Cationic bituminous emulsions
Assignee: Georgia-Pacific LLC
•
Filing: 1976-01-02
•
Granted: 1977-04-12
•
Expires: 1996-01-02
Abstract
Abstract A cationic bitumen emulsion stabilized with a polyamine-lignin reaction product is described.
Inventors
- 👤 Charles H. Ludwig
- 👤 Larry B. Fiske
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-29 22:53
CPC Classifications
C; C08; C08L; C08L95/00; C08L95/005
Claims Analysis
Total Claims: 18
Claim 1
Independent Claim
195 words
In a cationic bitumen emulsion wherein from 30 to about 75% by weight of bitumen is dispersed in an aqueous continuous phase using a cationic, water-soluble aliphatic amine salt or quaternary ammonium salt emulsifier, the improvement which comprises a lignin-polyamine reaction product being present in a sufficient amount to stabilize the set time of the emulsion in presence of negatively charged aggregate, said lignin-polyamine reaction product being a lignin heated under alkaline conditions at a pH of at least 10, with from 8 to 35 percent by weight of a water-soluble, aliphatic polyamine at a temperature of at least 100° C until sufficient amount of amine has reacted with the lignin for the reaction product to form aqueous solutions with the emulsifier under acid conditions, said lignin being soluble in an aqueous alkaline medium said polyamine containing at least one primary or secondary amine group and said polyamine having a molecular weight of from about 60 to 300 and containing from 20 to 47 percent organically bound amino-type nitrogen with only one amino-type nitrogen atom being attached to a particular carbon atom and said amino-type nitrogen being the only functional substituent on said carbon atom.
Claim 2
Dependent Claim
195 words
In a cationic bitumen emulsion wherein from 30 to about 75% by weight of bitumen is dispersed in an aqueous continuous phase using a cationic, water-soluble aliphatic amine salt or quaternary ammonium salt emulsifier, the improvement which comprises a lignin-polyamine reaction product being present in a sufficient amount to stabilize the set time of the emulsion in presence of negatively charged aggregate, said lignin-polyamine reaction product being a lignin heated under alkaline conditions at a pH of at least 10, with from 8 to 35 percent by weight of a water-soluble, aliphatic polyamine at a temperature of at least 100° C until sufficient amount of amine has reacted with the lignin for the reaction product to form aqueous solutions with the emulsifier under acid conditions, said lignin being soluble in an aqueous alkaline medium said polyamine containing at least one primary or secondary amine group and said polyamine having a molecular weight of from about 60 to 300 and containing from 20 to 47 percent organically bound amino-type nitrogen with only one amino-type nitrogen atom being attached to a particular carbon atom and said amino-type nitrogen being the only functional substituent on said carbon atom.
Claim 3
Dependent Claim
18 words
A composition according to claim 1 wherein the polyamine heated with lignin is a primary or secondary polyamine.
Claim 4
Dependent Claim
12 words
A composition according to claim 2 wherein the lignin is a lignosulfonate.
Claim 5
Dependent Claim
35 words
A composition according to claim 3 wherein the lignosulfonate is heated with the amine until at least 25% of the lignin is converted to a product soluble in 80% ethanol at a pH above 10.
Claim 6
Dependent Claim
23 words
A composition according to claim 4 wherein the polyamine is a polyalkylenimine having a molecular weight in the range of 60 to 220.
Claim 7
Dependent Claim
27 words
A composition of claim 5 wherein the polyamine is heated with the lignosulfonate in an amount of from about 12 to 20 weight percent of the lignosulfonate.
Claim 8
Dependent Claim
28 words
A composition according to claim 2 wherein the lignin is a kraft lignin heated with the polyamine in an amount of from about 12 to 20 weight percent.
Claim 9
Dependent Claim
43 words
A composition according to claim 7 wherein the emulsifier is selected from the group consisting essentially of N-alkyl polymethylene diamine and polyalkoxylated derivatives thereof and N-alkyl quaternary ammonium chloride and polyalkoxylated derivatives thereof, said alkyl substituent having from 8 to 22 carbon atoms.
Claim 10
Dependent Claim
22 words
A composition according to claim 8 wherein the emulsifier is N-alkyl-1,3-propane diamine, said alkyl radical having from 12 to 18 carbon atoms.
Claim 11
Dependent Claim
58 words
A composition according to claim 9 wherein the lignin is a lignosulfonate heated with from 12 to 20% of a primary or a secondary polyamine having a molecular weight in the range of 60 to 220 until at least 25 percent of the lignosulfonate is converted to a product soluble in 80% ethanol at a pH above 10.
Claim 12
Dependent Claim
194 words
In a process for the preparation of a cationic bitumen emulsion wherein from 30 to about 75 weight percent of bitumen is dispersed in an aqueous continuous phase using a cationic, water-soluble aliphatic amine salt or quaternary ammonium salt emulsifier, the improvement which comprises adding to the emulsifier a lignin-polyamine reaction product in a sufficient amount to stabilize the set time of the emulsion in presence of negatively charged aggregate, said lignin-polyamine reaction product being a lignin heated under alkaline conditions at a pH of at least 10 with from 8 to 35 percent by weight of a water-soluble, aliphatic polyamine at a temperature of at least 100° C for a reaction time up to 65 hours until a major portion of the polyamine has reacted with the lignin, said lignin being soluble in an aqueous alkaline medium said polyamine containing at least one primary or secondary group, and said polyamine having a molecular weight of from about 60 to 300 and containing from 20 to 47% organically bound nitrogen with not more than one amino-nitrogen being attached to a carbon atom and said amino-nitrogen being the only functional substituent on said carbon atom.
Claim 13
Dependent Claim
194 words
In a process for the preparation of a cationic bitumen emulsion wherein from 30 to about 75 weight percent of bitumen is dispersed in an aqueous continuous phase using a cationic, water-soluble aliphatic amine salt or quaternary ammonium salt emulsifier, the improvement which comprises adding to the emulsifier a lignin-polyamine reaction product in a sufficient amount to stabilize the set time of the emulsion in presence of negatively charged aggregate, said lignin-polyamine reaction product being a lignin heated under alkaline conditions at a pH of at least 10 with from 8 to 35 percent by weight of a water-soluble, aliphatic polyamine at a temperature of at least 100° C for a reaction time up to 65 hours until a major portion of the polyamine has reacted with the lignin, said lignin being soluble in an aqueous alkaline medium said polyamine containing at least one primary or secondary group, and said polyamine having a molecular weight of from about 60 to 300 and containing from 20 to 47% organically bound nitrogen with not more than one amino-nitrogen being attached to a carbon atom and said amino-nitrogen being the only functional substituent on said carbon atom.
Claim 14
Dependent Claim
27 words
A process according to claim 11 wherein the lignin and polyamine are reacted at a temperature of 130° to 150° C for from 2 to 8 hours.
Claim 15
Dependent Claim
19 words
A process according to claim 12 wherein the lignin is heated with 12 to 20 percent of the polyamine.
Claim 16
Dependent Claim
23 words
A process according to claim 13 wherein the polyamine is a polyalkylenimine having a molecular weight in the range of 60 to 220.
Claim 17
Dependent Claim
43 words
A process according to claim 13 wherein the emulsifier is selected from the group consisting essentially of N-alkyl polymethylene diamine and polyalkoxylated derivatives thereof and N-alkyl quaternary ammonium chloride and polyalkoxylated derivatives thereof, said alkyl substituent having from 8 to 22 carbon atoms.
Claim 18
Dependent Claim
34 words
A process according to claim 13 wherein the lignin is a lignosulfonate which is reacted with the polyalkyleneimine until at least 25% of the lignin is converted to a product soluble in 80% ethanol.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1980-04-11 | 1980-10-11 | 1981-04-12 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1984-04-11 | 1984-10-11 | 1985-04-12 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1988-04-11 | 1988-10-11 | 1989-04-12 | $7700.00 | Window Closed / Lapsed |