Process for preparing materials having improved mechanical and thermal properties and materials obtained thereby
Assignee: SnamProgetti SpA
•
Filing: 1974-10-31
•
Granted: 1977-03-22
•
Expires: 1994-10-31
Abstract
Abstract The mechanical and thermal properties of aluminum oxide, such as γ alumina, adapted for use as a catalyst or catalyst carrier are improved through a treatment thereof with a silicon compound such as an alkyl orthosilicate in which the aluminum oxide is impregnated with the silicon compound or a solution thereof in a compatible organic solvent whose boiling point is lower than the boiling point of the silicon compound. The impregnated aluminum oxide is dried at a temperature in the range from above the boiling point of the silicon compound to 500° C and is then subjected to controlled oxidation.
Inventors
- 👤 Franco Buonomo
- 👤 Vittorio Fattore
- 👤 Bruno Notari
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-31 12:20
CPC Classifications
B; B01; B01J; B01J37/00; B01J37/12; B01J37/14; B01J21/00; B01J21/06; B01J21/12; C; C01; C01F; C01F7/00; C01F7/02; B01J37/02; B01J37/03; B01J37/031; B01J37/033; C01P; C01P2002/00; C01P2002/80; C01P2002/82; C01P2006/00; C01P2006/12; C01P2006/13; Y; Y10; Y10S; Y10S502/00; Y10S502/50
Claims Analysis
Total Claims: 11
Claim 1
Independent Claim
161 words
The process of improving the mechanical and thermal properties of aluminum oxide adapted for use as a catalyst or catalyst carrier which comprises impregnating said aluminum oxide with a silicon compound having the general formula: ##STR2## in which X, Y, Z and W are selected from the group consisting of (--R), (--Cl), (--Br), (--SiH), (--COOR), (--SiH Cl), -- [OSi(OR)] p , OSi, (OR) 3 , in which R is an alkyl, cycloalkyl, aromatic alkylaromatic or alkyl-cycloalkyl radical having from 1 to 30 carbon atoms; n, m and p are whole numbers from 1 to 3, by bringing said silicon compound or a solution thereof in a compatible organic solvent whose boiling point is lower than the boiling point of the silicon compound into contact with said aluminum oxide, drying said impregnated aluminum oxide at a temperature in the range of from the boiling point of the silicon compound to 500° C, and then subjecting said impregnated aluminum oxide to controlled oxidation.
Claim 2
Dependent Claim
161 words
The process of improving the mechanical and thermal properties of aluminum oxide adapted for use as a catalyst or catalyst carrier which comprises impregnating said aluminum oxide with a silicon compound having the general formula: ##STR2## in which X, Y, Z and W are selected from the group consisting of (--R), (--Cl), (--Br), (--SiH), (--COOR), (--SiH Cl), -- [OSi(OR)] p , OSi, (OR) 3 , in which R is an alkyl, cycloalkyl, aromatic alkylaromatic or alkyl-cycloalkyl radical having from 1 to 30 carbon atoms; n, m and p are whole numbers from 1 to 3, by bringing said silicon compound or a solution thereof in a compatible organic solvent whose boiling point is lower than the boiling point of the silicon compound into contact with said aluminum oxide, drying said impregnated aluminum oxide at a temperature in the range of from the boiling point of the silicon compound to 500° C, and then subjecting said impregnated aluminum oxide to controlled oxidation.
Claim 3
Dependent Claim
13 words
Process according to claim 1, wherein said silicon compound is an alkyl orthosilicate.
Claim 4
Dependent Claim
33 words
Process according to claim 1, wherein said impregnation with the silicon compound is carried out in the liquid phase at atmospheric pressure and in the temperature range of from 50° to 500° C.
Claim 5
Dependent Claim
41 words
Process according to claim 1, wherein said impregnation with the silicon compound is carried out in the vapour phase at atmospheric pressure by flowing the silicon compound in an inert gas stream onto the aluminum oxide which is to be treated.
Claim 6
Dependent Claim
43 words
Process according to claim 1, wherein said aluminum oxide which is to be treated and the silicon compound are contacted in the pressure range of from room pressure to 50 kg/cm 2 and at temperatures ranging between the room temperature and 500° C.
Claim 7
Dependent Claim
18 words
Process according to claim 1, wherein the oxidation is carried out under an air stream at 500° C.
Claim 8
Dependent Claim
12 words
Process according to claim 1, wherein the aluminum oxide material is γ-alumina.
Claim 9
Dependent Claim
83 words
Stabilized alumina having a silicon content, expressed as silicon atoms per A 2 of area, of from 0.01 to 0.06 which shows, after a treatment at 1200° C over a period of 24 hours, no transformation other than from phase to phase, and which, after a treatment for 40 hours at 250° C under a steam pressure of 15 ata, keeps unchanged its starting crystalline structure and, after a treatment at 1000° C for 24 hours, shows a volume shrinkage lower than 2%.
Claim 10
Dependent Claim
83 words
Stabilized alumina having a silicon content, expressed as silicon atoms per A 2 of area, of from 0.01 to 0.06 which shows, after a treatment at 1200° C over a period of 24 hours, no transformation other than from phase to phase, and which, after a treatment for 40 hours at 250° C under a steam pressure of 15 ata, keeps unchanged its starting crystalline structure and, after a treatment at 1000° C for 24 hours, shows a volume shrinkage lower than 2%.
Claim 11
Dependent Claim
50 words
Stabilized alumina according to claim 8, which shows an infrared adsorption spectrum having a very strong band at 3745 cm - 1 characteristic of the group Si--OH and very weak bands or no band at 3795 cm - 1 and 3737 - 1 awardable to hydroxyls at the alumina surface.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1980-03-21 | 1980-09-20 | 1981-03-22 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1984-03-21 | 1984-09-20 | 1985-03-22 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1988-03-21 | 1988-09-20 | 1989-03-22 | $7700.00 | Window Closed / Lapsed |