Clad metal tubes
Assignee: Huntington Alloys Corp
•
Filing: 1975-07-31
•
Granted: 1977-04-05
•
Expires: 1995-07-31
Abstract
Abstract A method for producing high strength composite tubing having a corrosion-resistant metal lining. The composite tubing is prepared by extrusion of an assembly having a low alloy steel outer shell and metal powder lining. The metal powder is consolidated during extrusion and high strength is attained by heat treatment.
Inventors
- 👤 Robin Mackay Forbes Jones
- 👤 Walter Adrian Petersen
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-02 00:17
CPC Classifications
B; B22; B22F; B22F7/00; B22F7/06; B22F7/08; Y; Y10; Y10T; Y10T428/00; Y10T428/12; Y10T428/12493; Y10T428/12771; Y10T428/12861; Y10T428/12931
Claims Analysis
Total Claims: 20
Claim 1
Independent Claim
151 words
A process for preparing a composite metallic tubular member having an internally-lined metal surface comprising: preparing a metal shell having concentric inner and outer surfaces; attaching to said metal shell a first end closure plate and a metal inner liner so that said metal shell and said metal inner liner are concentrically aligned, thereby forming an annular space; pouring a pre-alloyed, argon atomized metal powder into said annular space between said metal shell and said metal inner liner; attaching to said metal shell and said metal inner liner a second end closure plate thereby enclosing said annular space containing said metal powder and completing an assembly; heating said assembly for a time period sufficient to substantially through-heat said assembly to a temperature substantially corresponding to the extrusion temperature to be employed; and extruding said assembly through an extrusion die to produce said composite metallic tubular member having an internally-lined metal surface.
Claim 2
Dependent Claim
151 words
A process for preparing a composite metallic tubular member having an internally-lined metal surface comprising: preparing a metal shell having concentric inner and outer surfaces; attaching to said metal shell a first end closure plate and a metal inner liner so that said metal shell and said metal inner liner are concentrically aligned, thereby forming an annular space; pouring a pre-alloyed, argon atomized metal powder into said annular space between said metal shell and said metal inner liner; attaching to said metal shell and said metal inner liner a second end closure plate thereby enclosing said annular space containing said metal powder and completing an assembly; heating said assembly for a time period sufficient to substantially through-heat said assembly to a temperature substantially corresponding to the extrusion temperature to be employed; and extruding said assembly through an extrusion die to produce said composite metallic tubular member having an internally-lined metal surface.
Claim 3
Dependent Claim
23 words
A process as defined in claim 1 wherein said first end closure plate or said second end closure plate contains an evacuation means.
Claim 4
Dependent Claim
32 words
A process as defined in claim 2 wherein entrained air is removed from said metal powder contained within said annular space through said evacuation means, and thereafter said evacuation means is sealed.
Claim 5
Dependent Claim
47 words
A process as defined in claim 1 wherein said extrusion assembly is heated in an upright position thereby providing an initial sintering operation of said metal powder to minimize settling of said metal powder during movement entailed in transporting and loading said extrusion assembly into an extruder.
Claim 6
Dependent Claim
15 words
A process as defined in claim 1 wherein said metal shell is a high-strength steel.
Claim 7
Dependent Claim
47 words
A process as defined in claim 5 wherein said high-strength steel contains up to about 0.4% carbon, up to about 0.2% silicon, up to about 2% manganese, up to about 1% molybdenum, up to about 0.1% vanadium, up to about 0.2% aluminum and the balance essentially iron.
Claim 8
Dependent Claim
15 words
A process as defined in claim 1 wherein said metal powder is a nickel-base alloy.
Claim 9
Dependent Claim
59 words
A process as defined in claim 7 wherein said metal powder contains from about 10% to about 30% chromium, up to about 40% cobalt, up to about 20% iron, up to about 20% molybdenum, up to about 10% tungsten, up to about 10% columbium, up to about 5% titanium, up to about 1% aluminum, and the balance essentially nickel.
Claim 10
Dependent Claim
68 words
A process as defined in claim 8 wherein said metal powder contains up to about 0.1% carbon, up to about 0.5% silicon, up to about 0.5% manganese, from about 20% to about 23% chromium, from about 8% to about 10% molybdenum, from about 3% to about 4% columbium, up to about 0.4% aluminum, up to about 0.4% titanium, up to about 5% iron, and the balance essentially nickel.
Claim 11
Dependent Claim
26 words
A process as defined in claim 1 wherein said metal inner liner, said first end closure plate and said second end closure plate are mild steel.
Claim 12
Dependent Claim
31 words
A process as defined in claim 1 wherein said metal shell, said metal inner liner, said first end closure plate and said second end closure plate are joined together by welding.
Claim 13
Dependent Claim
24 words
A process as defined in claim 1 wherein said extrusion assembly is heated to about 1800° F to about 2200° F prior to extrusion.
Claim 14
Dependent Claim
22 words
A process as defined in claim 1 wherein said metal inner liner is removed from said composite metallic tubular member by pickling.
Claim 15
Dependent Claim
51 words
A process as defined in claim 1 wherein said composite metallic tubular member is heated for about 1/2 hour to about 3 hours at about 1500° to about 1800°F, followed by water quenching and then heated for about 1/2 hour to about 10 hours at about 400° to about 1200° F.
Claim 16
Dependent Claim
24 words
A process as defined in claim 1 wherein said metal powder is highly flowable and has a sieve size below 100 and above 325.
Claim 17
Dependent Claim
90 words
A high-strength, corrosion-resistant composite metallic tubular member consisting of: a low alloy steel outer shell containing up to about 0.4% carbon, up to about 0.2% silicon, up to about 2% manganese, up to about 1% molybdenum, up to about 0.1% vanadium, up to about 0.2% aluminum, and the balance essentially iron and a nickel-base alloy inner lining containing from about 10% to about 30% chromium, up to about 20% iron, up to about 20% molybdenum, up to about 10% tungsten, up to about 10% columbium and the balance essentially nickel.
Claim 18
Dependent Claim
90 words
A high-strength, corrosion-resistant composite metallic tubular member consisting of: a low alloy steel outer shell containing up to about 0.4% carbon, up to about 0.2% silicon, up to about 2% manganese, up to about 1% molybdenum, up to about 0.1% vanadium, up to about 0.2% aluminum, and the balance essentially iron and a nickel-base alloy inner lining containing from about 10% to about 30% chromium, up to about 20% iron, up to about 20% molybdenum, up to about 10% tungsten, up to about 10% columbium and the balance essentially nickel.
Claim 19
Dependent Claim
71 words
A tubular member as defined in claim 16 wherein said nickel-base alloy inner lining contains up to about 0.1% carbon, up to about 0.5% silicon, up to about 0.5% manganese, from about 20% to about 23% chromium, from about 8% to about 10% molybdenum, from about 3% to about 4% columbium, up to about 0.4% aluminum, up to about 0.4% titanium, up to about 5% iron, and the balance essentially nickel.
Claim 20
Dependent Claim
60 words
A tubular member as defined in claim 17 wherein a yield strength in excess of about 130,000 psi is attained after heating for about 1/2 hour to about 3 hours at temperatures from about 1500° F, followed by water quenching and then reheating for about 1/2 hour to about 10 hours at temperatures from about 400° to about 1200° F.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1980-04-04 | 1980-10-04 | 1981-04-05 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1984-04-04 | 1984-10-04 | 1985-04-05 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1988-04-04 | 1988-10-04 | 1989-04-05 | $7700.00 | Window Closed / Lapsed |