Abstract
Abstract Method for forming a bond (hermetic seal) between sapphire and glass. In the preferred form of the invention, the sapphire and glass surfaces to be bonded each have applied to them thin films of chromium, copper, nickel and gold. The inner chromium film is several hundred angstroms thick, the copper and nickel films have a total thickness of about 10,000 angstroms and together comprise an intermediate film, and the outer gold film is about 20,000 angstroms thick. The thin films are applied in a vacuum by direct evaporation or vapor plating or by sputtering. A bond or hermetic seal is effected between the gold films on the respective sapphire and glass materials. An indium wire is inserted between the gold films and a clamping force is applied to the sapphire and glass materials to cause the indium wire to deform to increase substantially the indium surface area. In a vacuum, heat is applied to the sapphire, glass and indium materials sufficient to cause the indium to liquify. After a time period, for example, 15 to 20 minutes, the heat is removed and the liquified indium is allowed to solidify. The resulting bond is particularly suitable for use in forming a hermetic seal between the sapphire faceplate and glass envelope of a cathode ray tube.
Inventors
- 👤 Stuart M. Lee
- 👤 Jerrett D. Stafford
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-25 23:45
CPC Classifications
C; C03; C03C; C03C27/00; H; H01; H01J; H01J9/00; H01J9/24; H01J9/26; H01J9/263
Claims Analysis
Total Claims: 20
Claim 1
Independent Claim
176 words
A method for forming a bond between sapphire and glass comprising the steps of: 1. with respect to the surface of the sapphire to be bonded to the glass: a. applying an inner film of metal, capable of adhering to sapphire, on said sapphire surface; b. applying an intermediate film of metal on the exposed surface of said inner metal film; c. applying an outer metal film on the exposed surface of said intermediate metal film; 2. with respect to the surface of the glass to be bonded to the sapphire: a. applying an inner film of metal, capable of adhering to glass, on said glass surface; b. applying an intermediate film of metal on the exposed surface of said inner metal film; c. applying an outer metal film on the exposed surface of said intermediate metal film; 3. placing a metal wire between said outer metal films on said sapphire and glass surfaces and applying a force to said sapphire and glass sufficient to deform plastically said metal wire to increase substantially its surface area;
Claim 2
Independent Claim
176 words
A method for forming a bond between sapphire and glass comprising the steps of: 1. with respect to the surface of the sapphire to be bonded to the glass: a. applying an inner film of metal, capable of adhering to sapphire, on said sapphire surface; b. applying an intermediate film of metal on the exposed surface of said inner metal film; c. applying an outer metal film on the exposed surface of said intermediate metal film; 2. with respect to the surface of the glass to be bonded to the sapphire: a. applying an inner film of metal, capable of adhering to glass, on said glass surface; b. applying an intermediate film of metal on the exposed surface of said inner metal film; c. applying an outer metal film on the exposed surface of said intermediate metal film; 3. placing a metal wire between said outer metal films on said sapphire and glass surfaces and applying a force to said sapphire and glass sufficient to deform plastically said metal wire to increase substantially its surface area;
Claim 3
Dependent Claim
26 words
applying heat to said metal wire sufficient to cause it to liquify while said force is being applied; and 5. allowing the liquified metal to solidify.
Claim 4
Dependent Claim
26 words
applying heat to said metal wire sufficient to cause it to liquify while said force is being applied; and 5. allowing the liquified metal to solidify.
Claim 5
Dependent Claim
14 words
A method according to claim 1 wherein said metal wire is an indium wire.
Claim 6
Dependent Claim
25 words
A method according to claim 2 wherein said inner films on said sapphire and glass surfaces are chromium and wherein said outer films are gold.
Claim 7
Dependent Claim
22 words
A method according to claim 3 wherein each of said intermediate films on said sapphire and glass surfaces comprises two metallic elements.
Claim 8
Dependent Claim
19 words
A method according to claim 4 wherein said two metallic elements of said intermediate films are copper and nickel.
Claim 9
Dependent Claim
50 words
A method according to claim 5 wherein each of said intermediate films on said sapphire and glass surfaces is formed by the deposition of a layer of copper on each of said chromium inner films and by the deposition of a layer of nickel on each of said copper layers.
Claim 10
Dependent Claim
74 words
A method according to claim 6 wherein said films are applied in a vacuum to said sapphire and glass surfaces, wherein said step of applying heat to said indium metal wire is carried out with said indium metal wire and said sapphire and glass surfaces to be bonded located in a vacuum, and wherein the sapphire is maintained at a temperature in excess of the melting point of indium for at least 15 minutes.
Claim 11
Independent Claim
143 words
A method for forming a bond between sapphire and glass comprising the steps of: 1. with respect to the surface of the sapphire to be bonded to the glass, and with said sapphire surface in a vacuum: a. applying a film of chromium on said sapphire surface; b. applying an intermediate film, comprised of copper and nickel, on the exposed surface of said chromium film; c. applying a film of gold on the exposed surface of said intermediate film; 2. with respect to the surface of the glass to be bonded to the sapphire, and with said glass in a vacuum: a. applying a film of chromium on said glass surface; b. applying an intermediate film, comprised of copper and nickel, on the exposed surface of said chromium film; c. applying a film of gold on the exposed surface of said intermediate film;
Claim 12
Independent Claim
143 words
A method for forming a bond between sapphire and glass comprising the steps of: 1. with respect to the surface of the sapphire to be bonded to the glass, and with said sapphire surface in a vacuum: a. applying a film of chromium on said sapphire surface; b. applying an intermediate film, comprised of copper and nickel, on the exposed surface of said chromium film; c. applying a film of gold on the exposed surface of said intermediate film; 2. with respect to the surface of the glass to be bonded to the sapphire, and with said glass in a vacuum: a. applying a film of chromium on said glass surface; b. applying an intermediate film, comprised of copper and nickel, on the exposed surface of said chromium film; c. applying a film of gold on the exposed surface of said intermediate film;
Claim 13
Dependent Claim
77 words
placing an indium wire between said gold films on said sapphire and glass surfaces to be bonded and applying a force to said sapphire and glass sufficient to deform plastically said indium wire to increase substantially its surface area; 4. applying heat to said sapphire, glass and indium wire sufficient to cause said indium wire to liquify while said force is being applied; and 5. while said force is being applied, allowing the liquified indium to solidify.
Claim 14
Dependent Claim
77 words
placing an indium wire between said gold films on said sapphire and glass surfaces to be bonded and applying a force to said sapphire and glass sufficient to deform plastically said indium wire to increase substantially its surface area; 4. applying heat to said sapphire, glass and indium wire sufficient to cause said indium wire to liquify while said force is being applied; and 5. while said force is being applied, allowing the liquified indium to solidify.
Claim 15
Dependent Claim
38 words
A method according to claim 8 wherein each of said intermediate films formed by depositing said copper therein on said exposed surface of the associated chromium film and by depositing said nickel therein on said copper thus deposited.
Claim 16
Dependent Claim
33 words
A method according to claim 8 wherein said respective gold films are applied in a thickness approximately double that of the respective intermediate films on whose exposed surfaces the gold films are applied.
Claim 17
Dependent Claim
39 words
A method according to claim 10 wherein the total thickness of said intermediate and gold films on said sapphire surface and the total thickness of said intermediate and gold films on said glass surface are each about 30,000 angstroms.
Claim 18
Dependent Claim
22 words
A method according to claim 11 wherein said chromium films on said sapphire and said glass surfaces are several hundred angstroms thick.
Claim 19
Dependent Claim
29 words
A method according to claim 10 wherein said step of applying heat to said sapphire, glass and indium wire is carried out with these materials located in a vacuum.
Claim 20
Dependent Claim
29 words
A method according to claim 12 wherein said step of applying heat to said sapphire, glass and indium wire is carried out with these materials located in a vacuum.
References Cited (Backward Citations)
US3107756A
Cited
US3418423A
Cited
US3747173A
Cited
US3798746A
Cited
US3857161A
Cited
US3921885A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1980-04-18 | 1980-10-18 | 1981-04-19 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1984-04-18 | 1984-10-18 | 1985-04-19 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1988-04-18 | 1988-10-18 | 1989-04-19 | $7700.00 | Window Closed / Lapsed |