Laminate of biaxially oriented polystyrene film and polystyrene foam
Assignee: Mobil Oil AS
•
Filing: 1975-09-23
•
Granted: 1977-03-08
•
Expires: 1995-09-23
Abstract
Abstract A method for the production of laminates comprising oriented thermoplastic film heat bonded to a thermoplastic foam which comprises extrusion of a thermoplastic foam containing a blowing agent which has a plasticizing action upon the foam material and while the extruded foam still contains residual blowing agent, heat welding an oriented thermoplastic film to the foam. Disorientation of the oriented film in accord with the present method is eliminated by virtue of the lower heat bonding temperatures necessary to achieve an effective weld by virtue of the presence of the blowing agent-plasticizer material remaining in the foam.
Inventors
- 👤 Donald A. Haase
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-04 05:18
CPC Classifications
B; B32; B32B; B32B27/00; B32B27/06; B32B27/065; B29; B29C; B29C67/00; B29C67/20; B29C44/00; B29C44/34; B29C44/36; B29C44/46; B29C44/50; B29C44/507; B32B27/30; B32B27/302; B32B37/00; B32B37/04; B32B5/00; B32B5/18; B32B38/00; B32B38/0012; B32B2038/0028; B32B2266/00; B32B2266/02; B32B2266/0214; B32B2266/0221; B32B2266/0228; B32B2305/00; B32B2305/02; B32B2305/022; B32B2307/00; B32B2307/30; B32B2307/31; B32B2307/50; B32B2307/514; B32B2307/518; Y; Y10; Y10S; Y10S428/00; Y10S428/91; Y10T; Y10T428/00; Y10T428/24; Y10T428/24942; Y10T428/2495; Y10T428/24967; Y10T428/249921; Y10T428/249953; Y10T428/249987; Y10T428/249988; Y10T428/249991; Y10T428/249992; Y10T428/249993; Y10T428/31504; Y10T428/31855; Y10T428/31909
Claims Analysis
Total Claims: 9
Claim 1
Independent Claim
49 words
A laminate of a flat extruded sheet of pentane blown polystyrene foam directly heat sealed to a preformed film of biaxially oriented film of polystyrene in which laminate the preformed film of polystyrene has not undergone disorientation as a result of being directly heat sealed to the foam sheet.
Claim 2
Dependent Claim
49 words
A laminate of a flat extruded sheet of pentane blown polystyrene foam directly heat sealed to a preformed film of biaxially oriented film of polystyrene in which laminate the preformed film of polystyrene has not undergone disorientation as a result of being directly heat sealed to the foam sheet.
Claim 3
Dependent Claim
54 words
A laminate, as defined in claim 1, wherein the foam sheet is a pentane blown tubular extruded polystyrene foam that contained, during its having been directly heat sealed to said film, sufficient pentane to lower the heat softening point of said foam to a temperature below the disorientation temperature of said biaxially oriented film.
Claim 4
Dependent Claim
46 words
A laminate structure, as defined in claim 1, in which each side of said polystyrene foam sheet is directly heat sealed to a film of biaxially oriented polystyrene film having the orientation characteristics of said film prior to its being heat sealed to said foam sheet.
Claim 5
Dependent Claim
18 words
A laminate, as defined in claim 2, wherein the polystyrene film is a biaxially oriented crystalline polystyrene film.
Claim 6
Dependent Claim
61 words
A laminate, as defined in claim 1, wherein the foam sheet is a polystyrene foam tubular extruded at a blow-up ratio of 6:1, having a density of about 4.5 pounds per cubic foot, and containing residual pentane in an amount that lowers the heat softening point of said foam to a temperature below the disorientation temperature of said biaxially oriented film.
Claim 7
Dependent Claim
45 words
A laminate, as defined in claim 5, wherein the biaxially oriented polystyrene film is an extruded film having an elongation of about 5% in both the machine and transverse directions, a machine direction modulus of 423,000 psi. and a transverse direction modulus of 422,000 psi.
Claim 8
Dependent Claim
16 words
A triple laminate, as defined in claim 3, having an overall thickness of about 40 mils.
Claim 9
Dependent Claim
31 words
A laminate, as defined in claim 1, consisting of a layer of the foam sheet heat sealed to the film of polystyrene and having an overall thickness of about 48 mils.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1980-03-07 | 1980-09-06 | 1981-03-08 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1984-03-07 | 1984-09-06 | 1985-03-08 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1988-03-07 | 1988-09-06 | 1989-03-08 | $7700.00 | Window Closed / Lapsed |