US4009067A
Expired / Lapsed
US
⏱️ 0.0 years remaining
Process of fabricating composite structural members
Assignee: Individual
•
Filing: 1975-07-07
•
Granted: 1977-02-22
•
Expires: 1995-07-07
Abstract
Abstract A process of fabricating a composite structural member which has opposite sides produced from preformed sheets of thermoplastic material. In carrying out the process, reinforcing material comprising fibers and thermosetting resin in the uncured state is layed on the inside of one of the performed sheets. The two preformed sheets are assembled together with the reinforcing material located there between. The edges of the preformed sheets are sealed and a vacuum drawn. The resin is then allowed to cure to cause the resin and fiber to bond together and to the performed thermoplastic sheets and which become an integral part of the structural member.
Inventors
- 👤 Charles W. Rogers
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-05 15:36
CPC Classifications
B; B29; B29D; B29D99/00; B29D99/001; B29D99/0014; B29D99/0017; B29C; B29C51/00; B29C51/16; B29C70/00; B29C70/04; B29C70/06; B29C70/08; B29C70/086; B29C70/28; B29C70/30; B29C70/34; B29C70/342; B29C70/68; B29C70/86; B29C70/865; B29C43/00; B29C43/02; B29C43/10; B29C43/12; B29K; B29K2105/00; B29K2105/04; B29K2105/06; B29K2105/08; B29K2105/10; B29K2105/101; B29K2105/108; Y; Y10; Y10T; Y10T428/00; Y10T428/24; Y10T428/24132; Y10T428/24628; Y10T428/24669; Y10T428/24694
Claims Analysis
Total Claims: 7
Claim 1
Independent Claim
324 words
The method of fabricating a structural member having two opposite sides of predetermined shapes, respectively, comprising the steps of: obtaining two preformed sheets of thermoplastic material preformed to said predetermined shapes respectively, said two preformed sheets being adapted to be assembled together with their inside surfaces facing each other, said two preformed sheets being shaped such that the inside surfaces of their outer edges will abut against each other with a cavity formed between said two preformed sheets inward of their outer edges when said two preformed sheets are assembled together, laying reinforcing material on the inside of at least one of said two preformed sheets in an area which defines the wall of said cavity, said reinforcing material comprising thermosetting resin in the uncured state reinforced with fibers, said thermosetting resin being of the type capable of bonding to said thermoplastic material, said thermoplastic sheets of material having a thickness sufficient to maintain said predetermined shapes at atmospheric pressure during lay-up of the reinforcing material but thin enough to be moved inward to seat against the reinforcing material by a pressure differential created between the inside and outside of the cavity, assembling said two preformed sheets together by abutting the inside surfaces of their outer edges with said reinforcing material located in said cavity between said two preformed sheets, sealing together the outer edges of said two preformed sheets, creating a gas pressure differential between the inside and outside of the cavity with a lower pressure maintained within the cavity relative to the pressure outside of the cavity to cause the walls of said two preformed sheets to seat against said reinforcing material, and curing said resin at a temperature less than the softening temperature of said thermoplastic material to cause said resin and said fibers to bond together and to said preformed sheets such that said preformed sheets become an integral part of said structural member and define the outer surface thereof.
Claim 2
Independent Claim
324 words
The method of fabricating a structural member having two opposite sides of predetermined shapes, respectively, comprising the steps of: obtaining two preformed sheets of thermoplastic material preformed to said predetermined shapes respectively, said two preformed sheets being adapted to be assembled together with their inside surfaces facing each other, said two preformed sheets being shaped such that the inside surfaces of their outer edges will abut against each other with a cavity formed between said two preformed sheets inward of their outer edges when said two preformed sheets are assembled together, laying reinforcing material on the inside of at least one of said two preformed sheets in an area which defines the wall of said cavity, said reinforcing material comprising thermosetting resin in the uncured state reinforced with fibers, said thermosetting resin being of the type capable of bonding to said thermoplastic material, said thermoplastic sheets of material having a thickness sufficient to maintain said predetermined shapes at atmospheric pressure during lay-up of the reinforcing material but thin enough to be moved inward to seat against the reinforcing material by a pressure differential created between the inside and outside of the cavity, assembling said two preformed sheets together by abutting the inside surfaces of their outer edges with said reinforcing material located in said cavity between said two preformed sheets, sealing together the outer edges of said two preformed sheets, creating a gas pressure differential between the inside and outside of the cavity with a lower pressure maintained within the cavity relative to the pressure outside of the cavity to cause the walls of said two preformed sheets to seat against said reinforcing material, and curing said resin at a temperature less than the softening temperature of said thermoplastic material to cause said resin and said fibers to bond together and to said preformed sheets such that said preformed sheets become an integral part of said structural member and define the outer surface thereof.
Claim 3
Dependent Claim
24 words
The method of claim 1 wherein said gas pressure differential is created by withdrawing air from said cavity formed between said two preformed sheets.
Claim 4
Independent Claim
349 words
The method of fabricating a structural member having two opposite sides of predetermined shapes, respectively, comprising the steps of: forming said two sides by preforming two sheets of thermoplastic material to said predetermined shapes, respectively, said two preformed sheets being adapted to be assembled together with their inside surfaces facing each other, said two preformed sheets being shaped such that the inside surfaces of their outer edges will abut against each other with a cavity formed between said two preformed sheets inward of their outer edges when said two preformed sheets are assembled together, laying reinforcing material on the inside of at least one of said two preformed sheets in an area which defines the wall of said cavity, said reinforcing material comprising thermosetting resin in the uncured state reinforced with fibers, said thermosetting resin having a curing temperature less than the softening temperature of said thermoplastic material and being of the type capable of bonding to said thermoplastic material, said thermoplastic sheets of material having a thickness sufficient to maintain said predetermined shapes at atmospheric pressure during lay-up of the reinforcing material but thin enough to be moved inward to seat against the reinforcing material by pressure differential created between the inside and outside of the cavity, assembling said two preformed sheets together by abutting the inside surfaces of their outer edges with said reinforcing material located in said cavity between said two preformed sheets, sealing together the outer edges of said two preformed sheets, creating a gas pressure differential between the inside and outside of the cavity with a lower pressure maintained within the cavity relative to the pressure outside of the cavity to cause the walls of said two preformed sheets to seat against said reinforcing material, and heating said assembled structural member to a temperature less than the softening temperature of said thermoplastic material but sufficient to cure said resin and to cause said resin and said fibers to bond together and to said preformed sheets such that said preformed sheets become an integral part of said structural member and define the outer surface thereof.
Claim 5
Independent Claim
349 words
The method of fabricating a structural member having two opposite sides of predetermined shapes, respectively, comprising the steps of: forming said two sides by preforming two sheets of thermoplastic material to said predetermined shapes, respectively, said two preformed sheets being adapted to be assembled together with their inside surfaces facing each other, said two preformed sheets being shaped such that the inside surfaces of their outer edges will abut against each other with a cavity formed between said two preformed sheets inward of their outer edges when said two preformed sheets are assembled together, laying reinforcing material on the inside of at least one of said two preformed sheets in an area which defines the wall of said cavity, said reinforcing material comprising thermosetting resin in the uncured state reinforced with fibers, said thermosetting resin having a curing temperature less than the softening temperature of said thermoplastic material and being of the type capable of bonding to said thermoplastic material, said thermoplastic sheets of material having a thickness sufficient to maintain said predetermined shapes at atmospheric pressure during lay-up of the reinforcing material but thin enough to be moved inward to seat against the reinforcing material by pressure differential created between the inside and outside of the cavity, assembling said two preformed sheets together by abutting the inside surfaces of their outer edges with said reinforcing material located in said cavity between said two preformed sheets, sealing together the outer edges of said two preformed sheets, creating a gas pressure differential between the inside and outside of the cavity with a lower pressure maintained within the cavity relative to the pressure outside of the cavity to cause the walls of said two preformed sheets to seat against said reinforcing material, and heating said assembled structural member to a temperature less than the softening temperature of said thermoplastic material but sufficient to cure said resin and to cause said resin and said fibers to bond together and to said preformed sheets such that said preformed sheets become an integral part of said structural member and define the outer surface thereof.
Claim 6
Dependent Claim
25 words
The method of claim 3 wherein said fibers are structural fibers selected from the class consisting of fiberglass, graphite, boron and high modulus aramid polymers.
Claim 7
Dependent Claim
24 words
The method of claim 3 wherein said gas pressure differential is created by withdrawing air from said cavity formed between said two preformed sheets.
References Cited (Backward Citations)
US3072520A
Cited
US3767740A
Cited
US3686051A
Cited
US3687768A
Cited
US3674620A
Cited
US3932249A
Cited
US3959544A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1980-02-22 | 1980-08-23 | 1981-02-22 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1984-02-22 | 1984-08-23 | 1985-02-22 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1988-02-22 | 1988-08-23 | 1989-02-22 | $7700.00 | Window Closed / Lapsed |