Photosensitive colored glasses
Assignee: Corning Glass Works
•
Filing: 1976-01-02
•
Granted: 1977-04-12
•
Expires: 1996-01-02
Abstract
Abstract The instant invention relates to photosensitive glasses, i.e., glasses which, after an exposure to high energy or actinic radiations, can be heat treated in a certain manner to develop a colored transparent article, or which can be thermally opacified to produce a colored opal glass. More particularly, the instant invention is directed to alkali halide silver halide-containing photosensitive glasses which, through a unique sequence of shortwave radiation exposures and heat treatments, exhibit the total range of colors seen in the visible spectrum either in the transparent or in the opacified state and in three dimensions. The base glass composition can be varied widely, but the presence of silver, alkali oxide, fluorine, at least one of the group consisting of chlorine, bromine, and iodine, and, where ultra-violet radiations comprise the actinic radiations, cerium oxide is required. Multi-colored photographs and other unique decorative effects can be imparted into such glasses. Where desired, polarization effects can be secured in the glasses.
Inventors
- 👤 Joseph E. Pierson
- 👤 Stanley D. Stookey
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-26 17:52
CPC Classifications
C; C03; C03C; C03C4/00; C03C4/04; C03C21/00; C03C23/00; C03C3/00; C03C3/04; C03C3/076; C03C3/11; C03C3/112; C03C8/00; C03C8/14; C03C8/18; C03C2205/00
Claims Analysis
Total Claims: 18
Claim 1
Independent Claim
109 words
A glass article wherein at least a portion thereof is integrally colored by silver, said portion containing microcrystals of alkali fluoride in a concentration of at least 0.005% by volume and having: a. discrete colloidal particles of metallic silver less than about 200A in the smallest dimension; and/or b. metallic silver contained within said alkali fluoride microcrystals, said silver-containing part of the microcrystals being less than about 200A in the smallest dimension; and/or c. a coating of metallic silver on at least a portion of the surface of said alkali fluoride microcrystals, the portion of the microcrystal coated with silver being less than about 200A in the smallest dimension.
Claim 2
Dependent Claim
109 words
A glass article wherein at least a portion thereof is integrally colored by silver, said portion containing microcrystals of alkali fluoride in a concentration of at least 0.005% by volume and having: a. discrete colloidal particles of metallic silver less than about 200A in the smallest dimension; and/or b. metallic silver contained within said alkali fluoride microcrystals, said silver-containing part of the microcrystals being less than about 200A in the smallest dimension; and/or c. a coating of metallic silver on at least a portion of the surface of said alkali fluoride microcrystals, the portion of the microcrystal coated with silver being less than about 200A in the smallest dimension.
Claim 3
Dependent Claim
14 words
A glass article according to claim 1 wherein said microcrystals exhibit an acicular morphology.
Claim 4
Dependent Claim
34 words
A glass article according to claim 1 wherein said microcrystals consist essentially of sodium fluoride containing at least one silver halide selected from the group consisting of silver chloride, silver bromide, and silver iodide.
Claim 5
Dependent Claim
36 words
A glass article according to claim 3 exhibiting transparency wherein the concentration of said microcrystals does not exceed about 0.1% by volume and the size of said microcrystals does not exceed about 0.1 micron in diameter.
Claim 6
Dependent Claim
44 words
A glass article according to claim 4 wherein the content of silver is held below about 0.1% by weight, the fluoride content does not exceed about 3% by weight, and the total chloride and/or bromide and/or iodide is maintained below about 2% by weight.
Claim 7
Dependent Claim
13 words
A glass article according to claim 1 which also contains CeO 2 .
Claim 8
Dependent Claim
17 words
A glass article according to claim 1 wherein the glass composition is a sodium silicate based glass.
Claim 9
Dependent Claim
72 words
A glass article according to claim 7 wherein said base glass consists essentially, by weight on the oxide basis, of about 10-20% Na 2 O, 0.0005-0.3% Ag, 1-4% F, 0.01-0.2% CeO 2 , an amount of at least one halide selected from the group consisting of Cl, Br, and I sufficient to react stoichiometrically with the Ag, but not more than a total of about 3%, and the remainder SiO 2 .
Claim 10
Dependent Claim
26 words
A glass article according to claim 8 wherein said base glass also contains up to 18% ZnO and/or up to 10% Al 2 O 3 .
Claim 11
Dependent Claim
16 words
A glass article according to claim 9 wherein said SiO 2 content ranges between about 60-75%.
Claim 12
Dependent Claim
39 words
A glass article according to claim 8 wherein said base glass also contains up to about 1% Sb 2 O 3 and/or up to about 0.1% SnO, the total Sb 2 O 3 + SnO not exceeding about 1%.
Claim 13
Dependent Claim
16 words
A glass article according to claim 1 wherein said integrally colored portion is a color photograph.
Claim 14
Dependent Claim
14 words
A glass article according to claim 1 wherein said integrally colored portion is polychromatic.
Claim 15
Dependent Claim
14 words
A glass article according to claim 1 wherein said integrally colored portion is three-dimensional.
Claim 16
Dependent Claim
14 words
A glass article according to claim 1 wherein said integrally colored portion is monochromatic.
Claim 17
Dependent Claim
19 words
A glass article according to claim 1 wherein said integrally colored portion is of a different color from yellow.
Claim 18
Dependent Claim
14 words
A glass article according to claim 1 wherein said integrally colored portion is polarizing.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1980-04-11 | 1980-10-11 | 1981-04-12 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1984-04-11 | 1984-10-11 | 1985-04-12 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1988-04-11 | 1988-10-11 | 1989-04-12 | $7700.00 | Window Closed / Lapsed |