Production of particles for incorporation in dentifrices
Assignee: Colgate Palmolive Co
•
Filing: 1974-11-04
•
Granted: 1977-01-18
•
Expires: 1994-11-04
Abstract
Abstract Dentifrice speckles of substantially uniform shape and size are made by agitating the material of such speckles (binder plus dentifrice component) in a liquid dispersing medium at a temperature at which the binder is liquid but undissolved and unemulsified in the dispersing medium, and cooling the dispersion to a temperature below the solidification point of the speckling material so as to solidify it into speckles of desired size. Such speckles may be separated from the dispersing medium or may remain in it and be utilized with it. Preferably the speckles are incorporated in dentifrices and contain dentifrice components desirably maintained separate from the rest of the dentifrice. Also included within the invention described are the speckles and dentifrices containing them.
Inventors
- 👤 Giuseppe Mannara
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-25 03:55
CPC Classifications
A; A61; A61K; A61K8/00; A61K8/02; A61K8/0241; A61K8/0245; A61K8/18; A61K8/19; A61K8/28; A61K8/30; A61K8/33; A61K8/37; A61K8/375; A61Q; A61Q11/00; A61K2800/00; A61K2800/40; A61K2800/41
Claims Analysis
Total Claims: 10
Claim 1
Independent Claim
344 words
A process for making dentifrice speckles of substantially uniform shape and size which compriese: A. agitating a heated mixture of a speckling material and a dispersing liquid for said speckling material, said speckling material containing a dentifrice component and a binder for such component, at a temperature at which the binder is liquid, to produce a homogeneous dispersion in the dispersing liquid of individual droplets of said speckling material of sizes in the range of about 0.05 to 1 mm. effective diameter; said mixture being of about I. 1 to 40% by weight of such speckling material, which is a. about 75 to 99.9% by weight of a normally solid water insoluble organic dentifrice binder selected from the group consisting of thermoplastic resins, gums, gels, paraffins, waxes, polymers, higher fatty acids, higher fatty acid salts, lower alkylene glycol diesters, glyceryl diesters and glyceryl triesters; and b. about 0.01 to 25% by weight of a dentifrice component selected from the group consisting of fluorine-containing anti-caries agents, polishing agents, antimicrobial agents, ammoniating agents, vitamins, desensitizing agents, enzymes, optical brighteners, astringents, perservatives, flavoring agents and colorants; and Ii. about 60 to 99% by weight of a dispersing liquid which has a normal boiling point which is at least 10° C. above the solidification point of said binder and below the normal boiling point of said binder and which has a solidification point at least 20° C. below the solidification point of the binder, in which dispersing liquid the binder is substantially insoluble, said dispersing liquid being selected from the group consisting of water and aqueous solutions of lower polyhydric alcohols of 2 to 6 carbon atoms; and B. cooling such mixture of speckling material and dispersing liquid, while containing agitation thereof, to a temperature below the solidification point of said binder, at which temperature the dispersing liquid remains liquid, to obtain solid dentifrice speckles of the binder and dentifrice component in the dispersing liquid, having substantially uniform shape and sizes in the range of about 0.05 to 1 mm. effective diameter, homogeneously dispersed in said dispersing liquid.
Claim 2
Dependent Claim
344 words
A process for making dentifrice speckles of substantially uniform shape and size which compriese: A. agitating a heated mixture of a speckling material and a dispersing liquid for said speckling material, said speckling material containing a dentifrice component and a binder for such component, at a temperature at which the binder is liquid, to produce a homogeneous dispersion in the dispersing liquid of individual droplets of said speckling material of sizes in the range of about 0.05 to 1 mm. effective diameter; said mixture being of about I. 1 to 40% by weight of such speckling material, which is a. about 75 to 99.9% by weight of a normally solid water insoluble organic dentifrice binder selected from the group consisting of thermoplastic resins, gums, gels, paraffins, waxes, polymers, higher fatty acids, higher fatty acid salts, lower alkylene glycol diesters, glyceryl diesters and glyceryl triesters; and b. about 0.01 to 25% by weight of a dentifrice component selected from the group consisting of fluorine-containing anti-caries agents, polishing agents, antimicrobial agents, ammoniating agents, vitamins, desensitizing agents, enzymes, optical brighteners, astringents, perservatives, flavoring agents and colorants; and Ii. about 60 to 99% by weight of a dispersing liquid which has a normal boiling point which is at least 10° C. above the solidification point of said binder and below the normal boiling point of said binder and which has a solidification point at least 20° C. below the solidification point of the binder, in which dispersing liquid the binder is substantially insoluble, said dispersing liquid being selected from the group consisting of water and aqueous solutions of lower polyhydric alcohols of 2 to 6 carbon atoms; and B. cooling such mixture of speckling material and dispersing liquid, while containing agitation thereof, to a temperature below the solidification point of said binder, at which temperature the dispersing liquid remains liquid, to obtain solid dentifrice speckles of the binder and dentifrice component in the dispersing liquid, having substantially uniform shape and sizes in the range of about 0.05 to 1 mm. effective diameter, homogeneously dispersed in said dispersing liquid.
Claim 3
Dependent Claim
78 words
A process according to claim 1 wherein the heated mixture of speckling material and dispersing liquid is made by separately pre-heating speckling material and dispersing liquid and mixing them together, the heated mixture contains about 5 to 35% of speckling material and 65 to 95% of dispersing liquid, shear agitation is applied at the elevated temperature and the temprature to which the dispersing is cooled is at least about 20° C. below the solidification point of the binder.
Claim 4
Dependent Claim
122 words
A process according to claim 2 wherein the solidification temperature of the binder is at least 40° C., the normal boiling point of the binder is above the elevated temperature at which agitation is effected before cooling, the dispersing liquid is a liquid at room temperature, the normal boiling point of the dispersing liquid is below about 300° C., the temperature at which the dispersion is effected is between about 50° and 190° C., the temperature to which the dispersion is cooled is about room temperature, the shear agitation is turbulent flow agitation at 0.002 to 0.2 horsepower per kilogram of mixture and the viscosity of the mixture during agitation at elevated temperature is in the range of 0.1 to 500 centipoises.
Claim 5
Dependent Claim
52 words
A process according to claim 3 wherein the heated mixture contains about 10 to 25% of speckling material and 75 to 90% of dispersing liquid, the dispersing liquid is water, the elevated temperature at which dispersion is effected is below 100° C. and the solid speckles are separated from the dispersing liquid.
Claim 6
Dependent Claim
68 words
A process according to claim 4 whether the shear agitation is equivlent to that of a mixer having a blade size of over seven centimeters in diameter which is rotating at over 150 revolutions per minute, the speckling material contains about 0.01 to 2% of colorant which is mixed with molten binder before the speckling material is mixed with the dispersing liquid and the binder is glyceryl tristearate.
Claim 7
Dependent Claim
55 words
A process according to claim 5 wherein the colorant is present in the speckling material at a concentration of about 1% based on the weight of the speckling material and the agitation is effected by means of a mixer withh a blade having a linear peripheral speed of about 5 to 100 meters per second.
Claim 8
Dependent Claim
13 words
A process according to claim 6 wherein the colorant is oil soluble chlorphyll.
Claim 9
Dependent Claim
20 words
A process according to claim 7 wherein the speckling material contains about 20% of zirconium silicate as a polishing agent.
Claim 10
Dependent Claim
19 words
A process according to claim 8 wherein the speckling material contains about 20% of menthol as a flavoring agent.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1980-01-18 | 1980-07-19 | 1981-01-18 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1984-01-18 | 1984-07-19 | 1985-01-18 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1988-01-18 | 1988-07-19 | 1989-01-18 | $7700.00 | Window Closed / Lapsed |