US4017379A
Expired / Lapsed
US
⏱️ 0.0 years remaining
Conversion process of hydrocarbons
Assignee: Showa Shell Sekiyu KK
•
Filing: 1975-05-07
•
Granted: 1977-04-12
•
Expires: 1995-05-07
Abstract
Abstract This invention relates to a process for effectively and completely converting into a useful hydrocarbon oil comprising naphtha, kerosene and gas oil with high cracking rate, the tar-sand bitumen and the vacuum residues from various petroleum or origins which are difficult to treat in comparison with the ordinary crude oil and contain large amount of asphaltenes and resins according to the combined process of the thermal cracking and hydrocracking.
Inventors
- 👤 Tetsuya Iida
- 👤 Hideo Saori
- 👤 Masao Inoguchi
- 👤 Hiroo Tominaga
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-01 14:32
CPC Classifications
C; C10; C10G; C10G65/00; C10G65/02; C10G65/10; B; B01; B01J; B01J23/00; B01J23/70; B01J23/76; B01J23/84; B01J23/85; B01J23/88
Claims Analysis
Total Claims: 9
Claim 1
Independent Claim
151 words
A process for converting hydrocarbon wherein the process comprises (a) a step of thermal cracking of a tar-sand bitumen and vacuum residues having a boiling point of more than 530° C from various petroleum origins at a temperture of 400°14 800° C, a hydrogen pressure of 1-200 Kg/cm 2 and a contact time of 10-500 seconds to increase the amount of asphaltenes contained in the thermal cracked oil to 1.2 - 3.0 times of the amount of asphaltenes originally contained in the starting material and (b) a step of hydrocracking of the entire product oil obtained by the process of the step (a) at a temperature of 350°-500° C, a hydrogen pressure of 50-300 Kg/cm 2 and a liquid hourly space velocity of 0.1 - 5, in the presence of a catalyst supporting a metal or metals selected from the 6th and 8th groups of the periodic table on a carrier.
Claim 2
Dependent Claim
151 words
A process for converting hydrocarbon wherein the process comprises (a) a step of thermal cracking of a tar-sand bitumen and vacuum residues having a boiling point of more than 530° C from various petroleum origins at a temperture of 400°14 800° C, a hydrogen pressure of 1-200 Kg/cm 2 and a contact time of 10-500 seconds to increase the amount of asphaltenes contained in the thermal cracked oil to 1.2 - 3.0 times of the amount of asphaltenes originally contained in the starting material and (b) a step of hydrocracking of the entire product oil obtained by the process of the step (a) at a temperature of 350°-500° C, a hydrogen pressure of 50-300 Kg/cm 2 and a liquid hourly space velocity of 0.1 - 5, in the presence of a catalyst supporting a metal or metals selected from the 6th and 8th groups of the periodic table on a carrier.
Claim 3
Dependent Claim
45 words
A process as claimed in the claim 1 wherein the tar-sand bitumen and the vacuum residues from the various petroleum origins are thermally cracked at the temperture of 450-530° C, the hydrogen pressure of 20-50 Kg/cm 2 , and the contact time of 100-300 seconds.
Claim 4
Dependent Claim
77 words
A process for claimed in the claim 1 wherein the tar-sand bitumen and the vacuum residues from the various petroleum origins thermally cracked according to the step (a) as claimed in the claim 1 are hydrocracked at the temperature of 390°-450° C, the liquid hourly space velocity of 0.5-1.5 the hydrogen pressure of 100-200 Kg/cm 2 and the hydrogen feed rate of 800-1,500 1-H 2 /1-oil in the presence of the catalyst claimed in the claim 1.
Claim 5
Dependent Claim
28 words
A process claimed in the claim 1 wherein the hydrocracking catalyst is selected from the group comprising Mo--Co, Mo--Ni, W--Ni, Mo--Co--Ni, W--Co--Ni, and W--Co--Ni--Mo supported on the carrier.
Claim 6
Dependent Claim
74 words
A process claimed in claim 4 wherein the carrier is γ-alumina indicating the acidic colour by the benzene azodiphenyl amine indicator of pKa + 1.5 and manufacturing said catalysts from boehmite and boehmite gel by washing alumina gel with alcohol without aging, while controlling the formation of bayerite and then calcining the obtained gel at two steps, the first step of 100°-400° C, 2-10 hrs, and the 2nd step of 400°-700° C, 1-10 hrs.
Claim 7
Dependent Claim
43 words
A process claimed in the claim 5 wherein the carrier is γ-alumina having the properties of the surface of 100-450 m 2 /g, the pore volume of 0.3-0.9 ml/g, the bulk density of 0.3-0.9 g/ml and the mean pore diameter of 50-240 A.
Claim 8
Dependent Claim
45 words
A process claimed the in claim 1, wherein the carrier is boehmite gel having the properties of the surface area of 150-300 m 2 /g, the pore volume of 0.5-0.8 ml/g, the bulk density of 0.4-0.6 g/ml and the mean pore diameter of 120-160 A.
Claim 9
Dependent Claim
52 words
A process claimed in the claim 1, wherein the hydrocracking catalyst possesses the properties of the surface area of 196-210 m 2 /g, the pore volume of 0.57-0.58 ml/g, the mean pore diameter of 134-141 A, the bulk density of 0.65-0.67 g/ml and the bulk crushing strength of 5.4-6.6 Kg/cm 2 .
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1980-04-11 | 1980-10-11 | 1981-04-12 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1984-04-11 | 1984-10-11 | 1985-04-12 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1988-04-11 | 1988-10-11 | 1989-04-12 | $7700.00 | Window Closed / Lapsed |