Wrought pure grade aluminum alloy and process for producing same
Assignee: National Aluminum Corp
•
Filing: 1975-03-26
•
Granted: 1976-12-28
•
Expires: 1995-03-26
Abstract
Abstract Pure aluminum alloy which has been continuously cast and partially worked to a strip at a gauge of 0.25 inches through use of a Hunter-Caster, is heated to a temperature in a range of about 900 DEG to about 1150 DEG F. and then subjected to slow cooling in a range between cooling at around 600 DEG F./hr. as a maximum, and cooling at a rate of 25 DEG F./hr. as a practical minimum, until ambient temperature or about 100 DEG F. is reached. After cooling, the alloy strip is subjected to cold working and annealing until a desired gauge is reached for a particular product, one typical product being aluminum foil. In one process according to the invention, the strip is heated as it leaves a Hunter-Caster and then coiled, and the cooling is effected by leaving the coil in ambient air. In another process, it is coiled prior to heating which is then effected by placing the coil in a suitable furnace such as in box annealing. The coil is then cooled in the furnace, either as the furnace cools naturally or at a slower, controlled cooling rate. In another preferred process the alloy strip produced by the Hunter-Caster is subjected to conventional cold working until a suitable gauge, for example, 0.050 inches is reached. At this point, rather than subjecting the alloy to a conventional annealing process, it is subjected to the heat treatment and slow cooling described after which it is then cold worked further and subjected to a final stress relieving anneal at approximately 400 DEG F. The heating and slow cooling of the present invention improve the ductility and recrystallization kinetics of wrought pure aliminum produced through continuous casting, cold rolling and annealing.
Inventors
- 👤 David A. Chatfield
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-04 16:33
CPC Classifications
C; C22; C22F; C22F1/00; C22F1/04; B; B22; B22D; B22D11/00; B22D11/06; B22D11/0605
Claims Analysis
Total Claims: 45
Claim 1
Independent Claim
138 words
In a process of producing a wrought sheet of aluminum alloy of the class of pure and super pure grade containing not less than 99.00% aluminum wherein the molten alloy is continuously cast to form a sheet and the sheet cold reduced and annealed; the steps comprising: heating the continuously cast sheet to a temperature in the range of approximately 900° to 1150° F. after the sheet has been continuously cast to a first thickness gauge, and then cooling the heated continuously cast sheet at a rate not greater than a rate of cooling of about 600° F. per hour so as to precipitate impurities in such a size as will result in desired recrystallization of the grain structure of the sheet thereby to enhance the ductility of the alloy upon cold working and annealing of the sheet.
Claim 2
Dependent Claim
138 words
In a process of producing a wrought sheet of aluminum alloy of the class of pure and super pure grade containing not less than 99.00% aluminum wherein the molten alloy is continuously cast to form a sheet and the sheet cold reduced and annealed; the steps comprising: heating the continuously cast sheet to a temperature in the range of approximately 900° to 1150° F. after the sheet has been continuously cast to a first thickness gauge, and then cooling the heated continuously cast sheet at a rate not greater than a rate of cooling of about 600° F. per hour so as to precipitate impurities in such a size as will result in desired recrystallization of the grain structure of the sheet thereby to enhance the ductility of the alloy upon cold working and annealing of the sheet.
Claim 3
Dependent Claim
28 words
The process defined in claim 1 wherein the cooling rate is not greater than approximately 350° F. per hour and not less than about 25° F. per hour.
Claim 4
Dependent Claim
55 words
The process defined in claim 1 wherein after the sheet has been continuously cast to the first thickness gauge, the sheet is coiled, and wherein said heating and cooling are imparted to the coiled sheet after which the coil is unwound and the sheet reduced further in gauge by cold working and then is annealed.
Claim 5
Dependent Claim
33 words
The process defined in claim 3 wherein the heated coiled sheet is cooled at a rate not greater than approximately 350° F. per hour and not less than approximately 25° F. per hour.
Claim 6
Dependent Claim
29 words
The process defined in claim 1 wherein the continuously cast sheet is formed of 1145 aluminum alloy and wherein the continuously casting is effected by means of a Hunter-Caster.
Claim 7
Dependent Claim
50 words
The process defined in claim 1 wherein after the sheet is heated the sheet is coiled and said cooling is effected by holding the coiled sheet in ambient air and wherein after cooling the coiled sheet is unwound and the sheet further cold worked to reduce its gauge and annealed.
Claim 8
Dependent Claim
64 words
The process defined in claim 1 wherein after the sheet is continuously cast to said first thickness gauge, the sheet is further reduced to a second gauge by cold working and wherein said heating and cooling steps are applied to the sheet in the second gauge condition after which the sheet is subjected to another cold reduction followed by said annealing to relieve stresses.
Claim 9
Dependent Claim
37 words
The process defined in claim 7 wherein the first gauge is approximately 0.25 inches and the second gauge is approximately 0.050 inches and wherein the stress relief annealing step is conducted at a temperature of 400° F.
Claim 10
Dependent Claim
29 words
The process defined in claim 8 wherein the continuously cast sheet is formed of 1145 aluminum alloy and wherein the continuous casting is effected by means of a Hunter-Caster.
Claim 11
Dependent Claim
28 words
The process defined in claim 7 wherein the cooling rate is not greater than approximately 350° F. per hour and not less than about 25° F. per hour.
Claim 12
Dependent Claim
20 words
The process defined in claim 8 wherein after the annealing step the sheet is further cold reduced to foil gauge.
Claim 13
Dependent Claim
22 words
The process defined in claim 1 wherein the sheet is cooled to a temperature of approximately 100° F. in the cooling step.
Claim 14
Dependent Claim
33 words
The process defined in claim 1 wherein after cooling the sheet is cold worked further to reduce its gauge then subjected to said annealing at a temperature of about 650° to 700° F.
Claim 15
Dependent Claim
35 words
The process defined in claim 13 wherein after annealing the sheet is further cold worked to further reduce its gauge and then is annealed again at a temperature of about 400° F. to relieve stresses.
Claim 16
Dependent Claim
22 words
The process defined in claim 14 wherein after the last defined annealing step the sheet is further cold reduced to foil gauge.
Claim 17
Dependent Claim
26 words
The process defined in claim 1 wherein the sheet is held at said temperature for a period of time up to eight hours prior to cooling.
Claim 18
Dependent Claim
55 words
The process defined in claim 2 wherein after the sheet has been continuously cast to the first thickness gauge, the sheet is coiled, and wherein said heating and cooling are imparted to the coiled sheet after which the coil is unwound and the sheet reduced further in gauge by cold working and then is annealed.
Claim 19
Dependent Claim
27 words
The process defined in claim 2 wherein the sheet is formed of 1145 aluminum alloy and wherein the continuous casting is effected by means of a Hunter-Caster.
Claim 20
Dependent Claim
50 words
The process defined in claim 2 wherein after the sheet is heated the sheet is coiled and said cooling is effected by holding the coiled sheet in ambient air and wherein after cooling the coiled sheet is unwound and the sheet further cold worked to reduce its gauge and annealed.
Claim 21
Dependent Claim
64 words
The process defined in claim 2 wherein after the sheet is continuously cast to said first thickness gauge, the sheet is further reduced to a second gauge by cold working and wherein said heating and cooling steps are applied to the sheet in the second gauge condition after which the sheet is subjected to another cold working followed by said annealing to relieve stresses.
Claim 22
Dependent Claim
37 words
The process defined in claim 20 wherein the first gauge is approximately 0.25 inches and the second gauge is approximately 0.050 inches and wherein the stress relief annealing step is conducted at a temperature of 400° F.
Claim 23
Dependent Claim
22 words
The process defined in claim 2 wherein the sheet is cooled to a temperature of approximately 100° F. in the cooling step.
Claim 24
Dependent Claim
16 words
A continuously cast aluminum alloy sheet of improved ductility produced by the process of claim 1.
Claim 25
Dependent Claim
16 words
A continuously cast aluminum alloy sheet of improved ductility produced by the process of claim 2.
Claim 26
Dependent Claim
18 words
A cold reduced and annealed aluminum alloy sheet of improved ductility produced by the process of claim 3.
Claim 27
Dependent Claim
18 words
A cold reduced and annealed aluminum alloy sheet of improved ductility produced by the process of claim 4.
Claim 28
Dependent Claim
16 words
A continuously cast aluminum alloy sheet of improved ductility produced by the process of claim 5.
Claim 29
Dependent Claim
18 words
A cold reduced and annealed aluminum alloy sheet of improved ductility produced by the process of claim 6.
Claim 30
Dependent Claim
18 words
A cold reduced and annealed aluminum alloy sheet of improved ductility produced by the process of claim 7.
Claim 31
Dependent Claim
18 words
A cold reduced and annealed aluminum alloy sheet of improved ductility produced by the process of claim 8.
Claim 32
Dependent Claim
18 words
A cold reduced and annealed aluminum alloy sheet of improved ductility produced by the process of claim 9.
Claim 33
Dependent Claim
18 words
A cold reduced and annealed aluminum alloy sheet of improved ductility produced by the process of claim 10.
Claim 34
Dependent Claim
14 words
An aluminum alloy foil of improved ductility produced by the process of claim 11.
Claim 35
Dependent Claim
16 words
A continuously cast aluminum alloy sheet of improved ductility produced by the process of claim 12.
Claim 36
Dependent Claim
18 words
A cold reduced and annealed aluminum alloy sheet of improved ductility produced by the process of claim 13.
Claim 37
Dependent Claim
18 words
A cold reduced and annealed aluminum alloy sheet of improved ductility produced by the process of claim 14.
Claim 38
Dependent Claim
14 words
An aluminum alloy foil of improved ductility produced by the process of claim 15.
Claim 39
Dependent Claim
16 words
A continuously cast aluminum alloy sheet of improved ductility produced by the process of claim 16.
Claim 40
Dependent Claim
18 words
A cold reduced and annealed aluminum alloy sheet of improved ductility produced by the process of claim 17.
Claim 41
Dependent Claim
16 words
A continuously cast aluminum alloy sheet of improved ductility produced by the process of claim 18.
Claim 42
Dependent Claim
18 words
A cold reduced and annealed aluminum alloy sheet of improved ductility produced by the process of claim 19.
Claim 43
Dependent Claim
18 words
A cold reduced and annealed aluminum alloy sheet of improved ductility produced by the process of claim 20.
Claim 44
Dependent Claim
18 words
A cold reduced and annealed aluminum alloy sheet of improved ductility produced by the process of claim 21.
Claim 45
Dependent Claim
16 words
A continuously cast aluminum alloy sheet of improved ductility produced by the process of claim 22.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1979-12-28 | 1980-06-28 | 1980-12-28 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1983-12-28 | 1984-06-28 | 1984-12-28 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1987-12-28 | 1988-06-28 | 1988-12-28 | $7700.00 | Window Closed / Lapsed |