Rare earth metal silicide alloys
Assignee: Foote Mineral Co
•
Filing: 1975-08-05
•
Granted: 1977-04-19
•
Expires: 1995-08-05
Abstract
Abstract Rare earth metal silicide alloys comprising about 25 to about 40% rare earth metals, about 35 to about 50% Si, about 5 to about 25% Fe, about 2 to about 8% Ca, about 2 to about 4% Ba and about 1 to about 3% Sr, the proportions based on the weight of the alloy are disclosed. Also disclosed is a method of making rare earth metal silicide alloys and a method of treating high strength-low alloy steel with the rare earth metal silicide alloys of the invention.
Inventors
- 👤 John O. Staggers
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-06 09:01
CPC Classifications
C; C22; C22C; C22C30/00; C21; C21C; C21C7/00; C21C7/04; C21C7/076; Y; Y02; Y02P; Y02P10/00; Y02P10/20
Claims Analysis
Total Claims: 11
Claim 1
Independent Claim
55 words
A rare earth metal silicide alloy comprising about 25 to about 40% rare earth metals, about 35 to about 50% Si, about 5 to about 25% Fe, about 2 to about 8% Ca, about 2 to about 4% Ba and about 1 to about 3% Sr, the proportions based on the weight of the alloy.
Claim 2
Dependent Claim
55 words
A rare earth metal silicide alloy comprising about 25 to about 40% rare earth metals, about 35 to about 50% Si, about 5 to about 25% Fe, about 2 to about 8% Ca, about 2 to about 4% Ba and about 1 to about 3% Sr, the proportions based on the weight of the alloy.
Claim 3
Dependent Claim
31 words
The rare earth metal silicide alloy of claim 1 comprising about 32.5% rare earth metals, about 42.5% Si, about 15% Fe, about 5% Ca, about 3% Ba and about 2% Sr.
Claim 4
Dependent Claim
25 words
The rare earth silicide alloy of claim 1 wherein the ratio of rare earth metals to alkaline earth metals is about 3:1 to about 4:1.
Claim 5
Independent Claim
154 words
A method for producing rare earth metal silicide alloys which comprises carbothermically reducing agglomerated rare earth metal compounds, silica and iron at temperatures in excess of about 3500° F. in which said components are combined so that the resultant rare earth metal silicide alloys comprise about 25 to about 40% rare earth metals, about 35 to about 50% Si, about 5 to about 25% Fe, about 2 to about 8% Ca, aboout 2 to about 4% Ba and about 1 to about 3%, Sr, the proportions based on the weight of the alloys, the ratio of silica to iron present in the reduction process being from about 8:1 to about 12:1, and the amount of carbon present in the reduction process being in excess of the stoichiometric quantity required for reduction of the rare earth metal oxides, other metal oxides in the rare earth metal compounds and the silica present in the reduction process.
Claim 6
Independent Claim
154 words
A method for producing rare earth metal silicide alloys which comprises carbothermically reducing agglomerated rare earth metal compounds, silica and iron at temperatures in excess of about 3500° F. in which said components are combined so that the resultant rare earth metal silicide alloys comprise about 25 to about 40% rare earth metals, about 35 to about 50% Si, about 5 to about 25% Fe, about 2 to about 8% Ca, aboout 2 to about 4% Ba and about 1 to about 3%, Sr, the proportions based on the weight of the alloys, the ratio of silica to iron present in the reduction process being from about 8:1 to about 12:1, and the amount of carbon present in the reduction process being in excess of the stoichiometric quantity required for reduction of the rare earth metal oxides, other metal oxides in the rare earth metal compounds and the silica present in the reduction process.
Claim 7
Dependent Claim
21 words
The method of claim 4 wherein the ratio of silica to iron present in the carbothermic reduction process is about 10:1.
Claim 8
Dependent Claim
52 words
The process of claim 4 wherein the rare earth metal silicide alloy produced comprises about 32.5% rare earth metals, about 42.5% Si, about 15% Fe, about 5% Ca, about 3% Ba and about 2% Sr, and the ratio of rare earth metals to alkaline earth metals is about 3:1 to about 4:1.
Claim 9
Independent Claim
90 words
A method for treatment of HSLA steels which comprises treating molten HSLA steels with a sufficient quantity of a rare earth metal silicide alloy comprising about 25 to about 40% rare earth metals, about 35 to about 50% Si, about 5 to about 25% Fe, about 2 to about 8% Ca, about 2 to about 4% Ba and about 1 to about 3% Sr, the proportions based on the weight of the alloy, to produce a HSLA steel having a residual rare earth metal to sulfur ratio of about 1.
Claim 10
Independent Claim
90 words
A method for treatment of HSLA steels which comprises treating molten HSLA steels with a sufficient quantity of a rare earth metal silicide alloy comprising about 25 to about 40% rare earth metals, about 35 to about 50% Si, about 5 to about 25% Fe, about 2 to about 8% Ca, about 2 to about 4% Ba and about 1 to about 3% Sr, the proportions based on the weight of the alloy, to produce a HSLA steel having a residual rare earth metal to sulfur ratio of about 1.
Claim 11
Dependent Claim
40 words
The method of claim 8 wherein the HSLA steels are treated with a rare earth metal silicide alloy comprising about 32.5% rare earth metals, about 42.5% Si, about 15% Fe, about 5% Ca, about 3% Ba, and about 2% Sr.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1980-04-18 | 1980-10-18 | 1981-04-19 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1984-04-18 | 1984-10-18 | 1985-04-19 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1988-04-18 | 1988-10-18 | 1989-04-19 | $7700.00 | Window Closed / Lapsed |