene group of from 2 to 6 carbon atoms a carbon atom of which is bonded to silicon; G is an organic cap; r is zero or one; p is zero or one; b has an average value from about 3 to about 30; x is zero or a positive number having an average value up to about 20, y has an average value from about 2 to about 20, and z has an average value from about 2 to about 30, provided the average weight of said copolymer attributable to --(R°) r (OC 2 H 4 ) b OG is from about 50 to about 85 weight percent.