Method of preparing phenolaldehyde foamed plastics
Assignee: Individual
•
Filing: 1974-10-03
•
Granted: 1976-12-21
•
Expires: 1994-10-03
Abstract
Abstract A method of preparing a phenolaldehyde foamed plastic which involves mixing (1) a phenolaldehyde oligomer, such as a resol-type resin, or a mixture of such a resol-type resin with a novolac-type resin, (2) an acidic catalyst, such as an oligomeric product obtained by the treatment of an aromatic sulphoacid with formaldehyde, or an oligomeric product obtained by the treatment of an aromatic sulphoacid with formaldehyde and a nitrogen-containing compound, such as urea, aniline, and 4.4-diaminodiphenolmethane, (3) a compound of a complex-forming metal, such as cobalt, magnesium, manganese, vanadium, chromium, nickel, copper, iron, titanium, and lead, in the form of its oxide, hydroxide, salt, or mixtures thereof, (4) a surfactant, and (5) a foaming agent. The resulting mixture is foamed and cured at a temperature up to 100 DEG C. Introduction of the complex-forming metal insures improved water-resistance of the resulting foamed plastic.
Inventors
- 👤 Viktor Alexeevich Novak
- 👤 Jury Semenovich Murashov
- 👤 Vasily Dmitrievich Valgin
- 👤 Vsevolod Vasilievich Baranov
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-01 09:12
CPC Classifications
C; C08; C08J; C08J9/00; C08J9/04; C08J9/12; C08J9/14; C08G; C08G8/00; C08G8/28; C08J2361/00; C08J2361/04; C08J2361/06; C08J2361/14
Claims Analysis
Total Claims: 9
Claim 1
Independent Claim
139 words
A method of preparing phenolaldehyde foamed plastics having low water-absorbing properties comprising mixing a phenolaldehyde oligomer consisting of 100-15 parts by weight of a resol resin and 0-85 parts by weight of a novolac resin, with an acidic catalyst selected consisting essentially of (A) an oligomeric product obtained by the treatment of an aromatic sulphoacid with formaldehyde, or (B) an oligomeric product obtained by the treatment of an aromatic sulphoacid with formaldehyde and a nitrogen-containing compound selected from the group consisting of an amine and an amide, a complex-forming metal selected from the group consisting of cobalt, magnesium, manganese, vanadium, chromium, nickel, copper, iron, titanium, and lead and in the form of its oxide, hydroxide, salt, or mixtures thereof, a surfactant and a foaming agent, and then foaming and curing the mixture at a temperature up to 100° C.
Claim 2
Independent Claim
139 words
A method of preparing phenolaldehyde foamed plastics having low water-absorbing properties comprising mixing a phenolaldehyde oligomer consisting of 100-15 parts by weight of a resol resin and 0-85 parts by weight of a novolac resin, with an acidic catalyst selected consisting essentially of (A) an oligomeric product obtained by the treatment of an aromatic sulphoacid with formaldehyde, or (B) an oligomeric product obtained by the treatment of an aromatic sulphoacid with formaldehyde and a nitrogen-containing compound selected from the group consisting of an amine and an amide, a complex-forming metal selected from the group consisting of cobalt, magnesium, manganese, vanadium, chromium, nickel, copper, iron, titanium, and lead and in the form of its oxide, hydroxide, salt, or mixtures thereof, a surfactant and a foaming agent, and then foaming and curing the mixture at a temperature up to 100° C.
Claim 3
Dependent Claim
27 words
A method as claimed in claim 1, wherein said complex-forming metal is used in an amount ranging from 5 to 100% by weight of said acidic catalyst.
Claim 4
Dependent Claim
27 words
A method as claimed in claim 1, wherein said complex-forming metal is used in an amount ranging from 20 to 60% by weight of said acidic catalyst.
Claim 5
Dependent Claim
58 words
A method as claimed in claim 1, wherein said mixture contains 100 parts by weight of phenolaldehyde oligomer, 1 to 30 parts by weight of said foaming agent, 0.5 to 5 parts by weight of said surfactant, 10 to 50 parts by weight of an acidic catalyst and 0.5 to 50 parts by weight of said complex-forming metal.
Claim 6
Dependent Claim
156 words
A composition for producing a phenolaldehyde foamed plastic having low water-absorbing properties comprising 100 parts by weight of a phenolaldehyde oligomer consisting of 100-15 parts by weight of a resol resin and 0-85 parts by weight of a novolac resin, 1 to 30 parts by weight of a foaming agent, 0.5 parts to 5 parts by weight of a surfactant, 10 to 50 parts by weight of an acidic catalyst selected consisting essentially of (A) an oligomeric product obtained by the treatment of an aromatic sulphoacid with formaldehyde or (B) an oligomeric product obtained by treatment of an aromatic sulphoacid with formaldehyde and a nitrogen-containing compound selected from the group consisting of an amine and an amide, and 0.5 to 50 parts by weight of a complex-forming metal selected from the group consisting of cobalt, magnesium, manganese, vanadium, chromium, nickel, copper, iron, titanium and lead in the form of its oxide, hydroxide, salt, or mixtures thereof.
Claim 7
Dependent Claim
156 words
A composition for producing a phenolaldehyde foamed plastic having low water-absorbing properties comprising 100 parts by weight of a phenolaldehyde oligomer consisting of 100-15 parts by weight of a resol resin and 0-85 parts by weight of a novolac resin, 1 to 30 parts by weight of a foaming agent, 0.5 parts to 5 parts by weight of a surfactant, 10 to 50 parts by weight of an acidic catalyst selected consisting essentially of (A) an oligomeric product obtained by the treatment of an aromatic sulphoacid with formaldehyde or (B) an oligomeric product obtained by treatment of an aromatic sulphoacid with formaldehyde and a nitrogen-containing compound selected from the group consisting of an amine and an amide, and 0.5 to 50 parts by weight of a complex-forming metal selected from the group consisting of cobalt, magnesium, manganese, vanadium, chromium, nickel, copper, iron, titanium and lead in the form of its oxide, hydroxide, salt, or mixtures thereof.
Claim 8
Dependent Claim
20 words
The process of claim 1 wherein the nitrogen-containing compound is selected from the group consisting of urea, aniline, and 4,4'-diaminodiphenolmethane.
Claim 9
Dependent Claim
20 words
The composition of claim 5 wherein the nitrogen-containing compound is selected from the group consisting of urea, aniline, and 4,4'-diaminodiphenolmethane.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1979-12-21 | 1980-06-21 | 1980-12-21 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1983-12-21 | 1984-06-21 | 1984-12-21 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1987-12-21 | 1988-06-21 | 1988-12-21 | $7700.00 | Window Closed / Lapsed |