Conversion of waste rubber to fuel and other useful products
Assignee: Tennessee Valley Authority
•
Filing: 1975-01-31
•
Granted: 1976-12-07
•
Expires: 1995-01-31
Abstract
Abstract Heretofore waste rubber, a substantial amount of it in the form of used automobile tires, has been buried, burned, or otherwise disposed of in manners and by means totally inconsistent with good ecological practices and considerations. Now, such waste or scrap rubber, both natural and synthetic, can readily be converted in the presence of molten acidic halide Lewis salt catalysts to useful products, including fuels comprising a naptha-like oil, a burnable solid carbonaceous material, and a mixture of gases. The most promising salts are zinc chloride, tin chloride, and antimony iodide. Also, an extremely active catalyst can be prepared by adding up to about 60 percent by weight of sodium chloride to the zinc chloride catalyst. The burnable carbonaceous material has been shown to be a carbon black of moderate quality and is believed to be suitable for reuse in tires if blended with high-quality fresh carbon black.
Inventors
- 👤 John W. Larsen
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-03 11:01
CPC Classifications
C; C10; C10G; C10G1/00; C10G1/10; C09; C09C; C09C1/00; C09C1/44; C09C1/48; C09C1/482; C10B; C10B49/00; C10B49/14; C10B53/00; C10B53/07; C01; C01P; C01P2006/00; C01P2006/80; Y; Y02; Y02P; Y02P20/00; Y02P20/141; Y02P20/143
Claims Analysis
Total Claims: 8
Claim 1
Independent Claim
169 words
A process for converting waste solid rubber scrap including used vehicle tires and the like to useful liquid, solid, and gaseous chemicals which consists essentially of: a. heating at substantially atmospheric pressure a molten acidic halide Lewis salt selected from the group consisting of zinc chloride, tin chloride, antimony iodide, and mixtures thereof, to a temperature range from about 300° C to the respective boiling point of said salt, thereby converting same to a molten state; b. introducing into said heated molten salt solid waste rubber material for a predetermined time; c. removing from above the surface of said molten salt the resulting distilled gaseous and liquid products; d. removing from the surface of said molten salt at least a portion of the resulting carbonaceous residue formed thereon together with at least a portion of said molten salt to separating means wherefrom is recovered as a solid product, said solid carbonaceous material, and wherefrom is recycled back to said molten salt substantially all of the salt material removed therefrom.
Claim 2
Dependent Claim
169 words
A process for converting waste solid rubber scrap including used vehicle tires and the like to useful liquid, solid, and gaseous chemicals which consists essentially of: a. heating at substantially atmospheric pressure a molten acidic halide Lewis salt selected from the group consisting of zinc chloride, tin chloride, antimony iodide, and mixtures thereof, to a temperature range from about 300° C to the respective boiling point of said salt, thereby converting same to a molten state; b. introducing into said heated molten salt solid waste rubber material for a predetermined time; c. removing from above the surface of said molten salt the resulting distilled gaseous and liquid products; d. removing from the surface of said molten salt at least a portion of the resulting carbonaceous residue formed thereon together with at least a portion of said molten salt to separating means wherefrom is recovered as a solid product, said solid carbonaceous material, and wherefrom is recycled back to said molten salt substantially all of the salt material removed therefrom.
Claim 3
Dependent Claim
12 words
The process of claim 1 wherein said molten salt is zinc chloride.
Claim 4
Dependent Claim
12 words
The process of claim 1 wherein the molten salt is tin chloride.
Claim 5
Dependent Claim
12 words
The process of claim 1 wherein the molten salt is antimony iodide.
Claim 6
Dependent Claim
16 words
The process of claim 1 wherein the temperature ranges from about 300° to about 500° C.
Claim 7
Dependent Claim
28 words
The process of claim 1 wherein the residence time of said waste rubber material in contact with said molten salt ranges from about 1 to about 90 minutes.
Claim 8
Dependent Claim
17 words
The process of claim 6 wherein said residence time ranges from about 1 to about 15 minutes.
References Cited (Backward Citations)
US2567802A
Cited
US2610925A
Cited
US2701268A
Cited
US3704108A
Cited
US3736250A
Cited
US3790469A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1979-12-07 | 1980-06-07 | 1980-12-07 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1983-12-07 | 1984-06-07 | 1984-12-07 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1987-12-07 | 1988-06-07 | 1988-12-07 | $7700.00 | Window Closed / Lapsed |