Sealing material for preventing water-leakage and method of manufacturing same
Assignee: Toray Industries Inc
•
Filing: 1974-05-30
•
Granted: 1977-02-08
•
Expires: 1994-05-30
Abstract
Abstract A sealing material for the prevention of water-leakage used in, for example, waterproofed fabric and various building and construction materials is provided. The sealing material consists of (a) a water-insoluble partially saponified polyvinyl alcohol having a saponification degree of 35 to 65% by mole and a number average polymerization degree of 500 to 3,500, and (b) 5 to 100 parts by weight, based on 100 parts by weight of said partially saponified polyvinyl alcohol, of a mixture of glycerin and the glyceryl ester of a carboxylic acid.
Inventors
- 👤 Yosikazu Kosaka
- 👤 Makoto Kounosu
- 👤 Masaaki Kondo
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-01 16:05
CPC Classifications
C; C08; C08K; C08K5/00; C08K5/04; C08K5/05; C08K5/053; C08K5/10; C08K5/101; C08K5/103
Claims Analysis
Total Claims: 7
Claim 1
Independent Claim
148 words
Sealing material for prevention of waterleakage which possesses a degree of swelling with water of 50 to 300% by weight, a rate of swelling with water of 1.0 to 30% per minute and a hardness of 5 to 80 degrees, and consists essentially of (a) a water-insoluble partially saponified polyvinyl alcohol having a saponification degree of 35 to 65% by mole and a number average polymerization degree of 500 to 3,500, and (b) a mixture of glycerin and the glyceryl ester of a carboxylic acid selected from the group consisting of phthalic acid and propionic acid, the proportion of the glycerin to the glyceryl ester of a carboxylic acid being within the range of from 70:30 to 30:70 by weight and said mixture being present in an amount of 5 to 100 parts by weight based on 100 parts by weight of said water-insoluble partially saponified polyvinyl alcohol.
Claim 2
Dependent Claim
148 words
Sealing material for prevention of waterleakage which possesses a degree of swelling with water of 50 to 300% by weight, a rate of swelling with water of 1.0 to 30% per minute and a hardness of 5 to 80 degrees, and consists essentially of (a) a water-insoluble partially saponified polyvinyl alcohol having a saponification degree of 35 to 65% by mole and a number average polymerization degree of 500 to 3,500, and (b) a mixture of glycerin and the glyceryl ester of a carboxylic acid selected from the group consisting of phthalic acid and propionic acid, the proportion of the glycerin to the glyceryl ester of a carboxylic acid being within the range of from 70:30 to 30:70 by weight and said mixture being present in an amount of 5 to 100 parts by weight based on 100 parts by weight of said water-insoluble partially saponified polyvinyl alcohol.
Claim 3
Dependent Claim
206 words
A process of manufacturing a sealing material possessing a degree of swelling with water of 50 to 300% by weight, a rate of swelling with water of 1.0 to 30% per minute and a hardness of 5 to 80 degrees, which comprises the steps of: mixing (a) a water-insoluble partially saponified polyvinyl alcohol having a saponification degree of 35 to 65% by mole and a number average polymerization degree of 500 to 3,500, with (b) a mixture of glycerin and the glyceryl ester of carboxylic acid selected from the group consisting of phthalic acid and propionic acid, the proportion of the glycerin to the glyceryl ester of a carboxylic acid being within the range of from 70:30 to 30:70 by weight, in an amount of 5 to 100 parts by weight based on 100 parts by weight of said water-insoluble partially saponified polyvinyl alcohol, at a temperature of not higher than 40° C, heating the mixture to a temperature of 70° to 100° C maintaining the mixture at a temperature of 70° to 100° C until the partially saponified polyvinyl alcohol is intimately mixed with the mixture of glycerin and the glyceryl ester of a carboxylic acid and then melt shaping the intimate mixture thus obtained.
Claim 4
Dependent Claim
206 words
A process of manufacturing a sealing material possessing a degree of swelling with water of 50 to 300% by weight, a rate of swelling with water of 1.0 to 30% per minute and a hardness of 5 to 80 degrees, which comprises the steps of: mixing (a) a water-insoluble partially saponified polyvinyl alcohol having a saponification degree of 35 to 65% by mole and a number average polymerization degree of 500 to 3,500, with (b) a mixture of glycerin and the glyceryl ester of carboxylic acid selected from the group consisting of phthalic acid and propionic acid, the proportion of the glycerin to the glyceryl ester of a carboxylic acid being within the range of from 70:30 to 30:70 by weight, in an amount of 5 to 100 parts by weight based on 100 parts by weight of said water-insoluble partially saponified polyvinyl alcohol, at a temperature of not higher than 40° C, heating the mixture to a temperature of 70° to 100° C maintaining the mixture at a temperature of 70° to 100° C until the partially saponified polyvinyl alcohol is intimately mixed with the mixture of glycerin and the glyceryl ester of a carboxylic acid and then melt shaping the intimate mixture thus obtained.
Claim 5
Dependent Claim
17 words
Sealing material according to claim 1 which is prepared in the form of a sheet or film.
Claim 6
Dependent Claim
17 words
Sealing material according to claim 1 which is prepared in the form of a powder or particle.
Claim 7
Dependent Claim
17 words
Sealing material according to claim 1 which is prepared in the form of a rod or gut.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1980-02-08 | 1980-08-09 | 1981-02-08 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1984-02-08 | 1984-08-09 | 1985-02-08 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1988-02-08 | 1988-08-09 | 1989-02-08 | $7700.00 | Window Closed / Lapsed |