US4012131A
Expired / Lapsed
US
⏱️ 0.0 years remaining
High strength ophthalmic lens
Assignee: American Optical Corp
•
Filing: 1975-08-20
•
Granted: 1977-03-15
•
Expires: 1995-08-20
Abstract
Abstract An ophthalmic glass lens can be prepared by exposing an alkali metal silicate glass to an ion exchange process in which the glass is chemically strengthened by an exchange of potassium ions for sodium ions in the surface layer of the lens at a temperature either above or below the strain point of the glass. The glasses prepared are essentially free of alumina, have adequate strength and substantially increased depth of pentration of the neutral zone even when up to about 6 percent lime is utilized in the preparation of the glass. The effect of lime as a diffusion-retarding agent during the ion exchange process can be overcome (1) by use of an appropriate amount of zinc or magnesium oxide or mixtures thereof so as to maintain an adequate rate of diffusion during ion exchange or (2) by preparation of the glass essentially free of alumina.
Inventors
- 👤 David A. Krohn
- 👤 Emil W. Deeg
- 👤 Robert E. Graf
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-04 00:52
CPC Classifications
C; C03; C03C; C03C21/00; C03C21/001; C03C21/002; C03C3/00; C03C3/04; C03C3/076; C03C3/078; C03C3/083; C03C3/085; C03C3/089; C03C3/091; Y; Y10; Y10S; Y10S501/00; Y10S501/90; Y10S501/903
Claims Analysis
Total Claims: 8
Claim 1
Independent Claim
169 words
A chemically-strengthened ophthalmic glass lens having a compressively-stressed ion-exchanged surface zone that is at least 60 microns in depth, said lens being formed from a silicate glass comprising by weight about 3 to about 11 percent sodium oxide, about 7 to about 15 percent potassium oxide, up to about 5 percent of other alkali metal oxides, about 12 to about 20 percent of a total of sodium and potassium oxides and other alkali metal oxides, a minimum of 3 to about 6 percent of calcium oxide, the calcium oxide being balanced by an amount of about 3 to about 11 percent of a metal oxide selected from the group consisting of zinc oxide, magnesium oxide, and mixtures thereof, the oxides selected from said group being present in an amount sufficient to assure that the rate of diffusion and depth of penetration obtained during ion exchange of said lens is not detrimentally affected by the presence of the calcium oxide during ion exchange, and the balance of lens being silica.
Claim 2
Dependent Claim
169 words
A chemically-strengthened ophthalmic glass lens having a compressively-stressed ion-exchanged surface zone that is at least 60 microns in depth, said lens being formed from a silicate glass comprising by weight about 3 to about 11 percent sodium oxide, about 7 to about 15 percent potassium oxide, up to about 5 percent of other alkali metal oxides, about 12 to about 20 percent of a total of sodium and potassium oxides and other alkali metal oxides, a minimum of 3 to about 6 percent of calcium oxide, the calcium oxide being balanced by an amount of about 3 to about 11 percent of a metal oxide selected from the group consisting of zinc oxide, magnesium oxide, and mixtures thereof, the oxides selected from said group being present in an amount sufficient to assure that the rate of diffusion and depth of penetration obtained during ion exchange of said lens is not detrimentally affected by the presence of the calcium oxide during ion exchange, and the balance of lens being silica.
Claim 3
Dependent Claim
23 words
A chemically strengthened ophthalmic glass lens according to claim 1 further including about 0.2 to about 0.5 percent of aluminum or zirconium oxide.
Claim 4
Dependent Claim
48 words
A chemically-strengthened ophthalmic glass lens according to claim 2 wherein said glass consists by weight of 11 percent potassium oxide, 8 percent zinc oxide, 7 percent sodium oxide, 3.5 percent calcium oxide, 0.2 percent aluminum oxide, 0.25 percent arsenic oxide, 0.25 percent antimony oxide and the balance silica.
Claim 5
Dependent Claim
45 words
A chemically-strengthened ophthalmic glass lens according to claim 2 consisting by weight of 11 percent potassium oxide, 7 percent sodium oxide, 7 percent zinc oxide, 4.5 percent calcium oxide, 0.2 percent aluminum oxide, 0.25 percent arsenic oxide, 0.25 percent antimony oxide and the balance silica.
Claim 6
Dependent Claim
45 words
A chemically-strengthened ophthalmic glass lens according to claim 2 consisting by weight of 11 percent potassium oxide, 7 percent sodium oxide, 8 percent zinc oxide, 3.5 percent calcium oxide, 0.5 percent aluminum oxide, 0.25 percent arsenic oxide, 0.25 percent antimony oxide and the balance silica.
Claim 7
Dependent Claim
23 words
A chemically strengthened ophthalmic glass lens according to claim 1 further comprising about 1 to about 5 percent of aluminum or zirconium oxide.
Claim 8
Dependent Claim
58 words
A chemically strengthened ophthalmic glass lens according to claim 1 consisting by weight of 10.8 percent potassium oxide, 7 percent sodium oxide, 7.7 percent zinc oxide, 3.3 percent magnesium oxide, 3.1 percent calcium oxide, 2.5 percent aluminum oxide, 1.1 percent boron oxide, 0.8 percent titanium oxide, 0.25 percent arsenic oxide, 0.25 percent antimony oxide and the balance silica.
References Cited (Backward Citations)
US3287200A
Cited
US3357876A
Cited
US3477834A
Cited
US3743491A
Cited
US3697242A
Cited
US3741739A
Cited
US3790260A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1980-03-14 | 1980-09-13 | 1981-03-15 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1984-03-14 | 1984-09-13 | 1985-03-15 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1988-03-14 | 1988-09-13 | 1989-03-15 | $7700.00 | Window Closed / Lapsed |