Method for electroless copper plating
Assignee: Panasonic Holdings Corp
•
Filing: 1975-04-18
•
Granted: 1977-01-11
•
Expires: 1995-04-18
Abstract
Abstract This invention provides a method for electroless copper plating comprising: providing an electroless copper plating bath composition which comprises 0.005 to 0.3 mole per liter of a water soluble copper compound, 0.005 to 0.6 mole per liter of a cupric complexing agent, 0.02 to 3.0 mole per liter of formaldehyde, 0.01 to 1000 milligram per liter of additive agent selected from the group consisting of 2,2'-dipyridyl, 2,9-dimethyl-1,10-phenanthroline and 2-(2-phridyl)-benzimidazole, and alkaline compound to hold the pH of said aqueous solution 10.5 to 14 and immersing a material having catalytic action at the surface into said electroless copper plating bath composition kept at a temperature of 70 DEG to 90 DEG C whereby copper film with a high mechanical strength is deposited on said material.
Inventors
- 👤 Hyogo Hirohata
- 👤 Masahiro Oita
- 👤 Katsuhiko Honjo
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-05 06:42
CPC Classifications
C; C23; C23C; C23C18/00; C23C18/16; C23C18/31; C23C18/38; C23C18/40; C23C18/405
Claims Analysis
Total Claims: 9
Claim 1
Independent Claim
115 words
A method for electroless copper plating comprising providing an electroless copper plating bath which comprises 0.005 to 0.3 mole per liter of a water soluble copper salt, 0.005 to 0.6 mole per liter of ethylenediaminetetraacetate as a complexing agent for cupric ions, 0.02 to 3.0 mole per liter of formaldehyde, 0.05 to 1000 milligrams per liter of 2,2'-dipyridyl and an alkaline compound to maintain the pH of said aqueous solution to between 10.5 and 14 and immersing a material having catalytic action at the surface into said electroless copper plating bath composition maintained at a temperature of 70° to 90° C whereby a copper film having a high mechanical strength is deposited on said material.
Claim 2
Independent Claim
115 words
A method for electroless copper plating comprising providing an electroless copper plating bath which comprises 0.005 to 0.3 mole per liter of a water soluble copper salt, 0.005 to 0.6 mole per liter of ethylenediaminetetraacetate as a complexing agent for cupric ions, 0.02 to 3.0 mole per liter of formaldehyde, 0.05 to 1000 milligrams per liter of 2,2'-dipyridyl and an alkaline compound to maintain the pH of said aqueous solution to between 10.5 and 14 and immersing a material having catalytic action at the surface into said electroless copper plating bath composition maintained at a temperature of 70° to 90° C whereby a copper film having a high mechanical strength is deposited on said material.
Claim 3
Dependent Claim
46 words
A method according to claim 1, wherein the water soluble copper salt is selected from the group consisting of copper sulfate, copper nitrate, copper chloride and copper acetate and the alkaline compound is a member selected from the group consisting of sodium hydroxide and sodium carbonate.
Claim 4
Independent Claim
116 words
A method for electroless copper plating comprising providing an electroless copper plating bath which comprises 0.005 to 0.3 mole per liter of a water soluble copper salt, 0.005 to 0.6 mole per liter of ethylenediaminetetraacetate as a complexing agent for cupric ions, 0.02 to 3.0 mole per liter of formaldehyde, 10 to 1000 milligrams per liter of 2,9-dimethyl-1, 10-phenanthroline and an alkaline compound to maintain the pH of said aqueous solution to between 10.5 and 14 and immersing a material having catalytic action at the surface into said electroless copper plating bath composition maintained at a temperature of 70° to 90° C whereby a copper film having a high mechanical strength is deposited on said material.
Claim 5
Independent Claim
116 words
A method for electroless copper plating comprising providing an electroless copper plating bath which comprises 0.005 to 0.3 mole per liter of a water soluble copper salt, 0.005 to 0.6 mole per liter of ethylenediaminetetraacetate as a complexing agent for cupric ions, 0.02 to 3.0 mole per liter of formaldehyde, 10 to 1000 milligrams per liter of 2,9-dimethyl-1, 10-phenanthroline and an alkaline compound to maintain the pH of said aqueous solution to between 10.5 and 14 and immersing a material having catalytic action at the surface into said electroless copper plating bath composition maintained at a temperature of 70° to 90° C whereby a copper film having a high mechanical strength is deposited on said material.
Claim 6
Dependent Claim
46 words
A method according to claim 3, wherein the water soluble copper salt is selected from the group consisting of copper sulfate, copper nitrate, copper chloride and copper acetate and the alkaline compound is a member selected from the group consisting of sodium hydroxide and sodium carbonate.
Claim 7
Independent Claim
113 words
A method for electroless copper plating comprising providing an electroless copper plating bath which comprises 0.005 to 0.3 mole per liter of a water soluble copper salt, 0.005 to 0.6 mole per liter of ethylenediaminetetraacetate as a complexing agent for cupric ions, 0.02 to 3.0 mole per liter of formaldehyde, 1-1000 milligrams per liter of 2-(2-pyridyl)-benzimidazole and an alkaline compound to maintain the pH of said aqueous solution to between 10.5 and 14 and immersing a material having catalytic action at the surface into said electroless copper plating bath composition maintained at a temperature of 70° to 90° C whereby a copper film with a high mechanical strength is deposited on said material.
Claim 8
Independent Claim
113 words
A method for electroless copper plating comprising providing an electroless copper plating bath which comprises 0.005 to 0.3 mole per liter of a water soluble copper salt, 0.005 to 0.6 mole per liter of ethylenediaminetetraacetate as a complexing agent for cupric ions, 0.02 to 3.0 mole per liter of formaldehyde, 1-1000 milligrams per liter of 2-(2-pyridyl)-benzimidazole and an alkaline compound to maintain the pH of said aqueous solution to between 10.5 and 14 and immersing a material having catalytic action at the surface into said electroless copper plating bath composition maintained at a temperature of 70° to 90° C whereby a copper film with a high mechanical strength is deposited on said material.
Claim 9
Dependent Claim
46 words
A method according to claim 5, wherein the water soluble copper salt is selected from the group consisting of copper sulfate, copper nitrate, copper chloride and copper acetate and the alkaline compound is a member selected from the group consisting of sodium hydroxide and sodium carbonate.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1980-01-11 | 1980-07-12 | 1981-01-11 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1984-01-11 | 1984-07-12 | 1985-01-11 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1988-01-11 | 1988-07-12 | 1989-01-11 | $7700.00 | Window Closed / Lapsed |