Polymerizable compositions containing unsaturated polyester resins and aqueous alkali metal silicate, method of preparing shaped articles from such compositions and thermoset products thereof
Assignee: Hospitality Homes
•
Filing: 1975-01-29
•
Granted: 1977-03-08
•
Expires: 1995-01-29
Abstract
Abstract Polymerizable unsaturated polyester resin syrups can be extended with aqueous alkali metal silicate in compositions containing from 0.1 to 10.0 parts by weight of aqueous alkali metal silicate for each part by weight of the unsaturated polyester resin syrup. The preferred alkali metal silicate is aqueous sodium silicate. Compositions further can be extended (a) by the addition of reactive fillers such as metal oxides or hydrated metallic salts; (b) by the addition of inert fillers such as clay, silica, glass fibers, perlite; or (c) by the addition of both (a) and (b). The fillers also may include fibrous reinforcing materials such as dispersed glass fibers, randomly oriented fiber mats, wound filaments and woven fabrics. The fillers may be present in amounts from about 0.1 to about 5 times the combined weight of aqueous alkali metal silicate and unsaturated polyester resin syrup. The compositions can be employed in coatings, laminates, cast articles, molded articles, or other shaped articles. The polymerized products are resistant to combustion, have a low fuel content, a low flame spread and are useful thermal insulating materials. The products furthermore have a low smoke content. When exposed to fire, the organic content of these materials is burned and the residual inorganic content is converted to a refractory ceramic material which resists further thermal deterioration and functions as a thermal insulator to resist thermal transfer.
Inventors
- 👤 James M. Self
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-30 03:58
CPC Classifications
C; C08; C08K; C08K3/00; C08K3/34; Y; Y10; Y10S; Y10S106/00; Y10S106/02
Claims Analysis
Total Claims: 32
Claim 1
Independent Claim
83 words
A polymerizable composition consisting essentially of the alkaline reaction product of (a) one part by weight of unsaturated polyester resin syrup; and (b) 0.3 to 10 parts by weight of aqueous sodium silicate; said composition including a polymerization initiator for unsaturated polyester resin syrup, wherein the said aqueous sodium silicate contains 45 to 85 parts by weight water and 55 to 15 parts by weight of sodium silicate solids having a weight ratio of SiO 2 Na 2 O of 1.5 to 3.75.
Claim 2
Dependent Claim
83 words
A polymerizable composition consisting essentially of the alkaline reaction product of (a) one part by weight of unsaturated polyester resin syrup; and (b) 0.3 to 10 parts by weight of aqueous sodium silicate; said composition including a polymerization initiator for unsaturated polyester resin syrup, wherein the said aqueous sodium silicate contains 45 to 85 parts by weight water and 55 to 15 parts by weight of sodium silicate solids having a weight ratio of SiO 2 Na 2 O of 1.5 to 3.75.
Claim 3
Dependent Claim
27 words
A polymerizable composition having one part by weight of the composition of claim 1 uniformly dispersed with 0.01 to 5.0 parts by weight of finely divided fillers.
Claim 4
Dependent Claim
43 words
The composition of claim 2 wherein the finely divided fillers are aluminum oxide trihydrate in an amount which is less then the sum of 1.5 times the weight of unsaturated polyester resin syrup plus 3.0 times the weight of aqueous alkali metal silicate.
Claim 5
Dependent Claim
25 words
The composition of claim 1 wherein the said unsaturated polyester resin has an acid value of 10 to 100 on a 100 percent solids basis.
Claim 6
Dependent Claim
13 words
The composition of claim 2 wherein the finely divided fillers are inert materials.
Claim 7
Dependent Claim
19 words
The composition of claim 5 wherein the finely divided fillers are perlite, comprising 0.01 to 0.10 parts by weight.
Claim 8
Dependent Claim
20 words
The composition of claim 5 wherein the finely divided fillers are expanded vermiculite, comprising 0.01 to 0.1 parts by weight.
Claim 9
Dependent Claim
28 words
The composition of claim 3 wherein the finely divided fillers are glass fibers comprising from 10 to 200 percent by weight of the said unsaturated polyester resin syrup.
Claim 10
Dependent Claim
12 words
The composition of claim 1 including an accelerator for said polymerization initiator.
Claim 11
Dependent Claim
56 words
The polymerizable composition of claim 1 wherein the said unsaturated polyester resin syrup is a combination of A. unsaturated polyester resin comprising the reaction products of polyhydric alcohol and polycarboxylic acid or anhydride, at least a portion of which are ethylenically unsaturated polycarboxylic acids or anhydrides; and B. at least one copolymerizable monomer having ethylenic unsaturation.
Claim 12
Independent Claim
93 words
The method of preparing a cured thermoset article which comprises A. mixing together under reactive conditions as an alkaline mixture 1. component 1 comprising one part by weight of an unsaturated polyester resin syrup; and 2. component 2 comprising 0.1 to 10 parts by weight of an aqueous sodium silicate containing 450 to 85 weight percent water and 55 to 15 weight percent sodium silicate solids having a weight ratio of SiO 2 /Na.sub. 2 O of 1.5 to 3.75, the said alkaline mixture including a polymerization initiator for unsaturated polyester resin syrup;
Claim 13
Independent Claim
93 words
The method of preparing a cured thermoset article which comprises A. mixing together under reactive conditions as an alkaline mixture 1. component 1 comprising one part by weight of an unsaturated polyester resin syrup; and 2. component 2 comprising 0.1 to 10 parts by weight of an aqueous sodium silicate containing 450 to 85 weight percent water and 55 to 15 weight percent sodium silicate solids having a weight ratio of SiO 2 /Na.sub. 2 O of 1.5 to 3.75, the said alkaline mixture including a polymerization initiator for unsaturated polyester resin syrup;
Claim 14
Dependent Claim
22 words
B. shaping the said alkaline mixture into a mass having the shape of the desired article; and C. curing the said mass.
Claim 15
Dependent Claim
22 words
B. shaping the said alkaline mixture into a mass having the shape of the desired article; and C. curing the said mass.
Claim 16
Dependent Claim
16 words
The method of claim 11 wherein the said polymerization initiator is an ingredient of component 1.
Claim 17
Dependent Claim
16 words
The method of claim 11 wherein the said polymerization initiator is an ingredient of component 2.
Claim 18
Dependent Claim
19 words
The method of claim 13 wherein an accelerator for the said polymerization initiator is an ingredient of component 1.
Claim 19
Dependent Claim
27 words
The method of claim 11 wherein the said alkaline mixture includes glass fibers constituting from 10 to 200 percent by weight of the said unsaturated polyester syrup.
Claim 20
Dependent Claim
22 words
The method of claim 11 wherein the component 1 includes up to 1.5 parts by weight of finely divided aluminum oxide trihydrate.
Claim 21
Dependent Claim
28 words
The method of claim 11 wherein the component 2 includes finely divided aluminum oxide trihydrate in an amount up to three times the weight of aqueous sodium silicate.
Claim 22
Dependent Claim
28 words
The method of claim 11 wherein the component 2 includes finely divided aluminum oxide trihydrate in an amount up to three times the weight of aqueous sodium silicate.
Claim 23
Dependent Claim
14 words
The method of claim 11 wherein the said alkaline mixture includes finely divided fillers.
Claim 24
Dependent Claim
14 words
The method of claim 19 wherein the said finely divided inert filler is perlite.
Claim 25
Dependent Claim
15 words
The method of claim 19 wherein the said finely divided inert filler is expanded vermiculite.
Claim 26
Dependent Claim
75 words
A water insoluble polymerized glass fiber reinforced article consisting essentially of 6 to 30 parts by weight of glass fibers and a thermoset resin produced from the composition as defined by claim 1, said article containing at least 5 percent by weight of a hybrid colloidal silica gel homogeneously dispersed with cross-linked unsaturated polyester resin syrup wherein at least a portion of the said cross-linked polyester contains carboxylate salt end groups in its polymerized state.
Claim 27
Dependent Claim
26 words
The article of claim 22 including 0.1 to 5.0 parts by weight of inert fillers dispersed throughout one part by weight of the said resin composition.
Claim 28
Dependent Claim
68 words
A fiber reinforced laminate consisting essentially of randomly oriented reinforcing fibers dispersed in a continuous phase of a thermoset resin produced from the composition as defined in claim 1, said laminate containing containing at least 5 percent by weight of a hybrid colloidal silica gel homogeneously dispersed with cross-linked unsaturated polyester resin syrup wherein at least a portion of the said cross-linked polyester contains carboxylate salt end groups.
Claim 29
Dependent Claim
11 words
The laminate of claim 24 wherein the fibers are glass fibers.
Claim 30
Dependent Claim
20 words
The laminate of claim 25 wherein the glass fibers comprise 6 to 30 percent of the weight of the laminate.
Claim 31
Dependent Claim
23 words
The laminate of claim 24 including finely divided aluminum oxide trihydrate constituting fom 10 to 50 percent of the weight of the laminate.
Claim 32
Dependent Claim
22 words
The laminate of claim 24 including finely divided inert fillers consitituting from 0.1 to 5 percent of the weight of the laminate.
References Cited (Backward Citations)
US2634208A
Cited
US3392127A
Cited
US3297616A
Cited
US3371712A
Cited
US3560253A
Cited
US3926905A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1980-03-07 | 1980-09-06 | 1981-03-08 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1984-03-07 | 1984-09-06 | 1985-03-08 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1988-03-07 | 1988-09-06 | 1989-03-08 | $7700.00 | Window Closed / Lapsed |