Method of forming a thin film capacitor
Assignee: Kyocera Avx Components Corp
•
Filing: 1976-02-09
•
Granted: 1977-01-11
•
Expires: 1996-02-09
Abstract
Abstract A method of forming a thin film capacitor having a tantalum oxide dielectric is described. A dielectric substrate having formed thereon a duplex electrically conductive film comprising a non-tantalum electrically conductive film electrode covered by a thin tantalum film is disposed within an oxygen-inert gas containing vacuum environment, said non-tantalum film being disposed intermediate said substrate and said tantalum film. A film of tantalum oxide is applied over the conductive film by r-f sputtering of a tantalum oxide target within the oxygen-inert gas containing vacuum environment while the dielectric substrate and conductive film are being cooled. The composite may then be removed from said oxygen-inert gas containing environment and a second electrically conductive film electrode applied over the so-formed tantalum oxide film.
Inventors
- 👤 Francis P. Fehiner
- 👤 Arthur J. Whitman
- 👤 Peter L. Young
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-29 18:23
CPC Classifications
C; C23; C23C; C23C14/00; C23C14/06; C23C14/08; C23C14/083; C23C14/14; C23C14/18; H; H01; H01G; H01G4/00; H01G4/002; H01G4/018; H01G4/06; H01G4/08; Y; Y10; Y10T; Y10T29/00; Y10T29/43; Y10T29/435
Claims Analysis
Total Claims: 11
Claim 1
Independent Claim
131 words
A method of forming a capacitor comprising the sequential steps of providing a dielectric substrate, applying to said dielectric substrate a non-tantalum electrically conductive film to form a first capacitor electrode, applying over said electrode a thin film of tantalum which together with said electrically conductive film forms a duplex film, disposing said substrate and said duplex film within a vacuum environment containing an oxygen-inert gas mixture, r-f sputtering a film of tantalum oxide of desired thickness over said duplex film within said vacuum environment, said tantalum oxide being sputtered from a tantalum oxide target, cooling said dielectric substrate and duplex film while said film of tantalum oxide is being sputtered thereon, and thereafter applying an electrically conductive film over said film of tantalum oxide to form a counter capacitor electrode.
Claim 2
Independent Claim
131 words
A method of forming a capacitor comprising the sequential steps of providing a dielectric substrate, applying to said dielectric substrate a non-tantalum electrically conductive film to form a first capacitor electrode, applying over said electrode a thin film of tantalum which together with said electrically conductive film forms a duplex film, disposing said substrate and said duplex film within a vacuum environment containing an oxygen-inert gas mixture, r-f sputtering a film of tantalum oxide of desired thickness over said duplex film within said vacuum environment, said tantalum oxide being sputtered from a tantalum oxide target, cooling said dielectric substrate and duplex film while said film of tantalum oxide is being sputtered thereon, and thereafter applying an electrically conductive film over said film of tantalum oxide to form a counter capacitor electrode.
Claim 3
Dependent Claim
22 words
The method of claim 1 wherein said oxygen and inert gas mixture comprises at least about 4 percent by volume of oxygen.
Claim 4
Dependent Claim
14 words
The method of claim 1 wherein said first capacitor electrode is formed of aluminum.
Claim 5
Dependent Claim
14 words
The method of claim 3 wherein said counter capacitor electrode is formed of gold.
Claim 6
Dependent Claim
22 words
The method of claim 1 wherein said vacuum environment has a pressure of about 5 × 10 - 3 Torr or less.
Claim 7
Dependent Claim
39 words
The method of claim 4 wherein said oxygen and inert gas mixture comprises at least about 4 percent by volume of oxygen and said vacuum environment has a pressure of about 5 × 10 - 3 Torr or less.
Claim 8
Dependent Claim
22 words
The method of claim 6 wherein at least one of said first electrode and counter electrode is applied by physical vapor deposition.
Claim 9
Dependent Claim
24 words
The method of claim 1 wherein said counter electrode is formed of a material selected from the group consisting of gold, copper, and silver.
Claim 10
Dependent Claim
18 words
The method of claim 1 wherein said duplex film and counter electrode are applied in a vacuum atmosphere.
Claim 11
Dependent Claim
81 words
The method of claim 1 wherein said oxygen and inert gas mixture comprises at least about 4 percent by volume of oxygen and said vacuum environment has a pressure of about 5 × 10 - 3 Torr or less; said first capacitor electrode is formed of aluminum; said counter electrode is formed of a material selected from the group consisting of gold, copper and silver; and said first capacitor electrode, tantalum film and counter electrode are applied in a vacuum atmosphere.
References Cited (Backward Citations)
US3257305A
Cited
US3969197A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1980-01-11 | 1980-07-12 | 1981-01-11 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1984-01-11 | 1984-07-12 | 1985-01-11 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1988-01-11 | 1988-07-12 | 1989-01-11 | $7700.00 | Window Closed / Lapsed |