Abstract
Abstract Coated substrates of much superior wear and stain resistance are formed by successively superimposing epoxy resin and at least 3 coatings of polyurethane each formed from diisocyanate and branched chain polyols that are crosslinked by a polyhydroxy material, the outer coating being of different composition from inner coatings, and comprising a polycaprolactone chain extender. This invention relates to highly wear resistant and decorative seamless flooring which may be formed over various surfaces such as concrete, wood, vinyl asbestos tile, and the like, from a plurality of coats of liquid compositions. It particularly relates to the wear resistant glaze layers of a seamless flooring, and to a polyurethane base composition used for forming such layers.
Inventors
- 👤 Robert M. Evans
- 👤 Joseph S. Fogel
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-24 15:40
CPC Classifications
C; C04; C04B; C04B41/00; C04B41/009; B; B05; B05D; B05D5/00; B05D5/06; B05D5/061; C04B41/45; C04B41/52; C04B41/60; C04B41/61; C04B41/70; C08; C08G; C08G18/00; C08G18/06; C08G18/08; C08G18/10; C08G18/28; C08G18/40; C08G18/48; C08G18/4829; B05D7/00; B05D7/50; B05D7/56; B05D7/58; B05D7/586; C04B2111/00; C04B2111/60; Y; Y10; Y10S; Y10S524/00; Y10S524/914; Y10T; Y10T428/00; Y10T428/31504; Y10T428/31511; Y10T428/31551
Claims Analysis
Total Claims: 16
Claim 1
Independent Claim
104 words
A polyurethane base coating composition capable of forming films of high abrasion and stain resistance comprising: (1) a solution in volatile organic solvent of an --NCO terminated prepolymer of a diisocyanate having unequal reactivity of the two isocyanate groups and a polyoxypropylene triol which has an equivalent weight of 180 to 400; said prepolymer having a free --NCO content of 5 to 10%, and (2) a polycaprolactone triol in amounts to react with most of said --NCO of said prepolymer, the ratio of the equivalents of free --NCO in said prepolymer to equivalents of --OH in the polycaprolactone cross-linking agent being greater than 1.75.
Claim 2
Dependent Claim
104 words
A polyurethane base coating composition capable of forming films of high abrasion and stain resistance comprising: (1) a solution in volatile organic solvent of an --NCO terminated prepolymer of a diisocyanate having unequal reactivity of the two isocyanate groups and a polyoxypropylene triol which has an equivalent weight of 180 to 400; said prepolymer having a free --NCO content of 5 to 10%, and (2) a polycaprolactone triol in amounts to react with most of said --NCO of said prepolymer, the ratio of the equivalents of free --NCO in said prepolymer to equivalents of --OH in the polycaprolactone cross-linking agent being greater than 1.75.
Claim 3
Dependent Claim
18 words
The composition of claim 1 wherein the polymer solids content of said coating composition is at least 55%.
Claim 4
Dependent Claim
18 words
The composition of claim 2 wherein the volatile solvent is a mixture of aliphatic and aromatic hydrocarbon solvents.
Claim 5
Dependent Claim
11 words
The composition of claim 3 which also contains cellulose-acetate-butyrate dissolved therein.
Claim 6
Dependent Claim
15 words
The composition of claim 4 which contains an organic tin catalyst and a viscosity stabilizer.
Claim 7
Dependent Claim
39 words
The product of claim 1 wherein the prepolymer is prereacted with between 5 and 20% of the polycaprolacetone triol and the remaining portion required to reach an --NCO OH ratio greater than 1.75 is mixed in on the job.
Claim 8
Dependent Claim
21 words
The product of claim 1 which is partially prereacted with water and then reacted on the job with a polycaprolactone triol.
Claim 9
Dependent Claim
24 words
The composition of claim 1 wherein the --NCO terminated prepolymer of a diisocyanate having unequal reactivity of the two isocyanate groups is isophorone diisocyanate.
Claim 10
Dependent Claim
25 words
The composition of claim 1 wherein the --NCO terminated prepolymer of a diisocyanate having unequal reactivity of the two isocyanate groups is hydrogenated 2,4-tolylene diisocyanate.
Claim 11
Dependent Claim
102 words
A polyurethane base coating composition capable of forming films of high abrasion and stain resistance comprising: (1) a solution in volatile organic solvent of an --NCO terminated prepolymer of a diisocyanate having unequal reactivity of the two isocyanate groups and a polycaprolactone triol of equivalent weight between 100 and 250, said prepolymer having a free --NCO content of 5 to 10% and (2) a polycaprolactone triol in amount to react with most of said --NCO of said prepolymer, the ratio of the equivalents of free --NCO in said prepolymer to equivalents of --OH in the polycaprolactone crosslinking agent being greater than 1.75.
Claim 12
Dependent Claim
102 words
A polyurethane base coating composition capable of forming films of high abrasion and stain resistance comprising: (1) a solution in volatile organic solvent of an --NCO terminated prepolymer of a diisocyanate having unequal reactivity of the two isocyanate groups and a polycaprolactone triol of equivalent weight between 100 and 250, said prepolymer having a free --NCO content of 5 to 10% and (2) a polycaprolactone triol in amount to react with most of said --NCO of said prepolymer, the ratio of the equivalents of free --NCO in said prepolymer to equivalents of --OH in the polycaprolactone crosslinking agent being greater than 1.75.
Claim 13
Dependent Claim
115 words
A polyurethane base coating composition capable of forming films of high abrasion and stain resistance comprising: (1) a solution in volatile organic solvent of an --NCO terminated prepolymer of a diisocyanate having unequal reactivity of the two isocyanate groups and a polyoxypropylene triol which has an equivalent weight of 180 to 400; said prepolymer having a free --NCO content of 5 to 10%, and (2) an adipic acid-polyethylene glycol copolymer polyester with excess hydroxyl groups in amounts to react with most of said --NCO of said prepolymer, the ratio of the equivalents of free -NCO in said prepolymer to equivalents of -OH in said adipic acid-polyethylene glycol copolymer polyester crosslinking agent being greater than 1.75.
Claim 14
Dependent Claim
115 words
A polyurethane base coating composition capable of forming films of high abrasion and stain resistance comprising: (1) a solution in volatile organic solvent of an --NCO terminated prepolymer of a diisocyanate having unequal reactivity of the two isocyanate groups and a polyoxypropylene triol which has an equivalent weight of 180 to 400; said prepolymer having a free --NCO content of 5 to 10%, and (2) an adipic acid-polyethylene glycol copolymer polyester with excess hydroxyl groups in amounts to react with most of said --NCO of said prepolymer, the ratio of the equivalents of free -NCO in said prepolymer to equivalents of -OH in said adipic acid-polyethylene glycol copolymer polyester crosslinking agent being greater than 1.75.
Claim 15
Dependent Claim
12 words
The composition of claim 10 wherein the isocyanate prepolymer is isophorone diisocyanate.
Claim 16
Dependent Claim
12 words
The composition of claim 11 wherein the isocyanate prepolymer is isophorone diisocyanate.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1980-03-21 | 1980-09-20 | 1981-03-22 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1984-03-21 | 1984-09-20 | 1985-03-22 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1988-03-21 | 1988-09-20 | 1989-03-22 | $7700.00 | Window Closed / Lapsed |