Production of aromatic sulfide/sulfone polymers

Claim 2

A process for the production of high molecular weight aromatic sulfide/sulfone polymers which comprises contacting a. at least one dihalo aromatic sulfone represented by the formula ##STR6## where each X is selected from the group consisting of fluorine, chlorine, bromine, and iodine; Z is a divalent radical selected from the group consisting of ##STR7## n is 0 or 1; A is selected from the group consisting of oxygen, sulfur, sulfonyl, and CR 2 ; and each R is selected from the group consisting of hydrogen and alkyl radicals having 1 to about 4 carbon atoms, the total number of carbon atoms in all of the R groups in the molecule being 0 to about 12, b. at least one alkali metal sulfide selected from the group consisting of sodium sulfide, potassium sulfide, rubidium sulfide, and cesium sulfide, c. at least one alkali metal carboxylate represented by the formula R'CO 2 M wherein R' is a hydrocarbyl radical and M is an alkali metal, and d. at least one organic amide, under polymerization conditions including an elevated temperature, a period of time, and proportions of reactants sufficient to cause the reactants to react with each other and from an aromatic sulfide/sulfone polymer having recurring ##STR8## units, where each R, Z, and n is as defined above.

Claim 3

A process according to claim 1 wherein c. is an alkali metal carboxylate wherein R' is a hydrocarbyl radical having from 1 to about 20 carbon atoms, and d. is a cyclic or acyclic amide having from 1 to about 10 carbon atoms per molecule.

Claim 4

A process according to claim 1 wherein (a) can be represented by the formula ##STR9## where each X is selected from the group consisting of fluorine, chlorine, bromine, and iodine, and each R is selected from the group consisting of hydrogen and alkyl radicals having 1 to about 4 carbon atoms, the total number of carbon atoms in each molecule being within the range of 12 to about 24, c. can be represented by the formula R'CO 2 M wherein R' is a hydrocarbyl radical having from 1 to about 20 carbon atoms and M is an alkali metal, and d. is a cyclic or acyclic amide having from 1 to about 10 carbon atoms per molecule.

Claim 5

A process according to claim 1 wherein the temperature of the reaction is in the range of about 170° C to about 240° C under sufficient pressure to maintain liquid phase conditions and further wherein the mole ratio of (a) to (b) is in the range of 0.9:1 to 2:1, the mole ratio of (c) to (b) is in the range of 0.05:1 to 4:1, and the amount of (d) present is 100 grams to 2500 grams per gram mole of (b).

Claim 6

A process according to claim 1 wherein a. is bis(p-chlorophenyl) sulfone, b. is sodium sulfide, c. is lithium acetate dihydrate or lithium benzoate, and d. is N-methyl-2-pyrrolidone.

Claim 7

A process for the production of high molecular weight aromatic sulfide/sulfone polymers which comprises: 1. forming a mixture comprising: a. at least one alkali metal sulfide selected from the group consisting of sodium sulfide, potassium sulfide, rubidium sulfide, and cesium sulfide, b. at least one alkali metal carboxylate represented by the formula R'CO 2 M wherein R' is a hydrocarbyl radical and M is an alkali metal, and c. at least one organic amide, 2. heating the mixture formed in (1) to an elevated temperature and for a period of time sufficient to effect dehydration of said mixture, and 3. adding d. at least one dihalo aromatic sulfone represented by the formula ##STR10## wherein each X is selected from the group consisting of fluorine, chlorine, bromine, and iodine; Z is a divalent radical selected from the group consisting of ##STR11## each n is 0 or 1: A is selected from the group consisting of oxygen, sulfur, sulfonyl, and CR 2 ; and each R is selected from the group consisting of hydrogen and alkyl radicals having 1 to about 4 carbon atoms, the total number of carbon atoms in all of the R groups in the molecule being 0 to about 12, to the heated mixture of (1) and subjecting the mixture thus formed to polymerization conditions including an elevated temperature, a period of time, and proportions of reactants sufficient to cause the reactants to react with each other and form an aromatic sulfide/sulfone polymer having recurring ##STR12## units, where each R, Z, and n is as defined above.

Claim 8

A process for the production of high molecular weight aromatic sulfide/sulfone polymers which comprises: 1. forming a mixture comprising: a. at least one alkali metal sulfide selected from the group consisting of sodium sulfide, potassium sulfide, rubidium sulfide, and cesium sulfide, b. at least one alkali metal carboxylate represented by the formula R'CO 2 M wherein R' is a hydrocarbyl radical and M is an alkali metal, and c. at least one organic amide, 2. heating the mixture formed in (1) to an elevated temperature and for a period of time sufficient to effect dehydration of said mixture, and 3. adding d. at least one dihalo aromatic sulfone represented by the formula ##STR10## wherein each X is selected from the group consisting of fluorine, chlorine, bromine, and iodine; Z is a divalent radical selected from the group consisting of ##STR11## each n is 0 or 1: A is selected from the group consisting of oxygen, sulfur, sulfonyl, and CR 2 ; and each R is selected from the group consisting of hydrogen and alkyl radicals having 1 to about 4 carbon atoms, the total number of carbon atoms in all of the R groups in the molecule being 0 to about 12, to the heated mixture of (1) and subjecting the mixture thus formed to polymerization conditions including an elevated temperature, a period of time, and proportions of reactants sufficient to cause the reactants to react with each other and form an aromatic sulfide/sulfone polymer having recurring ##STR12## units, where each R, Z, and n is as defined above.

Claim 9

A process according to claim 6 wherein the heating of (2) is carried out under conditions such that the mixture is substantially dehydrated before addition of the dihalo aromatic sulfone and the mixture is cooled prior to addition of (d).

Claim 10

A process according to claim 6 wherein b. is an alkali metal carboxylate wherein R' is a hydrocarbyl radical having from 1 to about 20 carbon atoms, and c. is a cyclic or acyclic amide having from 1 to about 10 carbon atoms per molecule.

Claim 11

A process according to claim 6 wherein (d) can be represented by the formula ##STR13## where each X is selected from the group consisting of fluorine, chlorine, bromine, and iodine, and each R is selected from the group consisting of hydrogen and alkyl radicals having 1 to about 4 carbon atoms, the total number of carbon atoms in each molecule being within the range of 12 to about 24, b. can be represented by the formula R'CO 2 M wherein R' is a hydrocarbyl radical having from 1 to about 20 carbon atoms and M is an alkali metal, and c. is a cyclic or acyclic amide having from 1 to about 10 carbon atoms per molecule.

Claim 12

a process according to claim 6 wherein the temperature of the reaction is in the range of about 170° C to about 240° C under sufficient pressure to maintain liquid phase conditions and further wherein the mole ratio of (d) to (a) is in the range of 0.9:1 to 2:1, the mole ratio of (b) to (a) is in the range of 0.05:1 to 4:1 and the amount of (c) present is 100 grams to 2500 grams per gram mole of (a).

Claim 13

A process according to claim 6 wherein a. is sodium sulfide, b. is lithium acetate dihydrate or lithium benzoate, c. is N-methyl-2-pyrrolidone, and d. is bis(p-chlorophenyl) sulfone.

Claim 14

A process according to claim 1 wherein the temperature of the reaction is in the range of about 170° C. to about 240° C. and under sufficient pressure to maintain liquid phase condition and further wherein the mole ratio of (a) to (b) is 1:1 to 1.03:1 to produce an aromatic sulfide/sulfone polymer exhibiting good melt processability.

Claim 15

A process according to claim 6 wherein the temperature of the reaction is in the range of about 170° C. to about 240° C. and under sufficient pressure to maintain liquid phase conditions and further wherein the mole ratio of (a) to (b) is 1:1 to 1.03:1 to produce an aromatic sulfide/sulfone polymer exhibiting good melt processability.

Claim 16

A process according to claim 13 wherein a. is bis(p-chlorophenyl) sulfone, b. is sodium sulfide, c. is lithium acetate dihydrate, and d. is N-methyl-2-pyrrolidone.

Claim 17

A process according to claim 1 wherein the polymer produced is separated from the reaction mass and then washed with water, at least a portion of the washing being conducted at a temperature of 130°-250° C., for a period of time sufficient to yield a polymeric product exhibiting low ash values and high melt flow stability.

Claim 18

A process according to claim 15 wherein a. is bis(p-chlorophenyl) sulfone, b. is sodium sulfide, c. is lithium acetate dihydrate, and d. is N-methyl-2-pyrrolidone.

Claim 19

A process according to claim 6 wherein the polymer produced is separated from the reaction mass and then washed with water, at least a portion of the washing being conducted at a temperature of 130°-250° C., for a period of time sufficient to yield a polymeric product exhibiting low ash values and high melt flow stability.