Abstract
Abstract A heat treated cast iron wherein the carbon and silicon contents are controlled to produce a white iron as cast in a sand mold and the sulfur content is in excess of that required to combine with all the manganese in the iron. The iron is annealed to produce temper carbon and a ferrous matrix containing a uniform distribution of iron sulfide particles of finite size.
Inventors
- 👤 Franklin B. Rote
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-31 19:35
CPC Classifications
C; C22; C22C; C22C37/00; B; B22; B22D; B22D27/00; Y; Y10; Y10S; Y10S148/00; Y10S148/902
Claims Analysis
Total Claims: 12
Claim 1
Independent Claim
250 words
The method of producing a wear and abrasion resistant iron casting which comprises, melting an iron alloy consisting essentially of 2.5 to 3.10% carbon, 1.40 to 2.00% silicon, manganese, sulfur in an amount equal to about 0.02 to 0.4% in excess of that required to combine with all the manganese in the alloy and the balance iron, the carbon and silicon contents being selected to produce a carbon equivalent of 3.00 to 3.60%, the carbon equivalent being between 3.00 and 3.30 when the sulfur in excess of that required to combine with all the manganese is below 0.05%; casting said alloy in a sand mold to produce a white iron casting having a microstructure characterized by substantially all of the carbon being in the combined form and appearing as discrete particles of an iron sulfide-iron carbide complex in a pearlitic matrix; annealing the casting for a period of 2 to 20 hours at a temperatutre of between 1650° to 1850° F. to graphitize the iron and at least partially break down the iron sulfide-iron carbide particles; causing the iron sulfide particles so formed to grow in size by furnace cooling the casting down to a temperature of about 1500° to 1600° F. and subsequently cooling the casting to room temperature at a more rapid rate to produce a microstructure having a pearlitic or martensitic matrix containing graphite in the form of temper carbon and discrete particles of iron sulfide of generally rounded shape visible at a magnification of 100 diameters.
Claim 2
Independent Claim
250 words
The method of producing a wear and abrasion resistant iron casting which comprises, melting an iron alloy consisting essentially of 2.5 to 3.10% carbon, 1.40 to 2.00% silicon, manganese, sulfur in an amount equal to about 0.02 to 0.4% in excess of that required to combine with all the manganese in the alloy and the balance iron, the carbon and silicon contents being selected to produce a carbon equivalent of 3.00 to 3.60%, the carbon equivalent being between 3.00 and 3.30 when the sulfur in excess of that required to combine with all the manganese is below 0.05%; casting said alloy in a sand mold to produce a white iron casting having a microstructure characterized by substantially all of the carbon being in the combined form and appearing as discrete particles of an iron sulfide-iron carbide complex in a pearlitic matrix; annealing the casting for a period of 2 to 20 hours at a temperatutre of between 1650° to 1850° F. to graphitize the iron and at least partially break down the iron sulfide-iron carbide particles; causing the iron sulfide particles so formed to grow in size by furnace cooling the casting down to a temperature of about 1500° to 1600° F. and subsequently cooling the casting to room temperature at a more rapid rate to produce a microstructure having a pearlitic or martensitic matrix containing graphite in the form of temper carbon and discrete particles of iron sulfide of generally rounded shape visible at a magnification of 100 diameters.
Claim 3
Dependent Claim
36 words
The method called for in claim 1 wherein the carbon equivalent of the alloy is above 3.30% only when the free sulfur content exceeds 0.05% and approaches 3.60% only as the free sulfur content approaches 0.40%.
Claim 4
Dependent Claim
44 words
The method called for in claim 1 wherein the time and temperature of annealing is selected to retain in the microstructure of the finished casting particles of said iron sulfide-iron carbide complex in the matrix in addition to said discrete particles of iron sulfide.
Claim 5
Dependent Claim
25 words
The method called for in claim 1 wherein said step of more rapid cooling comprises cooling the casting in air to produce a pearlitic matrix.
Claim 6
Dependent Claim
25 words
The method called for in claim 1 wherein said step of more rapid cooling comprises quenching the casting in oil to produce a martensitic matrix.
Claim 7
Dependent Claim
66 words
The method called for in claim 1 wherein the casting comprises a camshaft and said step of more rapid cooling to room temperature is controlled to produce a pearlitic matrix and thereafter the cam surface portions of the camshaft are subjected to a surface heat treatment at a temperature below the annealing temperature to produce a martensitic structure on said cam surface portions of the casting.
Claim 8
Dependent Claim
128 words
A wear and abrasion resistant heat treated iron casting consisting essentially of 2.5 to 3.10% carbon, 1.40 to 2.00% silicon, manganese, sulfur in an amount equal to about 0.02 to 0.4% in excess of that required to combine with all the manganese in the iron and the balance iron, the metal having a carbon equivalent of 3.0 to 3.60% and having a carbon equivalent of 3.00 to 3.30 when the sulfur in excess of that required to combine with all the manganese is below about 0.05%, said casting having an annealed microstructure of a pearlitic or martensitic matrix containing particles of graphite in the form of temper carbon and a dispersion of discrete particles of iron sulfide of generally rounded shape visible at a magnification of 100 diameters.
Claim 9
Dependent Claim
128 words
A wear and abrasion resistant heat treated iron casting consisting essentially of 2.5 to 3.10% carbon, 1.40 to 2.00% silicon, manganese, sulfur in an amount equal to about 0.02 to 0.4% in excess of that required to combine with all the manganese in the iron and the balance iron, the metal having a carbon equivalent of 3.0 to 3.60% and having a carbon equivalent of 3.00 to 3.30 when the sulfur in excess of that required to combine with all the manganese is below about 0.05%, said casting having an annealed microstructure of a pearlitic or martensitic matrix containing particles of graphite in the form of temper carbon and a dispersion of discrete particles of iron sulfide of generally rounded shape visible at a magnification of 100 diameters.
Claim 10
Dependent Claim
31 words
An iron casting as called for in claim 7 wherein there is also dispersed in said matrix particles of iron sulfide-iron carbide complex of larger size than said iron sulfide particles.
Claim 11
Dependent Claim
20 words
An iron casting as called for in claim 7 wherein the casting is a camshaft for an internal combustion engine.
Claim 12
Dependent Claim
32 words
An iron casting as called for in claim 9 wherein the cam surface portions of the camshaft have a martensitic matrix and the internal sections of the camshaft have a pearlitic matrix.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1979-12-21 | 1980-06-21 | 1980-12-21 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1983-12-21 | 1984-06-21 | 1984-12-21 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1987-12-21 | 1988-06-21 | 1988-12-21 | $7700.00 | Window Closed / Lapsed |