Method of washing glassware and inhibited cleaning solution and additive composition useful therein
Assignee: Diversey Wyandotte Corp
•
Filing: 1975-11-05
•
Granted: 1977-04-12
•
Expires: 1995-11-05
Abstract
Abstract Soiled hot end coated glassware having a substantially colorless and transparent thin protective coating thereon including an organic coating material is washed in an inhibited aqueous caustic soda cleaning solution to inhibit the deleterious effects of repeated washings and thereby increase the effective life of the protective coating. The cleaning solution comprises on a weight basis from 0.3 to 6% of caustic soda, from 0.01% to 0.3% of at least one soluble zinc containing compound when calculated as zinc oxide, and the remainder water. Other ingredients which may be present include from 0.002 to 0.05% of a synthetic organic phosphate ester anionic surfactant having hydrotrophic properties, from 0.001 to 0.03% of a low foaming synthetic alkoxylated nonionic surfactant, and from 0.008 to 0.2% of a hard water conditioning sequesterant. The protective coating preferably comprises polyethylene, and for best results a metal oxide layer is applied to the surface of the glassware while hot and a layer of the organic coating material is applied thereover and bonded thereto. A novel inhibited caustic soda cleaning solution having the above composition is provided, and also a liquid additive composition which is useful in preparing the cleaning solution and maintaining the ingredients thereof at proper concentrations. The desirable properties of the hot end coated glassware such as improved lubricity and increased strength are preserved and unsightly discoloration is prevented.
Inventors
- 👤 Malachi E. Sorgenfrei
- 👤 Otto T. Aepli
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-30 06:30
CPC Classifications
C; C11; C11D; C11D3/00; C11D3/02; C11D3/04; C11D3/044; C11D1/00; C11D1/38; C11D1/42; C11D1/44; C11D3/046; C11D3/12; C11D3/1213
Claims Analysis
Total Claims: 16
Claim 1
Independent Claim
275 words
A liquid additive composition for aqueous caustic soda cleaning solutions used in washing coated glass containers having a thin coating thereon including a coating of an organic hot end coating material applied to the glass containers while hot, the resultant hot end coating initially being substantially free of objectionable color and imparting abrasion resistance to the glass containers and being altered by repeated washings therein whereby the glass containers exhibit loss of abrasion resistance or an objectionable discoloration appears, the additive composition consisting essentially of on a weight basis from about 15 to 20% of caustic soda, from about 2 to 5% of at least one soluble zinc containing compound when calculated as zinc oxide, from about 0.5 to 1% of at least one synthetic organic phosphate ester anionic surfactant, from about 0.2 to 0.6% of at least one low foaming synthetic alkoxylated nonionic surfactant, from about 2 to 5% of at least one hard water conditioning sequesterant which sequesters calcium ion or magnesium ion from hard water contaning the same and the remainder water, the said caustic soda, zinc containing compound, anionic surfactant, nonionic surfactant and sequesterant being dissolved in the liquid additive composition to form a homogeneous aqueous solution thereof which is compatible with aqueous caustic soda cleaning solutions, and the said liquid additive composition being effective to prolong the useful life of the said hot end coating including the coating of the organic hot end coating material when added to said aqueous caustic soda cleaning solutions in an amount to provide the zinc containing compound therein in a concentration of from about 0.01 to 0.3% by weight when calculated as zinc oxide.
Claim 2
Dependent Claim
275 words
A liquid additive composition for aqueous caustic soda cleaning solutions used in washing coated glass containers having a thin coating thereon including a coating of an organic hot end coating material applied to the glass containers while hot, the resultant hot end coating initially being substantially free of objectionable color and imparting abrasion resistance to the glass containers and being altered by repeated washings therein whereby the glass containers exhibit loss of abrasion resistance or an objectionable discoloration appears, the additive composition consisting essentially of on a weight basis from about 15 to 20% of caustic soda, from about 2 to 5% of at least one soluble zinc containing compound when calculated as zinc oxide, from about 0.5 to 1% of at least one synthetic organic phosphate ester anionic surfactant, from about 0.2 to 0.6% of at least one low foaming synthetic alkoxylated nonionic surfactant, from about 2 to 5% of at least one hard water conditioning sequesterant which sequesters calcium ion or magnesium ion from hard water contaning the same and the remainder water, the said caustic soda, zinc containing compound, anionic surfactant, nonionic surfactant and sequesterant being dissolved in the liquid additive composition to form a homogeneous aqueous solution thereof which is compatible with aqueous caustic soda cleaning solutions, and the said liquid additive composition being effective to prolong the useful life of the said hot end coating including the coating of the organic hot end coating material when added to said aqueous caustic soda cleaning solutions in an amount to provide the zinc containing compound therein in a concentration of from about 0.01 to 0.3% by weight when calculated as zinc oxide.
Claim 3
Dependent Claim
72 words
The additive composition of claim 1 wherein the caustic soda is present in an amount of about 18%, the zinc containing compound is present in an amount of about 3.5% when calculated as zinc oxide, the anionic surfactant is present in an amount of about 0.8%, the nonionic surfactant is present in an amount of about 0.4%, the sequesterant is present in an amount of about 3.6%, and the remainder is water.
Claim 4
Dependent Claim
29 words
The additive composition of claim 1 wherein the anionic surfactant is selected from the group consisting of alkylphenol polyglycol ether phosphates and the alkali metal and ammonium salts thereof.
Claim 5
Dependent Claim
83 words
The additive composition of claim 1 wherein the sequesterant is a mixture consisting essentially of (1) at least one sequestering agent selected from the group consisting of sugar acids and the alkali metal and ammonium salts thereof, and (2) at least one sequestering agent selected from the group consisting of α, α', α "-amino tris-(methyl phosphonic acid) and the alkali metal and ammonium salts thereof, the sequesterant containing a ratio of sequestering agent (1) to sequestering agent (2) from about 15:1 to 25:1.
Claim 6
Dependent Claim
63 words
The additive composition of claim 1 wherein the nonionic surfactant is a polyoxyethylene-polyoxypropylene adduct of ethylenediamine corresponding to the structural formula ##STR3##wherein y is an integer of a numerical value to insure that the ethylene oxide residua constitute a maximum of about 20% by weight of the total weight of the molecule, the molecular weight of the molecule being about 900 to 7800.
Claim 7
Dependent Claim
162 words
The additive composition of claim 1 wherein the anionic surfactant is selected from the group consisting of alkylphenol polyglycol ether phosphates and the alkali metal and ammonium salts thereof, the sequesterant is a mixture consisting essentially of (1) at least one sequestering agent selected from the group consisting of sugar acids and the alkali metal and ammonium salts thereof, and (2) at least one sequestering agent selected from the group consisting of α, α', α "-amino tris-(methyl phosphonic acid) and the alkali metal and ammonium salts thereof, the sequesterant containing a ratio of sequestering agent (1) to sequestering agent (2) from about 15:1 to 25:1, and the nonionic surfactant is a polyoxyethylene-polyoxypropylene adduct of ethylenediamine corresponding to the structural formula: ##STR4##wherein y is an integer of a numerical value to insure that the ethylene oxide residua constitute a maximum of about 20% by weight of the total weight of the molecule, the molecular weight of the molecule being about 900 to 7800.
Claim 8
Dependent Claim
72 words
The additive composition of claim 6, wherein the caustic soda is present in an amount of about 18%, the zinc containing compound is present in an amount of about 3.5% when calculated as zinc oxide, the anionic surfactant is present in an amount of about 0.8%, the nonionic surfactant is present in an amount of about 0.4%, the sequesterant is present in an amount of about 3.6%, and the remainder is water.
Claim 9
Dependent Claim
200 words
An aqueous caustic soda cleaning solution for use in washing coated glass containers having a thin coating thereon including a coating of an organic hot end coating material applied to the glass containers while hot, the resultant hot end coating initially being substantially free of objectionable color and imparting abrasion resistance to the glass containers and being altered by repeated washings therein whereby the glass containers exhibit loss of abrasion resistance or an objectionable discoloration appears, the aqueous caustic soda cleaning solution consisting essentially of on a weight basis from 0.3 to 6% of caustic soda, from 0.01 to 0.3% of at least one soluble zinc containing compound when calculated as zinc oxide, from 0.002 to 0.05% of at least one synthetic organic phosphate ester anionic surfactant, from 0.001 to 0.03% of at least one low foaming synthetic alkoxylated nonionic surfactant, from 0.008 to 0.2% of at least one hard water conditioning sequesterant which sequesters calcium ion or magnesium ion from hard water containing the same, and the remainer water, the said aqueous caustic soda cleaning solution being effective to prolong the useful life of the said hot end coating including the coating of the organic hot end coating material.
Claim 10
Dependent Claim
200 words
An aqueous caustic soda cleaning solution for use in washing coated glass containers having a thin coating thereon including a coating of an organic hot end coating material applied to the glass containers while hot, the resultant hot end coating initially being substantially free of objectionable color and imparting abrasion resistance to the glass containers and being altered by repeated washings therein whereby the glass containers exhibit loss of abrasion resistance or an objectionable discoloration appears, the aqueous caustic soda cleaning solution consisting essentially of on a weight basis from 0.3 to 6% of caustic soda, from 0.01 to 0.3% of at least one soluble zinc containing compound when calculated as zinc oxide, from 0.002 to 0.05% of at least one synthetic organic phosphate ester anionic surfactant, from 0.001 to 0.03% of at least one low foaming synthetic alkoxylated nonionic surfactant, from 0.008 to 0.2% of at least one hard water conditioning sequesterant which sequesters calcium ion or magnesium ion from hard water containing the same, and the remainer water, the said aqueous caustic soda cleaning solution being effective to prolong the useful life of the said hot end coating including the coating of the organic hot end coating material.
Claim 11
Dependent Claim
79 words
The caustic soda cleaning solution of claim 8 wherein the caustic soda is present in an amount from 2 to 4%, the zinc containing compound is present in an amount from 0.03 to 0.1% when calculated as zinc oxide, the anionic surfactant is present in an amount from 0.01 to 0.03%, the nonionic surfactant is present in an amount from 0.005 to 0.01%, the sequesterant is present in an amount from 0.03 to 0.1%, and the remainder is water.
Claim 12
Dependent Claim
31 words
The caustic soda cleaning solution of claim 8 wherein the anionic surfactant is selected from the group consisting of alkylphenol polyglycol ether phosphates and the alkali metal and ammonium salts thereof.
Claim 13
Dependent Claim
86 words
The caustic soda cleaning solution of claim 8 wherein the sequesterant is a mixture consisting essentially of (1) at least one sequestering agent selected from the group consisting of sugar acids and the alkali metal and ammonium salts thereof, and (2) at least one sequestering agent selected from the group consisting of α, α ', α "-amino tris-(methyl phosphonic acid) and the alkali metal and ammonium salts thereof, the sequesterant containing a ratio of sequestering agent (1) to sequestering agent (2) from about 15:1 to 25:1.
Claim 14
Dependent Claim
65 words
The caustic soda cleaning solution of claim 8 wherein the nonionic surfactant is a polyoxyethylene-polyoxypropylene adduct of ethylenediamine corresponding to the structural formula ##STR5##wherein y is an integer of a numerical value to insure that the ethylene oxide residua constitute a maximum of about 20% by weight of the total weight of the molecule, the molecular weight of the molecule being about 900 to 7800.
Claim 15
Dependent Claim
165 words
The caustic soda cleaning solution of claim 8 wherein the anionic surfactant is selected from the group consisting essentially of alkylphenol polyglycol ether phosphates and the alkali metal and ammonium salts thereof, the sequesterant is a mixture comprising (1) at least one sequestering agent selected from the group consisting of sugar acids and the alkali metal and ammonium salts thereof, and (2) at least one sequestering agent selected from the group consisting of α, α ', α ",-amino tris-(methyl phosphonic acid) and the alkali metal and ammonium salts thereof, the sequesterant containing a ratio of sequestering agent (1) to sequestering agent (2) from about 15:1 to 25:1, and the nonionic surfactant is a polyoxyethylene-polyoxypropylene adduct of ethylenediamine corresponding to the structural formula: ##STR6## wherein y is an integer of a numerical value to insure that the ethylene oxide residua constitute a maximum of about 20% by weight of the total weight of the molecule, the molecular weight of the molecule being about 900 to 7800.
Claim 16
Dependent Claim
74 words
The caustic soda cleaning solution of claim 13 wherein the caustic soda is present in an amount of about 3%, the zinc containing compound is present in an amount of about 0.06% when calculated as zinc oxide, the anionic surfactant is present in an amount of about 0.013%, the nonionic surfactant is present in an amount of about 0.007%, the sequesterant is present in an amount of about 0.06%, and the remainder is water.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1980-04-11 | 1980-10-11 | 1981-04-12 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1984-04-11 | 1984-10-11 | 1985-04-12 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1988-04-11 | 1988-10-11 | 1989-04-12 | $7700.00 | Window Closed / Lapsed |