Intumescent flame-retardant coating compositions
Assignee: Hoechst AG
•
Filing: 1974-11-26
•
Granted: 1977-02-22
•
Expires: 1994-11-26
Abstract
Abstract Production of intumescent flame-retardant coating compositions which substantially contain a film-forming binder, an ammonium polyphosphate, one or more substances carbonizing under the action of heat, dispersing agents and fillers, if desired. The compositions contain more particularly an ammonium polyphosphate of the general formula: H.sub.(n.sub.-m).sub.+2 (NH.sub.4).sub.m P.sub.n O.sub.3n.sub.+1 in which n stands for a whole number averaging a value of more than 400 up to about 800 and the ratio of m:n is about 1.
Inventors
- 👤 Franz-Josef Dany
- 👤 Joachim Wortmann
- 👤 Joachim Kandler
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-05 13:21
CPC Classifications
C; C09; C09D; C09D5/00; C09D5/18
Claims Analysis
Total Claims: 6
Claim 1
Independent Claim
125 words
An improved intumescent flame-retardant coating composition comprising a. a film-forming binder selected from the group consisting of an aqueous polyvinyl acetate dispersion, an aqueous dispersion of a vinyl acetate-dibutylmaleate copolymer and a solution of a urea-formaldehyde resin in a solvent blend of butanol and xylene, b. about 5-25 weight %, based on the total weight of the composition, of an ammonium polyphosphate, c. a substance carbonizing under the action of heat selected from the group consisting of dicyanamide, pentaerythritol, melamine and mixtures thereof, and d. a dispersing agent, the improved coating composition containing as the b) component an ammonium polyphosphate of the formula H.sub.(n.sub.-m).sub.+2 (NH.sub.4).sub.m P.sub.n O.sub.3n.sub.+1 wherein n is an average whole number of about 600-800 and the ratio of m/n is about 1.
Claim 2
Dependent Claim
125 words
An improved intumescent flame-retardant coating composition comprising a. a film-forming binder selected from the group consisting of an aqueous polyvinyl acetate dispersion, an aqueous dispersion of a vinyl acetate-dibutylmaleate copolymer and a solution of a urea-formaldehyde resin in a solvent blend of butanol and xylene, b. about 5-25 weight %, based on the total weight of the composition, of an ammonium polyphosphate, c. a substance carbonizing under the action of heat selected from the group consisting of dicyanamide, pentaerythritol, melamine and mixtures thereof, and d. a dispersing agent, the improved coating composition containing as the b) component an ammonium polyphosphate of the formula H.sub.(n.sub.-m).sub.+2 (NH.sub.4).sub.m P.sub.n O.sub.3n.sub.+1 wherein n is an average whole number of about 600-800 and the ratio of m/n is about 1.
Claim 3
Dependent Claim
61 words
The coating compositions as claimed in claim 1, containing between about 15 and 35 weight % of film-forming binder, 5 and 25 weight % of ammonium polyphosphate, 10 and 25 weight % of at least one substance carbonizing under the action of heat, 20 and 55 weight % of dispersant and, if desired, 5 and 35 weight % of filler material.
Claim 4
Dependent Claim
27 words
The coating compositions as claimed in claim 1, wherein the dispersing agent is selected from the group consisting of water, ethyl acetate, butyl acetate, xylene or toluene.
Claim 5
Dependent Claim
36 words
The coating compositions as claimed in claim 2, wherein the fillers are selected from the group consisting of titanium dioxide, wollastonit, kaolin, magnesium silicate, potassium silicate or aluminum silicate, basic zeolite, carboxymethylcellulose, flame-retardant agents or pigments.
Claim 6
Dependent Claim
53 words
The coating compositions as claimed in claim 1, containing an ammonium polyphosphate being obtained by heating approximately equimolar proportions of ammonium orthophosphate and phosphorus pentoxide to temperatures within the range 170° and 350° C in the presence of gaseous ammonia while continually and simultaneously mixing, kneading and comminuting the material to undergo reaction.
References Cited (Backward Citations)
US3562197A
Cited
US3423343A
Cited
US3513114A
Cited
US3681273A
Cited
US3658579A
Cited
US3654190A
Cited
US3733289A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1980-02-22 | 1980-08-23 | 1981-02-22 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1984-02-22 | 1984-08-23 | 1985-02-22 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1988-02-22 | 1988-08-23 | 1989-02-22 | $7700.00 | Window Closed / Lapsed |