Cutting tool and method for making same
Assignee: Air Products and Chemicals Inc
•
Filing: 1975-04-30
•
Granted: 1977-02-22
•
Expires: 1995-04-30
Abstract
Abstract A cutting tool and method for making same are described in which a hard metal alloy coating is thermochemically deposited on the body of the tool to form a long wearing, high strength, layer. At least one cutting edge is machined in the layer.
Inventors
- 👤 Robert A. Holzl
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-26 06:26
CPC Classifications
B; B21; B21D; B21D37/00; B21D37/20; B21D37/205; B23; B23B; B23B27/00; B23B27/14; B23B27/148; B23P; B23P15/00; B23P15/28; Y; Y10; Y10T; Y10T407/00; Y10T407/27; Y10T408/00; Y10T408/78
Claims Analysis
Total Claims: 25
Claim 1
Independent Claim
137 words
A cutting tool comprising, a tool body and a thermochemically deposited hard metal alloy layer extending from at least one surface of said tool body, said layer having a thickness of at least about 25 microns and having at least one cutting edge machined within the boundaries of said layer, said thermochemically deposited hard metal alloy being comprised primarily of tungsten and carbon and having a Vickers hardnes of at least about 1,500 kg. per sq. mm. and a modulus of rupture in bending of greater than about 200 kg. per sq. mm. in the deposited or deposited and heat-treated condition, and wherein the thickness and strength of said layer are sufficient that the modulus of rupture in bending of the composite of said body and said layer is at least about 200 kg. per sq. mm.
Claim 2
Dependent Claim
137 words
A cutting tool comprising, a tool body and a thermochemically deposited hard metal alloy layer extending from at least one surface of said tool body, said layer having a thickness of at least about 25 microns and having at least one cutting edge machined within the boundaries of said layer, said thermochemically deposited hard metal alloy being comprised primarily of tungsten and carbon and having a Vickers hardnes of at least about 1,500 kg. per sq. mm. and a modulus of rupture in bending of greater than about 200 kg. per sq. mm. in the deposited or deposited and heat-treated condition, and wherein the thickness and strength of said layer are sufficient that the modulus of rupture in bending of the composite of said body and said layer is at least about 200 kg. per sq. mm.
Claim 3
Dependent Claim
36 words
A cutting tool according to claim 1 wherein the thickness of said layer is sufficient to enable said layer itself to withstand a substantial amount of the forces applied thereto as a result of cutting loads.
Claim 4
Dependent Claim
49 words
A cutting tool according to claim 1 wherein an intermediate layer of material is provided between said tool body and said hard metal alloy layer, said intermediate layer comprising a material having thermal expansion compatibility with both the material of said tool body and with said hard metal alloy.
Claim 5
Dependent Claim
19 words
A cutting tool according to claim 1 wherein said body of said tool is made of cemented tungsten carbide.
Claim 6
Dependent Claim
20 words
A cutting tool according to claim 1 wherein said body of said tool is made of tungsten or tungsten alloy.
Claim 7
Dependent Claim
20 words
A cutting tool according to claim 1 wherein said body of said tool is made of molybdenum or molybdenum alloy.
Claim 8
Independent Claim
128 words
A method for making a cutting tool comprising, thermochemically depositing on at least one surface of a body a hard metal alloy to form a layer having a thickness of at least 25 microns, said hard metal alloy being comprised primarily of tungsten and carbon and having a Vickers hardness of at least about 1,500 kg. per sq. mm., and a modulus of rupture in bending of greater than about 200 kg. per sq. mm. in the deposited or deposited and heat-treated condition, and machining at least one cutting edge in said layer, said layer having a thickness and strength after machining sufficient that the modulus of rupture in bending of the composite of said body and said layer is at least about 200 kg. per sq. mm.
Claim 9
Independent Claim
128 words
A method for making a cutting tool comprising, thermochemically depositing on at least one surface of a body a hard metal alloy to form a layer having a thickness of at least 25 microns, said hard metal alloy being comprised primarily of tungsten and carbon and having a Vickers hardness of at least about 1,500 kg. per sq. mm., and a modulus of rupture in bending of greater than about 200 kg. per sq. mm. in the deposited or deposited and heat-treated condition, and machining at least one cutting edge in said layer, said layer having a thickness and strength after machining sufficient that the modulus of rupture in bending of the composite of said body and said layer is at least about 200 kg. per sq. mm.
Claim 10
Dependent Claim
135 words
A penetrating tool comprising a shank, a body and a thermochemically deposited hard metal alloy layer extending from at least one surface of said body and having a thickness of at least about 25 microns, said layer having at least one cutting edge machined within the boundaries of said layer, said thermochemically deposited hard metal alloy being comprised primarily of tungsten and carbon and having a Vickers hardness of at least about 1,500 kg. per sq. mm. and a modulus of rupture in bending of greater than 200 kg, per sq. mm. in the deposited or deposited and heat-treated condition, wherein the thickness and strength of said layer are sufficient that the modulus of rupture in bending of the composite of said body and said layer is at least about 200 kg. per sq. mm.
Claim 11
Dependent Claim
135 words
A penetrating tool comprising a shank, a body and a thermochemically deposited hard metal alloy layer extending from at least one surface of said body and having a thickness of at least about 25 microns, said layer having at least one cutting edge machined within the boundaries of said layer, said thermochemically deposited hard metal alloy being comprised primarily of tungsten and carbon and having a Vickers hardness of at least about 1,500 kg. per sq. mm. and a modulus of rupture in bending of greater than 200 kg, per sq. mm. in the deposited or deposited and heat-treated condition, wherein the thickness and strength of said layer are sufficient that the modulus of rupture in bending of the composite of said body and said layer is at least about 200 kg. per sq. mm.
Claim 12
Dependent Claim
20 words
A penetrating tool according to claim 8 wherein said layer extends axially from said body at least about 200 microns.
Claim 13
Dependent Claim
46 words
A penetrating tool in accordance with claim 8 wherein said deposit forms a sleeve around at least a portion of said body, said sleeve having a thickness of at least about 200 microns or 25% of the finished outer diameter of the tool, whichever is less.
Claim 14
Dependent Claim
33 words
A penetrating tool according to claim 8 wherein said tool comprises a drill, wherein the end of said body is pointed, and wherein said layer extends axially from the end of said body.
Claim 15
Dependent Claim
22 words
A penetrating tool in accordance with claim 11 wherein two machined helical flutes extend axialy in both said body and said layer.
Claim 16
Dependent Claim
22 words
A penetrating tool according to claim 11 wherein two machined flat parallel surfaces extend axially in both said body and said layer.
Claim 17
Dependent Claim
29 words
A penetrating tool according to claim 8 wherein said tool comprises a punch having a flat tip, and wherein said layer extends axially from an end of said body.
Claim 18
Dependent Claim
20 words
A penetrating tool in accordance with claim 8 wherein said body of the tool is made of cemented tungsten carbide.
Claim 19
Dependent Claim
21 words
A penetrating tool in accordance with claim 8 wherein said body of the tool is made of tungsten or tungsten alloy.
Claim 20
Dependent Claim
19 words
A penetrating tool in accordance with claim 8 wherein said body of the tool is made of molybdenum alloy.
Claim 21
Independent Claim
97 words
A method for making a penetrating tool comprising, thermochemically depositing on the end of a body a hard metal alloy to form a tip having an axial dimension sufficient to allow a cutting edge to be machined therein, said hard metal alloy being comprised primarily of tungsten and carbon and having a Vickers hardness of at least about 1,500 kg. per sq. mm. and a modulus of rupture in bending of greater than about 200 kg. per sq. mm. in the deposited or deposited and heat-treated condition, and machining at least one cutting edge in said tip.
Claim 22
Independent Claim
97 words
A method for making a penetrating tool comprising, thermochemically depositing on the end of a body a hard metal alloy to form a tip having an axial dimension sufficient to allow a cutting edge to be machined therein, said hard metal alloy being comprised primarily of tungsten and carbon and having a Vickers hardness of at least about 1,500 kg. per sq. mm. and a modulus of rupture in bending of greater than about 200 kg. per sq. mm. in the deposited or deposited and heat-treated condition, and machining at least one cutting edge in said tip.
Claim 23
Dependent Claim
37 words
A method according to claim 18 wherein said tool comprises a twist drill, wherein said body is machined with helical grooves therein, and wherein said tip is machined to a point on the axis of said body.
Claim 24
Dependent Claim
33 words
A method according to claim 18 wherein said tool comprises a punch, and wherein said tip is machined to have a flat perpendicular to the tool axis and having an annular cutting edge.
Claim 25
Dependent Claim
38 words
A method according to claim 18 wherein said tool comprises a spade drill wherein substantially flat parallel surfaces are machined in said body, and wherein said tip is machined to a point on the axis of said body.
References Cited (Backward Citations)
US1485444A
Cited
US1847302A
Cited
US2858718A
Cited
US2887407A
Cited
US3574672A
Cited
US3564683A
Cited
US3565676A
Cited
US3616506A
Cited
US3658577A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1980-02-22 | 1980-08-23 | 1981-02-22 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1984-02-22 | 1984-08-23 | 1985-02-22 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1988-02-22 | 1988-08-23 | 1989-02-22 | $7700.00 | Window Closed / Lapsed |