Method of preparation of dispersion strengthened silver electrical contacts
Assignee: Engelhard Minerals and Chemicals Corp
•
Filing: 1975-09-05
•
Granted: 1977-04-19
•
Expires: 1995-09-05
Abstract
Abstract Preparation of compositions of silver and CeO 2 by powder metallurgy techniques overcomes problems inherent in melting silver and pure cerium and subsequently internally oxidizing the cerium in the mixture. Small concentrations of CeO 2 substantially improve the electrical contact properties of silver. Silver with dispersed CeO 2 is superior to silver alone for use as an electrical contact because of much greater resistance to arc erosion and welding and only slightly higher contact resistance.
Inventors
- 👤 James S. Hill
- 👤 Emil L. Carbone
- 👤 Victor G. Mooradian
- 👤 Walter G. Keyes
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-03 00:56
CPC Classifications
C; C22; C22C; C22C1/00; C22C1/04; C22C1/05; H; H01; H01H; H01H1/00; H01H1/02; H01H1/021; H01H1/023; H01H1/0237
Claims Analysis
Total Claims: 16
Claim 1
Independent Claim
54 words
The method of preparing a composition of Ag and CeO 2 comprising the steps of preparing a powder mixture of Ag and from about 11/4 to about 21/2 percent by weight of CeO 2 , consolidating said powder mixture into a solid billet, and mechanically reducing said solid billet into an electrical contact body.
Claim 2
Independent Claim
54 words
The method of preparing a composition of Ag and CeO 2 comprising the steps of preparing a powder mixture of Ag and from about 11/4 to about 21/2 percent by weight of CeO 2 , consolidating said powder mixture into a solid billet, and mechanically reducing said solid billet into an electrical contact body.
Claim 3
Dependent Claim
109 words
The method of claim 1 wherein the preparing of a powder mixture step comprises the sub-steps of forming a mixed solution by mixing a solution of a silver salt with a solution of a cerium salt, precipitating a mixture of precipitates of Ag 2 O and Ce(OH) 3 by adding a base to said mixed solution, filtering and washing the mixture of precipitates, drying the mixture of precipitates, grinding said mixture of precipitates to a fine powder, and heating said powder at temperature between about 250° and about 450° C from between about 1 and about 60 hours to yield a powder mixture of Ag and CeO 2 .
Claim 4
Dependent Claim
124 words
The method of claim 1 wherein the preparing of a powder mixture step comprises the sub-steps of forming a mixed solution by mixing a solution of a silver salt with a solution of a cerium salt, precipitating a mixture of precipitates of Ag 2 O and Ce(OH) 3 by adding a base to said mixed solution, filtering and washing the mixture of precipitates, drying the mixture of precipitates, grinding said mixture of precipitates to a fine powder, heating said powder at a relatively low temperature of about 250° C for a relatively long time of about 48 hours, and then heating said powder at a relatively high temperature of about 350° C for a relatively short time of from about 1 to 4 hours.
Claim 5
Dependent Claim
53 words
The method of claim 1 wherein said consolidating step comprises placing said powder mixture of Ag and CeO 2 into a flexible sealed container, hydrostatically pressing it at 30,000 psi to form a solid billet, and then sintering said billet at a temperature between about 700° to 900° C for about 2 hours.
Claim 6
Dependent Claim
42 words
The method of claim 1 wherein said reducing step comprises the sub-steps of hot extruding of the solid billet into a small diameter rod, drawing said rod into smaller diameter rods, and forming said smaller diameter rods into an electrical contact body.
Claim 7
Dependent Claim
44 words
The method of claim 1 wherein said reducing step comprises the sub-steps of cold swaging said solid billet with intermediate anneals to smaller diameter rods, drawing the smaller diameter rods to even smaller diameter wire, and forming said wire into an electrical contact body.
Claim 8
Dependent Claim
30 words
The method of claim 1 wherein said reducing step comprises the steps of hot rolling said solid billet into a sheet, and forming said sheet into an electrical contact body.
Claim 9
Dependent Claim
30 words
The method of claim 1 wherein said reducing step comprises the steps of cold rolling said solid billet into a sheet, and forming said sheet into an electrical contact body.
Claim 10
Independent Claim
109 words
The method of preparing a composition of Ag and from about 11/4 to about 21/2 percent by weight of CeO 2 comprising the steps of adding high-purity silver powder to a cerium salt solution to yield a mixed solution, heating said mixed solution until the solution evaporates leaving a powder of Ag particles coated with a cerium salt, heating said silver particles at a temperature in the range of about 250° to about 450° C, until said cerium salt is converted to CeO 2 , grinding and sieving the resulting powder, consolidating said powder mixture into a solid billet, and mechanically reducing said billet into an electrical contact rivet.
Claim 11
Independent Claim
109 words
The method of preparing a composition of Ag and from about 11/4 to about 21/2 percent by weight of CeO 2 comprising the steps of adding high-purity silver powder to a cerium salt solution to yield a mixed solution, heating said mixed solution until the solution evaporates leaving a powder of Ag particles coated with a cerium salt, heating said silver particles at a temperature in the range of about 250° to about 450° C, until said cerium salt is converted to CeO 2 , grinding and sieving the resulting powder, consolidating said powder mixture into a solid billet, and mechanically reducing said billet into an electrical contact rivet.
Claim 12
Independent Claim
87 words
The method of preparing a composition of Ag and from about 11/4 to about 21/2 percent by weight of CeO 2 comprising the steps of forming a colloidal solution of substantially pure powdered Ag and powdered CeO 2 in distilled water, milling said solution to uniformly distribute CeO 2 particles throughout the Ag powder, drying said solution to yield a powder mixture of Ag and CeO 2 , consolidating said powder mixture into a solid billet, and mechanically reducing said solid billet into an electrical contact rivet.
Claim 13
Independent Claim
87 words
The method of preparing a composition of Ag and from about 11/4 to about 21/2 percent by weight of CeO 2 comprising the steps of forming a colloidal solution of substantially pure powdered Ag and powdered CeO 2 in distilled water, milling said solution to uniformly distribute CeO 2 particles throughout the Ag powder, drying said solution to yield a powder mixture of Ag and CeO 2 , consolidating said powder mixture into a solid billet, and mechanically reducing said solid billet into an electrical contact rivet.
Claim 14
Dependent Claim
30 words
The method of claim 10 wherein the preparing of a powder mixture step further comprises the step of grinding and sieving said powder mixture of Ag and CeO 2 .
Claim 15
Dependent Claim
71 words
An electrical contact made from material comprising substantially pure silver mixed with from about 11/4 to about 21/2 percent by weight of CeO 2 , said material prepared by the steps comprising: preparing a powder mixture of Ag and from about 11/4 to about 21/2 percent by weight of CeO 2 , consolidating said powder mixture into a solid billet, and mechanically reducing said solid billet into an electrical contact body.
Claim 16
Dependent Claim
71 words
An electrical contact made from material comprising substantially pure silver mixed with from about 11/4 to about 21/2 percent by weight of CeO 2 , said material prepared by the steps comprising: preparing a powder mixture of Ag and from about 11/4 to about 21/2 percent by weight of CeO 2 , consolidating said powder mixture into a solid billet, and mechanically reducing said solid billet into an electrical contact body.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1980-04-18 | 1980-10-18 | 1981-04-19 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1984-04-18 | 1984-10-18 | 1985-04-19 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1988-04-18 | 1988-10-18 | 1989-04-19 | $7700.00 | Window Closed / Lapsed |