Conduction system for thin film and hybrid integrated circuits
Assignee: AT&T Inc
•
Filing: 1975-05-12
•
Granted: 1977-04-05
•
Expires: 1995-05-12
Abstract
Abstract A metallization scheme for interconnection of elements in thin film and hybrid circuits is described. A thin layer of titanium is first formed, preferably by evaporation or sputtering, on the surface of the insulating substrate. A thin layer of copper is then formed in the same manner over the titanium layer. This is followed by electroplating of copper to a desired thickness onto selected portions of the Ti-Cu multilayer. Successive layers of nickel and gold are then selectively electroplated onto the plated copper regions. An additional layer of palladium may also be included between the titanium and copper layers for improved adhesion. The Ti-Cu-Ni-Au metallization system has been found unusually compatible with the major processing requirements of thin film circuits, for example, thermocompression bonding, soldering, via-hole coverage and resistor stabilization.
Inventors
- 👤 Nathan George Lesh, deceased
- 👤 Executor By Merchants National Bank Of Allentown
- 👤 Joseph Michael Morabito
- 👤 John Henry Thomas, III
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-27 04:51
CPC Classifications
H; H05; H05K; H05K3/00; H05K3/38; H05K3/388; H01; H01B; H01B1/00; H05K3/22; H05K3/24; H05K3/243; H05K3/244; H05K1/00; H05K1/02; H05K1/03; H05K1/0306; H05K2201/00; H05K2201/03; H05K2201/0332; H05K2201/0364; H05K2201/0367; H05K2203/00; H05K2203/07; H05K2203/0703; H05K2203/0723; H05K3/02; H05K3/06; H05K3/061; H05K3/062; H05K3/10; H05K3/108; Y; Y10; Y10T; Y10T428/00; Y10T428/12; Y10T428/12493; Y10T428/12632; Y10T428/12639; Y10T428/12771; Y10T428/12806
Claims Analysis
Total Claims: 22
Claim 1
Independent Claim
149 words
A method of forming electrical interconnections of a desired resistivity between thin film elements on an insulating substrate comprising the steps of: forming on the substrate a first metal layer comprising titanium in a desired pattern to a thickness in the range 1,500-3,000 A; forming over said titanium layer a second metal layer comprising copper to a thickness within the range 3,000-7,000 A; electroplating additional copper onto said second layer to produce a total copper thickness within the range 25,000-40,000 A on selected areas of said second layer; electroplating a third metal layer comprising nickel over said electroplated copper layer to a thickness within the range 8,000-20,000 A; electroplating a fourth metal layer comprising gold on at least portions of said third layer to a thickness within the range 15,000-25,000 A; and removing those portions of said first and second layers which are not covered by said electroplated metals.
Claim 2
Independent Claim
149 words
A method of forming electrical interconnections of a desired resistivity between thin film elements on an insulating substrate comprising the steps of: forming on the substrate a first metal layer comprising titanium in a desired pattern to a thickness in the range 1,500-3,000 A; forming over said titanium layer a second metal layer comprising copper to a thickness within the range 3,000-7,000 A; electroplating additional copper onto said second layer to produce a total copper thickness within the range 25,000-40,000 A on selected areas of said second layer; electroplating a third metal layer comprising nickel over said electroplated copper layer to a thickness within the range 8,000-20,000 A; electroplating a fourth metal layer comprising gold on at least portions of said third layer to a thickness within the range 15,000-25,000 A; and removing those portions of said first and second layers which are not covered by said electroplated metals.
Claim 3
Dependent Claim
22 words
The method according to claim 1 wherein the fourth metal layer is formed on substantially the entire surface of said third layer.
Claim 4
Dependent Claim
30 words
The method according to claim 1 wherein the fourth metal layer is formed only on the portions of said third metal layer which comprise the bonding pads for said circuit.
Claim 5
Dependent Claim
28 words
The method according to claim 1 further comprising the step of, prior to formation of said second layer, forming over said first layer a fifth layer comprising palladium.
Claim 6
Dependent Claim
17 words
The method according to claim 1 wherein said first and second metal layers are formed by evaporation.
Claim 7
Dependent Claim
17 words
The method according to claim 1 wherein said first and second metal layers are formed by sputtering.
Claim 8
Dependent Claim
26 words
The method according to claim 1 wherein the additional layer of Cu is electroplated in a bath comprising CuSO 4 and H 2 SO 4 .
Claim 9
Dependent Claim
39 words
The method according to claim 1 wherein said second layer of Cu is removed by immersing in a solution comprising ammonium persulfate and the first layer of Ti is subsequently removed by immersion in a solution comprising hydrofluoric acid.
Claim 10
Dependent Claim
35 words
The method according to claim 1 further comprising the steps of heating the resulting structure at a temperature of approximately 250° C for a period of time within the range 30 minutes to 10 hours.
Claim 11
Dependent Claim
36 words
The method according to claim 9 further comprising the step of heating the resulting structure at a temperature of approximately 300° C for a period of time within the range of 30 minutes to 4 hours.
Claim 12
Dependent Claim
35 words
The method according to claim 9 further comprising the step of heating the resulting structure at a temperature of approximately 350° C for a period of time within the range 30 minutes to 2 hours.
Claim 13
Independent Claim
284 words
A method of forming a circuit including thin film elements and electrical interconnections having a resistivity no greater than 0.005 ohms/square on the major surface of an insulating substrate comprising the steps of: evaporating onto substantially the entire major surface of said substrate a first metal layer consisting essentially of titanium to a thickness within the range 1,500-3,000 A; evaporating onto substantially the entire surface of said first metal layer a second metal layer consisting essentially of palladium to a thickness within the range 200-1,000 A; evaporating onto substantially the entire surface of said second metal laye a third metal layer consisting essentially of copper to a thickness within the range 3,000-7,000 A; electroplating additional copper onto selected portions of said evaporated layer of copper in the desired interconnection pattern to produce a total Cu thickness within the range 25,000-40,000 A utilizing a plating bath comprising CuSO 4 and H 2 SO 4 ; while said electroplated copper layer is still wet, electroplating a fourth metal layer consisting essentially of nickel on substantially the entire surface of said electroplated copper layer to a thickness within the range 8,000-20,000 A utilizing a plating bath comprising nickel sulfamate; electroplating onto at least portions of said fourth metal layer a fifth metal layer consisting essentially of gold to a thickness within the range 15,000-25,000 A utilizing a plating bath comprising gold cyanide; removing the portions of the evaporated copper layer not covered by at least one of said electroplated layers by immersing in an etching solution comprising ammonium persulfate; and removing the portions of the evaporated titanium layer not covered by at least one of said electroplated layers by immersing in an etching solution comprising hydrofluoric acid.
Claim 14
Independent Claim
284 words
A method of forming a circuit including thin film elements and electrical interconnections having a resistivity no greater than 0.005 ohms/square on the major surface of an insulating substrate comprising the steps of: evaporating onto substantially the entire major surface of said substrate a first metal layer consisting essentially of titanium to a thickness within the range 1,500-3,000 A; evaporating onto substantially the entire surface of said first metal layer a second metal layer consisting essentially of palladium to a thickness within the range 200-1,000 A; evaporating onto substantially the entire surface of said second metal laye a third metal layer consisting essentially of copper to a thickness within the range 3,000-7,000 A; electroplating additional copper onto selected portions of said evaporated layer of copper in the desired interconnection pattern to produce a total Cu thickness within the range 25,000-40,000 A utilizing a plating bath comprising CuSO 4 and H 2 SO 4 ; while said electroplated copper layer is still wet, electroplating a fourth metal layer consisting essentially of nickel on substantially the entire surface of said electroplated copper layer to a thickness within the range 8,000-20,000 A utilizing a plating bath comprising nickel sulfamate; electroplating onto at least portions of said fourth metal layer a fifth metal layer consisting essentially of gold to a thickness within the range 15,000-25,000 A utilizing a plating bath comprising gold cyanide; removing the portions of the evaporated copper layer not covered by at least one of said electroplated layers by immersing in an etching solution comprising ammonium persulfate; and removing the portions of the evaporated titanium layer not covered by at least one of said electroplated layers by immersing in an etching solution comprising hydrofluoric acid.
Claim 15
Dependent Claim
21 words
The method according to claim 12 wherein the fifth layer is formed on substantially the entire surface of said fourth layer.
Claim 16
Dependent Claim
28 words
The method according to claim 12 wherein the fifth layer is formed only on the areas of the fourth layer which comprise the bonding pads for said circuit.
Claim 17
Dependent Claim
29 words
The method according to claim 12 further comprising the steps of heating the resulting structure to a temperature of approximately 250° C for approximately 30 minutes to 10 hours.
Claim 18
Dependent Claim
28 words
The method according to claim 15 further comprising the step of heating the structure to a temperature of approximately 300° C for approximately 30 minutes to 4 hours.
Claim 19
Dependent Claim
28 words
The method according to claim 15 further comprising the step of heating the structure to a temperature of approximately 350° C for approximately 30 minutes to 2 hours.
Claim 20
Independent Claim
124 words
A method of forming electrical interconnections of a desired resistivity between thin film elements on the major surface of an insulating substrate comprising the steps of: forming on the substrate a first metal layer comprising titanium in a desired pattern; forming over said first metal layer a second metal layer comprising palladium; forming over said second metal layer a third metal layer comprising copper; electroplating additional copper onto said third layer on selected areas of said third layer; electroplating a fourth metal layer comprising nickel over said electroplated copper layer; electroplating a fifth metal layer comprising gold on at least portions of said fourth layer; and removing those portions of said first, second and third layers which are not covered by said electroplated metals.
Claim 21
Independent Claim
124 words
A method of forming electrical interconnections of a desired resistivity between thin film elements on the major surface of an insulating substrate comprising the steps of: forming on the substrate a first metal layer comprising titanium in a desired pattern; forming over said first metal layer a second metal layer comprising palladium; forming over said second metal layer a third metal layer comprising copper; electroplating additional copper onto said third layer on selected areas of said third layer; electroplating a fourth metal layer comprising nickel over said electroplated copper layer; electroplating a fifth metal layer comprising gold on at least portions of said fourth layer; and removing those portions of said first, second and third layers which are not covered by said electroplated metals.
Claim 22
Dependent Claim
19 words
The method according to claim 1 wherein the resistivity of the electrical interconnections is not greater than 0.005 ohms/square.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1980-04-04 | 1980-10-04 | 1981-04-05 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1984-04-04 | 1984-10-04 | 1985-04-05 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1988-04-04 | 1988-10-04 | 1989-04-05 | $7700.00 | Window Closed / Lapsed |