Reinforced composite alloys, process and apparatus for the production thereof
Assignee: Industrielle de Combustible Nucleaire Ste
•
Filing: 1974-09-27
•
Granted: 1977-02-08
•
Expires: 1994-09-27
Abstract
Abstract This invention relates to improved process and apparatus for producing reinforced composite light alloys. The improved apparatus comprises means for feeding a fluidized mixture of particulate additions, carried by a neutral gas, to a crucible in which a basic metal consisting preferably of nearly pure aluminium ingots is molten. Means are provided for stirring the contents of crucible during the feeding of said mixture thereto, in order to prevent the sedimentation or decantation of the dispersion formed therein. Means are further provided for transferring the mixture of basic metal and additions into another receptacle in which the desorption and degasing of said mixture take place.
Inventors
- 👤 Raymond Henri Sifferlen
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-26 13:41
CPC Classifications
C; C22; C22C; C22C1/00; C22C1/10; C22C1/1036; C22C1/02; B; B22; B22F; B22F2999/00; Y; Y10; Y10T; Y10T428/00; Y10T428/12; Y10T428/12486
Claims Analysis
Total Claims: 6
Claim 1
Independent Claim
199 words
A process for preparing a reinforced composite alloy without residual porosity, having improved properties and particularly good ductility, consisting of a matrix of very pure aluminium having dispersed therein 3 to 20% by weight of a refractory material addition in grain form, said addition being insoluble in aluminum both in the solid and liquid states, and said addition grains being dispersed homogeneously throughout the aluminum matrix to which they are bonded individually, said process comprising the following steps: a. forming a dispersion of grains of a refractory material using a fluidized suspension in a stream of preheated gas, which is neutral with respect to the addition grains and to the aluminum; b. desorbing moisture, oxygen and nitrogen from said grains to superficially activate said grains; c. introducing said dispersion into molten aluminum with energetic stirring, at a temperature selected in the range from 850° to 1300° C to form a homogeneous composite alloy; d. degasing the homogeneous composite alloy; e. casting and solidifying the composite alloy; f. subjecting the solidified composite alloy; to at least one hot-rolling step at about 400° C; and g. subjecting the rolled composite alloy to at least one annealing step at about 350° C.
Claim 2
Dependent Claim
199 words
A process for preparing a reinforced composite alloy without residual porosity, having improved properties and particularly good ductility, consisting of a matrix of very pure aluminium having dispersed therein 3 to 20% by weight of a refractory material addition in grain form, said addition being insoluble in aluminum both in the solid and liquid states, and said addition grains being dispersed homogeneously throughout the aluminum matrix to which they are bonded individually, said process comprising the following steps: a. forming a dispersion of grains of a refractory material using a fluidized suspension in a stream of preheated gas, which is neutral with respect to the addition grains and to the aluminum; b. desorbing moisture, oxygen and nitrogen from said grains to superficially activate said grains; c. introducing said dispersion into molten aluminum with energetic stirring, at a temperature selected in the range from 850° to 1300° C to form a homogeneous composite alloy; d. degasing the homogeneous composite alloy; e. casting and solidifying the composite alloy; f. subjecting the solidified composite alloy; to at least one hot-rolling step at about 400° C; and g. subjecting the rolled composite alloy to at least one annealing step at about 350° C.
Claim 3
Dependent Claim
47 words
A process according to claim 1, wherein said addition consists of TiB 2 grains having substantially the same average size selected in the range from one fraction of a micron to a few microns, said molten aluminum being kept at a temperature substantially equal to 900° C.
Claim 4
Dependent Claim
29 words
A process according to claim 2, wherein said matrix consists of 99.5% pure aluminum, and said addition consists of 10 to 20% by weight of said TiB 2 grains.
Claim 5
Dependent Claim
46 words
The process according to claim 1, wherein said addition consists of TiN grains having substantially the same average size selected in the range from one fraction of a micron to a few microns, the molten aluminum being kept at a temperature substantially equal to 900° C.
Claim 6
Dependent Claim
28 words
A process according to claim 4, wherein said matrix consists of 99.5% pure aluminum and said addition consists of 10 to 20% by weight of said TiN grains.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1980-02-08 | 1980-08-09 | 1981-02-08 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1984-02-08 | 1984-08-09 | 1985-02-08 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1988-02-08 | 1988-08-09 | 1989-02-08 | $7700.00 | Window Closed / Lapsed |