Sandwich panel construction
Assignee: Babcock and Wilcox Co
•
Filing: 1975-08-22
•
Granted: 1977-03-22
•
Expires: 1995-08-22
Abstract
Abstract A typical embodiment of the resinous foam sandwich construction that characterizes the invention has face sheets of fiber reinforced thermoplastic resin laminates. The foam core is a mixture of hollow glass spheres and resin, in which the resin in the core is the same as the resin used to form the face sheets.
Inventors
- 👤 William Gordon Long
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-26 06:52
CPC Classifications
B; B32; B32B; B32B27/00; B32B27/06; B32B27/065; B29; B29C; B29C70/00; B29C70/02; B29C70/021; B29C70/025; B29C70/58; B29C70/66; B32B27/08; B32B27/28; B32B27/286; B32B37/00; B32B37/02; B32B37/14; B32B37/144; B32B5/00; B32B5/18; B32B5/20; B32B5/22; B32B5/24; B32B5/245; B32B7/00; B32B7/04; E; E04; E04C; E04C2/00; E04C2/02; E04C2/10; E04C2/20; E04C2/205; E04C2/24; E04C2/243; B29K; B29K2105/00; B29K2105/06; B29K2105/08; B29K2105/0809; B29K2105/0845; B29K2105/16; B29K2105/165; B29L; B29L2007/00; B29L2007/002; B32B2250/00; B32B2250/40; B32B2262/00; B32B2262/10; B32B2262/106; B32B2264/00; B32B2264/10; B32B2264/101; B32B2266/00; B32B2266/02; B32B2266/0214; B32B2307/00; B32B2307/50; B32B2307/546; B32B2307/558; B32B2307/70; B32B2307/732; B32B2605/00; B32B2605/003; B32B2605/18; B32B2607/00; B64; B64C; B64C1/00; B64C1/18; Y; Y10; Y10S; Y10S264/00; Y10S264/06; Y10S273/00; Y10S273/23; Y10S428/00; Y10S428/902; Y10T; Y10T428/00; Y10T428/249921; Y10T428/249953; Y10T428/249971; Y10T428/249974; Y10T428/249987; Y10T428/249991; Y10T428/249992; Y10T428/25; Y10T428/252
Claims Analysis
Total Claims: 8
Claim 1
Independent Claim
92 words
A sandwich panel consisting essentially of a foam core of thermoplastic resin, non-fibrous shapes mixed with said thermoplastic resin and formed from material remaining in the solid state at a higher temperature than the plasticizing temperature of said thermoplastic resin wherein said non-fibrous shapes are not more than 35% by weight of said foam core, and face sheets formed from thermoplastic resin reinforced with graphite fibers for, said face sheets being bonded to said foam core, said thermoplastic resin in said face sheets being the same type as said foam core resin.
Claim 2
Dependent Claim
92 words
A sandwich panel consisting essentially of a foam core of thermoplastic resin, non-fibrous shapes mixed with said thermoplastic resin and formed from material remaining in the solid state at a higher temperature than the plasticizing temperature of said thermoplastic resin wherein said non-fibrous shapes are not more than 35% by weight of said foam core, and face sheets formed from thermoplastic resin reinforced with graphite fibers for, said face sheets being bonded to said foam core, said thermoplastic resin in said face sheets being the same type as said foam core resin.
Claim 3
Dependent Claim
14 words
A sandwich panel according to claim 1 wherein said shapes are hollow glass spheres.
Claim 4
Dependent Claim
92 words
A sandwich panel consisting essentially of a foam polysulfone core, hollow glass spheres ranging in size from 10 to 140 microns mixed with said polysulfone core resin in an amount of 35 percent by weight or less of said spheres to 65% by weight or more of said core resin, said core having a thickness from approximately 1/8 inch to 3/8 inch, and face sheets bonded to said core, said face sheets being formed from polysulfone thermoplastic resin and graphite fibers, said face sheet thickness ranging from 0.040 inch to 0.120 inch.
Claim 5
Dependent Claim
92 words
A sandwich panel consisting essentially of a foam polysulfone core, hollow glass spheres ranging in size from 10 to 140 microns mixed with said polysulfone core resin in an amount of 35 percent by weight or less of said spheres to 65% by weight or more of said core resin, said core having a thickness from approximately 1/8 inch to 3/8 inch, and face sheets bonded to said core, said face sheets being formed from polysulfone thermoplastic resin and graphite fibers, said face sheet thickness ranging from 0.040 inch to 0.120 inch.
Claim 6
Independent Claim
138 words
A method for manufacturing a sandwich panel consisting essentially of the steps of mixing a thermoplastic resin with a solvent to dissolve said thermoplastic resin, mixing hollow glass spheres with said dissolved thermoplastic resin, casting said mixture of glass spheres and dissolved thermoplastic resin into a desired shape, drying said cast mixture to drive off said solvent to form a foam core for the sandwich panel wherein said spheres are not more than 35% by weight of said foam core preparing a mixture of said thermoplastic resin with graphite fibers, compression molding said resin and fibers to produce a void-free face sheet, placing said face sheet on said foam core, and remolding under conditions of heat and pressure said face sheet to cause said thermoplastic resin to flow and to bond said face sheet to said foam core.
Claim 7
Independent Claim
138 words
A method for manufacturing a sandwich panel consisting essentially of the steps of mixing a thermoplastic resin with a solvent to dissolve said thermoplastic resin, mixing hollow glass spheres with said dissolved thermoplastic resin, casting said mixture of glass spheres and dissolved thermoplastic resin into a desired shape, drying said cast mixture to drive off said solvent to form a foam core for the sandwich panel wherein said spheres are not more than 35% by weight of said foam core preparing a mixture of said thermoplastic resin with graphite fibers, compression molding said resin and fibers to produce a void-free face sheet, placing said face sheet on said foam core, and remolding under conditions of heat and pressure said face sheet to cause said thermoplastic resin to flow and to bond said face sheet to said foam core.
Claim 8
Dependent Claim
27 words
A method according to claim 4 further comprising the step of interposing an additional layer of said thermoplastic resin between said face sheet and said foam core.
References Cited (Backward Citations)
US3316139A
Cited
US3515625A
Cited
US3524794A
Cited
US3551197A
Cited
US3769126A
Cited
US3649435A
Cited
US3769150A
Cited
US3707434A
Cited
US3778334A
Cited
US3788937A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1980-03-21 | 1980-09-20 | 1981-03-22 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1984-03-21 | 1984-09-20 | 1985-03-22 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1988-03-21 | 1988-09-20 | 1989-03-22 | $7700.00 | Window Closed / Lapsed |