Assignee: Nippon Steel Corp
•
Filing: 1975-09-29
•
Granted: 1976-12-28
•
Expires: 1995-09-29
Abstract
Abstract A quicklime is treated by CO2 gas so as to form a CaCO3 film on the surface of the particle thereof. It serves to prevent moisture absorption so that a steel making process, especially for the production of low hydrogen steel, can be done very effectively with low cost by the use of this CO2-treated lime.
Inventors
- 👤 Mitsuo Furuya
- 👤 Shigehiro Kimura
- 👤 Hiroyuki Kajioka
- 👤 Hiroyuki Katayama
- 👤 Kiyomi Shio
- 👤 Arata Tanaka
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-27 06:24
CPC Classifications
C; C21; C21C; C21C7/00; C21C7/04; C21C7/076; Y; Y02; Y02P; Y02P10/00; Y02P10/20
Claims Analysis
Total Claims: 10
Claim 1
Independent Claim
104 words
A method for making a flux for use in a steel making operation to reduce the hydrogen content of steel produced by such operation, said flux being characterized by having excellent moistureproof property, which method comprises calcining a material selected from the group consisting of limestone and dolomite to decompose said material to produce calcium oxide, and immediately thereafter uniformly reacting the outer surfaces of particles of said material with a sufficient amount of a carbon dioxide-containing gas to convert from about 2% to about 30% by weight of the calcium oxide in said particles to a film of calcium carbonate on said particles.
Claim 2
Independent Claim
104 words
A method for making a flux for use in a steel making operation to reduce the hydrogen content of steel produced by such operation, said flux being characterized by having excellent moistureproof property, which method comprises calcining a material selected from the group consisting of limestone and dolomite to decompose said material to produce calcium oxide, and immediately thereafter uniformly reacting the outer surfaces of particles of said material with a sufficient amount of a carbon dioxide-containing gas to convert from about 2% to about 30% by weight of the calcium oxide in said particles to a film of calcium carbonate on said particles.
Claim 3
Dependent Claim
18 words
The method according to claim 1 in which said carbon dioxide-containing gas contains at least 20% carbon dioxide.
Claim 4
Dependent Claim
29 words
The method according to claim 1 in which the reacting of the material with the carbon dioxide-containing gas is carried out at temperatures between 300° C and 750° C.
Claim 5
Dependent Claim
41 words
The method according to claim 1 in which the particles of decomposed material are subjected to mutual movement with each other while said reaction is being carried out to effect uniform reacting of the surfaces thereof with the carbon dioxide-containing gas.
Claim 6
Dependent Claim
29 words
The method according to claim 1 in which the reacting of the material with the carbon dioxide-containing gas is completed at the final temperature of 350° C or less.
Claim 7
Dependent Claim
38 words
The method according to claim 3 in which the reacting of the material with the carbon dioxide-containing gas is completed by effecting a gradual cooling from about 400° C to about 300° C for at least 20 minutes.
Claim 8
Dependent Claim
22 words
The method according to claim 1 in which the carbon dioxide-containing gas contains the carbon dioxide produced by decomposition of the material.
Claim 9
Dependent Claim
46 words
The method according to claim 1 in which the decomposed material is sieved in an oscillating sieving operation to remove lumps and powders therefrom, the remaining decomposed material being subjected to adjustment of the particle size thereof before reacting with same with the carbon dioxide-containing gas.
Claim 10
Dependent Claim
11 words
A flux produced in accordance with the method of claim 1.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1979-12-28 | 1980-06-28 | 1980-12-28 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1983-12-28 | 1984-06-28 | 1984-12-28 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1987-12-28 | 1988-06-28 | 1988-12-28 | $7700.00 | Window Closed / Lapsed |