Making a conglomerated bonded mass consisting of particles of activated carbon
Assignee: PATENT PROTECTION Ltd
•
Filing: 1970-08-11
•
Granted: 1976-12-28
•
Expires: 1990-08-11
Abstract
Abstract A method of forming a conglomerated, bonded and preferably molded mass of particles of activated carbon bonded together by means of a polymer which is rendered adhesive by a solvent permeating a random and loose mass of the carbon particles and subsequently drained off.
Inventors
- 👤 Cyril A. Redfarn
- 👤 John Bedford
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-26 15:13
CPC Classifications
C; C04; C04B; C04B35/00; C04B35/515; C04B35/52; C04B35/524; C01; C01B; C01B32/00; C01B32/30; C01B32/354; C01B32/384
Claims Analysis
Total Claims: 12
Claim 1
Independent Claim
247 words
A method of making a conglomerated bonded porous mass of activated carbon particles, comprising: a. permeating a random and loose mass of activated carbon particles with a solvent in which a subsequently employed polymer is soluble; b. removing said solvent from said carbon particles to the extent of leaving substantially only the internal pores of said carbon particles containing said solvent; c. mixing the solvent permeated carbon particles from step (b) with dry particles of a solid polymer soluble in said solvent, said polymer particles having a particle size which is not too fine a mesh in order to avoid their solubilizing and spreading over the superficies of said carbon particles, said polymer particles being present in an amount to position said polymer particles at points of contact between adjacent carbon particles over relatively small areas of each carbon particle surface; d. evaporating some of said solvent in a manner to cause the solvent to leave the pores of the carbon particles and contact the adjacent polymer particles to solvate at least a portion of the polymer particles and render the particles adhesive at their points of contact with said carbon particles; and e. removing the remaining solvent by evaporation, whereby said carbon particles and polymer particles are rigidly bonded by said polymer particles as a conglomerated mass in which the superficies of the carbon particles are covered by said solvated polymer particles over relatively small areas of contact between the carbon particles and the polymer particles.
Claim 2
Independent Claim
247 words
A method of making a conglomerated bonded porous mass of activated carbon particles, comprising: a. permeating a random and loose mass of activated carbon particles with a solvent in which a subsequently employed polymer is soluble; b. removing said solvent from said carbon particles to the extent of leaving substantially only the internal pores of said carbon particles containing said solvent; c. mixing the solvent permeated carbon particles from step (b) with dry particles of a solid polymer soluble in said solvent, said polymer particles having a particle size which is not too fine a mesh in order to avoid their solubilizing and spreading over the superficies of said carbon particles, said polymer particles being present in an amount to position said polymer particles at points of contact between adjacent carbon particles over relatively small areas of each carbon particle surface; d. evaporating some of said solvent in a manner to cause the solvent to leave the pores of the carbon particles and contact the adjacent polymer particles to solvate at least a portion of the polymer particles and render the particles adhesive at their points of contact with said carbon particles; and e. removing the remaining solvent by evaporation, whereby said carbon particles and polymer particles are rigidly bonded by said polymer particles as a conglomerated mass in which the superficies of the carbon particles are covered by said solvated polymer particles over relatively small areas of contact between the carbon particles and the polymer particles.
Claim 3
Dependent Claim
22 words
A method according to claim 1 in which the particulate dry solid soluble polymer is an uncured polymer which is heat curable.
Claim 4
Dependent Claim
40 words
A method according to claim 2 in which the conglomerated bonded mass of activated carbon particles and dry solid soluble polymer particles is heated after step (e) so as to cure the polymer particles and render said mass solvent resistant.
Claim 5
Dependent Claim
19 words
A method according to claim 3 in which the particulate dry solid soluble polymer is polyacrylamide mixed with paraformaldehyde.
Claim 6
Dependent Claim
27 words
A method according to claim 1 in which the conglomerated bonded mass of activated carbon particles and particulate dry solid soluble polymer is formed in a mold.
Claim 7
Dependent Claim
15 words
A method according to claim 1 in which the said evaporation is effected by heating.
Claim 8
Dependent Claim
48 words
Method according to claim 1 in which the ratio of weight of polymer to weight of carbon is in an inverse relationship with the grade of carbon particles used and is so selected as to involve the least amount of polymer which will ensure conglomeration of the mass.
Claim 9
Dependent Claim
25 words
A method according to claim 1 in which the conglomerated bonded mass of activated carbon particles is formed in a mold made of perforated metal.
Claim 10
Dependent Claim
31 words
A method according to claim 1 in which the conglomerated mass is formed in a mold partially lined with a lamina of porous textile material adapted to adhere to the mass.
Claim 11
Dependent Claim
92 words
A process according to claim 1 in which said solvent and said particulate dry solid soluble polymer are selected from the group consisting of water and hydroxypropyl methyl cellulose, water and cellulose derivatives related to hydroxypropyl methyl cellulose, water and polyvinyl alcohol, water and polyacrylamide, water and urea-formaldehyde resins, water and casein, ethanol and polyvinyl butyral, ethanol and phenol-formaldehyde resins, acetone and polyvinyl acetate, acetone and cellulose acetate, ethyl methyl ketone and vinyl chloride vinyl adetate copolymers, a mixed solvent of ethanol and toluene and polyvinyl formal, and carbon tetrachloride and polystyrene.
Claim 12
Dependent Claim
45 words
A process according to claim 1 in which said solvent is water and said particulate dry solid soluble polymer is polyacrylamide and paraformaldehyde and in which the conglomerated bonded mass of activated carbon particles is heated after step (e) to cure the polyacrylamide paraformaldehyde bond.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1979-12-28 | 1980-06-28 | 1980-12-28 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1983-12-28 | 1984-06-28 | 1984-12-28 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1987-12-28 | 1988-06-28 | 1988-12-28 | $7700.00 | Window Closed / Lapsed |