Alloy and method for producing the same
Assignee: Individual
•
Filing: 1975-07-10
•
Granted: 1976-12-21
•
Expires: 1995-07-10
Abstract
Abstract An alloy having the appearance and many desirable characteristics of gold; the alloy comprising copper, aluminum and indium; the disclosure also including methods for producing said alloy as well as various finishing treatments of castings produced from said alloy.
Inventors
- 👤 William A. Rhodes
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-24 01:35
CPC Classifications
B; B22; B22C; B22C9/00; B22C9/02; B22C9/04; B22D; B22D25/00; B22D25/02; B22D25/026; C; C22; C22C; C22C9/00; C22C9/01
Claims Analysis
Total Claims: 6
Claim 1
Independent Claim
51 words
An alloy comprising: copper, aluminum and Indium; the aluminum ranging between 0.5% to 7.5% by weight of the alloy and the Indium ranging between 1% and 5% by weight of the alloy; and the copper ranging in an amount to equal the remaining percentage by weight of the alloy weighing 100%.
Claim 2
Dependent Claim
51 words
An alloy comprising: copper, aluminum and Indium; the aluminum ranging between 0.5% to 7.5% by weight of the alloy and the Indium ranging between 1% and 5% by weight of the alloy; and the copper ranging in an amount to equal the remaining percentage by weight of the alloy weighing 100%.
Claim 3
Dependent Claim
78 words
An alloy method comprising: the alloying of copper, aluminum and Indium comprising aluminum ranging between 0.5% to 7.5% by weight of the alloy and the Indium ranging between 1% and 5% by weight of the alloy and the copper ranging in an amount equal to the remaining percentage by weight of the alloy weighing 100%; wherein the method comprises first heating the copper to a molten state and adding the Indium and the aluminum to the molten copper.
Claim 4
Dependent Claim
78 words
An alloy method comprising: the alloying of copper, aluminum and Indium comprising aluminum ranging between 0.5% to 7.5% by weight of the alloy and the Indium ranging between 1% and 5% by weight of the alloy and the copper ranging in an amount equal to the remaining percentage by weight of the alloy weighing 100%; wherein the method comprises first heating the copper to a molten state and adding the Indium and the aluminum to the molten copper.
Claim 5
Dependent Claim
48 words
The invention as defined in claim 2, wherein: phosphorus rich copper is first added to the molten copper then Indium is added to the molten copper and then aluminum is added to the copper and Indium melt until the aluminum is melted into the molten copper and Indium.
Claim 6
Dependent Claim
42 words
The invention as defined in claim 3, wherein: the Indium is first added to the melt and then the phosphorus rich copper is added to the melt and thereafter causes a deoxidizing action in the melt for substantially thirty seconds or more.
References Cited (Backward Citations)
US1960740A
Cited
US3091527A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1979-12-21 | 1980-06-21 | 1980-12-21 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1983-12-21 | 1984-06-21 | 1984-12-21 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1987-12-21 | 1988-06-21 | 1988-12-21 | $7700.00 | Window Closed / Lapsed |