Method for treating flue dust containing lead

Assignee: PAUL BERGSOE AND SON AS
•
Filing: 1975-06-04
•
Granted: 1977-03-22
•
Expires: 1995-06-04
📄 Original PDF 🌐 Google Patents 🔄 Sync Now

Abstract

Abstract A method for pretreating of flue dust having a content of lead therein, by which method the flue dust is fused at a relatively low temperature without any substantial reduction taking place, whereupon the slag thus formed is cooled until solidification, reagents for the improvement of the process and/or the material being added at one or more of the process steps before, during or after fusion of the flue dust, said reagents comprising slag-forming chemicals, a material for raising the melting temperatures, and a ferrous reduction agent. Item an apparatus for the pretreatment of flue dust in accordance with the above method and comprising a fusing furnace with a hearth and heating means and having an outlet leading to a vessel for collecting the molten material, conveying means for feeding the flue dust to the fusing furnace from a dust collecting device, and dispensing means for dispensing additive reagents to either the flue dust, the fusing furnace or the molten material flowing therefrom through the outlet or simultaneously to more of said positions and at a rate proportional to the flue dust feed rate. The vessel for collecting the molten material may comprise heating means and means for stirring the slag.

Inventors

  • 👤 Svend Bergsoe

Bibliographic Details

Application Number —
Jurisdiction US
Data Source google_patents
Last Synchronized 2026-11-06 00:57
CPC Classifications
C; C22; C22B; C22B7/00; C22B7/02; Y; Y02; Y02P; Y02P10/00; Y02P10/20; Y10; Y10S; Y10S75/00; Y10S75/961

Claims Analysis

Total Claims: 11
Claim 1
Independent Claim 96 words
A method of recovering metal from flue dust having lead oxide therein, comprising the steps of: heating and fusing the flue dust to a molten and substantially fluid mass in a fusing furnace without substantial simultaneous reduction; adding a pre-treating material prior to cooling said substantially fluid mass for facilitating the recovery of metal from said flue dust; cooling the mass until said mass solidifies; forming and preparing said solidified mass for charging into a metallurgical furnace; charging said prepared mass into said metallurgical furnace; and smelting and reducing said prepared mass in said metallurgical furnace.
Claim 2
Independent Claim 96 words
A method of recovering metal from flue dust having lead oxide therein, comprising the steps of: heating and fusing the flue dust to a molten and substantially fluid mass in a fusing furnace without substantial simultaneous reduction; adding a pre-treating material prior to cooling said substantially fluid mass for facilitating the recovery of metal from said flue dust; cooling the mass until said mass solidifies; forming and preparing said solidified mass for charging into a metallurgical furnace; charging said prepared mass into said metallurgical furnace; and smelting and reducing said prepared mass in said metallurgical furnace.
Claim 3
Dependent Claim 36 words
A method in accordance with claim 1 wherein said pre-treating material includes a slag-forming material for facilitating melting of said flue dust and said pre-treating material is added prior to heating and fusing said flue dust.
Claim 4
Dependent Claim 13 words
A method in accordance with claim 2 wherein said pre-treating material includes borax.
Claim 5
Dependent Claim 14 words
A method in accordance with claim 2 wherein said pre-treating material includes sodium carbonate.
Claim 6
Dependent Claim 34 words
A method in accordance with claim 2 further including the steps of mixing the slag-forming material with said flue dust and simultaneously conveying the flue dust and slag forming material to said fusing furnace.
Claim 7
Dependent Claim 23 words
A method in accordance with claim 1 wherein said pre-treating material is a melting-retardant material for increasing the melting temperature of said mass.
Claim 8
Dependent Claim 13 words
A method in accordance with claim 6 wherein said melting-retardant material is lime.
Claim 9
Dependent Claim 32 words
A method in accordance with claim 6 wherein said melting-retardant material is a ferrous reduction agent which further assists in said smelting and said ferrous reduction agent is added after each fusing.
Claim 10
Dependent Claim 29 words
A method in accordance with claim 8 wherein said ferrous reduction agent is selected from the group consisting substantially of pyrite cinder, iron oxide, iron scale and iron filings.
Claim 11
Dependent Claim 53 words
A method in accordance with claim 1 further including the steps of: collecting said flue dust in a separation device; conveying said flue dust to said fusing furnace; collecting the molten slag in a collecting means; heating the molten mass in said collecting means; and stirring said molten mass in said collecting means.

References Cited (Backward Citations)

GB191227762A Cited
US2139065A Cited

USPTO Annuity & Maintenance Windows

Annuity Stage Window Opens Payment Deadline Surcharge Period Until Estimated Fee Status
3.5 Years (Year 4) 1980-03-21 1980-09-20 1981-03-22 $2000.00 Window Closed / Lapsed
7.5 Years (Year 8) 1984-03-21 1984-09-20 1985-03-22 $3760.00 Window Closed / Lapsed
11.5 Years (Year 12) 1988-03-21 1988-09-20 1989-03-22 $7700.00 Window Closed / Lapsed

Assigned Categories & Tags

No categories assigned to this patent yet.

Assign Category Tag