Abstract For hydrostatically hot pressing bodies of borides, carbides or nitrides of titanium, zirconium or chromium from a powder having an excess of boron, carbon or nitrogen, the power is enclosed in a sealed container of a material which forms compounds with boron, carbon or nitrogen which have a melting point at least equal to that of the material of the container. Container materials may be for example metals from Group IVb of the Periodic System, particularly titanium and zirconium or their alloys in the case of titanium or chromium compounds and zirconium or zirconium base alloys in the case of zirconium compounds. This allows pressing at temperatures of up to 1700°-1800° C, which is high enough to cause bonding between the powder grains.
A method of manufacturing bodies of borides of titanium from a powder possibly having an excess of boron, which comprises enclosing said powder in a container selected from the group consisting of titanium and titanium base alloys, said container forming with boron, compounds which have a melting point at least equal to that of said container, and isostatically hot pressing said container.
Claim 2
Independent Claim
62 words
A method of manufacturing bodies of borides of titanium from a powder possibly having an excess of boron, which comprises enclosing said powder in a container selected from the group consisting of titanium and titanium base alloys, said container forming with boron, compounds which have a melting point at least equal to that of said container, and isostatically hot pressing said container.
Claim 3
Dependent Claim
42 words
Method as claimed in claim 1, in which the powder is titanium diboride (TiB 2 ) powder containing an excess of boron (B), and is hot pressed at at least 700 bar, at at least 1350° C for at least 0.5 hours.
Claim 4
Dependent Claim
22 words
Method as claimed in claim 2, which includes hot pressing the container at 700-3000 bar at 1350°-1500° C and for 0.5-10 hours.