Process of making laminated structural member
Assignee: General Cable Industries Inc
•
Filing: 1975-02-10
•
Granted: 1977-04-05
•
Expires: 1995-02-10
Abstract
Abstract A process for making a laminated structural member is disclosed in which the member is fabricated with one layer of sheet material such as plywood or fiberboard and an adjacent layer bonded thereto and formed from a mixture of scrap particles of thermoplastic wire and cable insulation, wood particles, comminuted paper, sawdust, and a suitable resin binder. The fabrication process is carried out by initially forming a mixture of reclaimed thermoplastic wire or cable insulation, a thermosetting binder, a wood-like filler, and a mold release agent. The mixture is then placed in a mold with the sheet material and subjected to heat and pressure to form a laminated structural member.
Inventors
- 👤 John Philip Pringle
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-05 01:49
CPC Classifications
B; B65; B65H; B65H75/00; B65H75/50; B29; B29B; B29B17/00; B29B17/0026; H; H01; H01B; H01B3/00; H01B3/18; H01B3/48; H01B3/52; B29L; B29L2031/00; B29L2031/704; B65H2701/00; B65H2701/50; B65H2701/51; B65H2701/512; B65H2701/5126; Y; Y02; Y02W; Y02W30/00; Y02W30/50; Y02W30/62
Claims Analysis
Total Claims: 8
Claim 1
Independent Claim
218 words
A process for forming a flexible laminated structural member comprising: a. admixing from about 30 to about 60 weight percent of particulate thermoplastic material wherein at least 50 percent of the particles have a particle dimension of from about 1/16 inch to about 1/4 inch with from aout 70 to about 40 weight percent of a particulate wood filler material to form a first mixture; b. admixing from about 11 to about 18 weight percent of a thermosetting binder, based upon the weight of the first mixture, to the first mixture to form a resultant mixture; c. placing a sheet material having at least one surface into a mold; d. placing an effective amount of the resultant mixture into the mold adjacent to at least one of the surfaces of the sheet material to cover the surface to a desired depth; and e. heating and compressing the resultant mixture and the sheet material at a temperature in the range from about 250° F. to about 450° F. and at a pressure from about 75 psi to about 350 psi for a period of time effective to enable the particulate thermoplastic material to form flexible discrete zones whereby the discrete zones bond together and said resulant mixture bonds to said sheet material to form a flexible laminated structural member.
Claim 2
Dependent Claim
218 words
A process for forming a flexible laminated structural member comprising: a. admixing from about 30 to about 60 weight percent of particulate thermoplastic material wherein at least 50 percent of the particles have a particle dimension of from about 1/16 inch to about 1/4 inch with from aout 70 to about 40 weight percent of a particulate wood filler material to form a first mixture; b. admixing from about 11 to about 18 weight percent of a thermosetting binder, based upon the weight of the first mixture, to the first mixture to form a resultant mixture; c. placing a sheet material having at least one surface into a mold; d. placing an effective amount of the resultant mixture into the mold adjacent to at least one of the surfaces of the sheet material to cover the surface to a desired depth; and e. heating and compressing the resultant mixture and the sheet material at a temperature in the range from about 250° F. to about 450° F. and at a pressure from about 75 psi to about 350 psi for a period of time effective to enable the particulate thermoplastic material to form flexible discrete zones whereby the discrete zones bond together and said resulant mixture bonds to said sheet material to form a flexible laminated structural member.
Claim 3
Dependent Claim
37 words
The process of claim 1 wherein the particulate thermoplastic material is scrap thermoplastic wire and cable insulation and at least 50 percent by weight of the particulate thermoplastic material has an average particle dimension of 1/8 inch.
Claim 4
Dependent Claim
30 words
The process of claim 1 wherein at least 50 percent by weight of the particulate wood filler material has a particle dimension from about 1/8 inch to about 3/8 inch.
Claim 5
Dependent Claim
36 words
The process of claim 1 wherein the sheet material is provided with a thickness from about 1/4 inch to about 1/2 inch and the sheet material is selected from a group consisting of fiberboard and plywood.
Claim 6
Dependent Claim
67 words
The process of claim 4 wherein the resultant mixture comprises from about 27 to about 51 weight percent particulate thermoplastic material, from about 34 to about 63 weight percent wood filler material, from about 10 to about 15 weight percent thermosetting binder, and an effective amount of a mold release agent to aid, after the heating and compressing step, in removing the resultant mixture from the mold.
Claim 7
Dependent Claim
13 words
The process of claim 5 wherein said thermosetting binder is a phenolic resin.
Claim 8
Dependent Claim
66 words
The process of claim 6 wherein said sheet material has a thickness of about 3/8 inch and said heating and compressing is carried out at a temperature in the range of from about 300° F. to about 350° F. and at a pressure of from about 150 psi to about 250 psi for a period of time of from about 8 minutes to about 20 minutes.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1980-04-04 | 1980-10-04 | 1981-04-05 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1984-04-04 | 1984-10-04 | 1985-04-05 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1988-04-04 | 1988-10-04 | 1989-04-05 | $7700.00 | Window Closed / Lapsed |