US3993590A
Expired / Lapsed
US
⏱️ 0.0 years remaining
Process for preparing spheroidal silico-alumina particles
Assignee: Labofina SA
•
Filing: 1975-02-10
•
Granted: 1976-11-23
•
Expires: 1995-02-10
Abstract
Abstract A process for preparing silico-alumina beads containing silica and at least an equal amount of alumina comprising dispersing as droplets into a hot and practically water-immiscible fluid, an aqueous mixture which comprises alumina hydrogel, alumina hydrosol as alumina precursors, an alkali silicate and silica gel as silica precursors, the amount of alkali silicate, based on SiO 2 , not exceeding 20% of the total weight of SiO 2 and Al 2 O 3 , and the total amount of alkali silica and silica gel, based on SiO 2 , not exceeding 50% of the total weight of SiO 2 and Al 2 O 3 , and at least a water-soluble monomer whose uncross-linked polymer is water-soluble or forms a gel, and maintaining the droplets of the aqueous mixture in the hot fluid until substantial polymerization of said monomer occurs.
Inventors
- 👤 Jacques Maurice Jules Ghislain Andre
- 👤 Raymond Marc Cahen
- 👤 Henri Robert Debus
- 👤 Rene Odon Lammers
- 👤 Hugo Johannes VAN Thillo
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-04 09:38
CPC Classifications
C; C01; C01F; C01F7/00; C01F7/48; B; B01; B01J; B01J2/00; B01J2/28; B01J21/00; B01J21/12; B01J37/00; B01J37/0072; B01J35/00; B01J35/50; B01J35/51
Claims Analysis
Total Claims: 13
Claim 1
Independent Claim
226 words
A process for preparing silica-alumina beads containing silica and at least an equal amount of alumina comprising dispersing as droplets into a hot and practically water-immiscible fluid, an aqueous mixture which comprises finely divided alumina hydrogel, alumina hydrosol as alumina precursors, the weight ratio of said hydrogel to said hydrosol being between 99:1 and 50:50, an alkali silicate and silica gel as silica precursors, the amount of alkali silicate, based on SiO 2 , not exceeding 20% of the total weight of SiO 2 and Al 2 O 3 , and the total amount of alkali silicate and silica gel, based on SiO 2 , not exceeding 50% of the total weight of SiO 2 and Al 2 O 3 and a water-soluble monomer whose cross-linked polymer is water soluble or forms a gel, said monomer being an acrylic compound of the general formula ##EQU1## wherein R 1 is H or the methylradical and R 2 is a -- OR 3 or --NR 3 R 4 radical with R 3 and R 4 in such radical being H or a hydrophilic radical, the amount of said monomer being between 5% and 100% of the weight of alumina dnd silica precursors, based on their oxides, and maintaining the droplets of the aqueous mixture in the hot fluid under polymerization conditions until substantial polymerization of said monomer occurs.
Claim 2
Dependent Claim
226 words
A process for preparing silica-alumina beads containing silica and at least an equal amount of alumina comprising dispersing as droplets into a hot and practically water-immiscible fluid, an aqueous mixture which comprises finely divided alumina hydrogel, alumina hydrosol as alumina precursors, the weight ratio of said hydrogel to said hydrosol being between 99:1 and 50:50, an alkali silicate and silica gel as silica precursors, the amount of alkali silicate, based on SiO 2 , not exceeding 20% of the total weight of SiO 2 and Al 2 O 3 , and the total amount of alkali silicate and silica gel, based on SiO 2 , not exceeding 50% of the total weight of SiO 2 and Al 2 O 3 and a water-soluble monomer whose cross-linked polymer is water soluble or forms a gel, said monomer being an acrylic compound of the general formula ##EQU1## wherein R 1 is H or the methylradical and R 2 is a -- OR 3 or --NR 3 R 4 radical with R 3 and R 4 in such radical being H or a hydrophilic radical, the amount of said monomer being between 5% and 100% of the weight of alumina dnd silica precursors, based on their oxides, and maintaining the droplets of the aqueous mixture in the hot fluid under polymerization conditions until substantial polymerization of said monomer occurs.
Claim 3
Dependent Claim
164 words
The process of claim 1 wherein an aqueous mixture is prepared comprising alumina hydrogel and hydrosol as Al 2 O 3 precursors, an alkali silicate and silica gel as SiO 2 precursors, the amount of alkali silicate, based on SiO 2 , not exceeding 20% of the total weight of SiO 2 and Al 2 O 3 , and the total amount of alkali silicate and silica and silica gel, based on SiO 2 , not exceeding 50% of the total weight of SiO 2 and Al 2 O 3 silica and alumina generators, and a water-soluble monomer whose uncross-linked polymer is water-soluble or forms a gel, said aqueous mixture is dispersed as droplets into a hot and substantially water-immiscible fluid, under polymerization conditions such as to bring about substantial polymerization of the monomer contained in each droplet of aqueous mixture, said beads are recovered and thereafter dried and calcined to obtain silico-alumina beads containing silica and at least an equal amount of alumina.
Claim 4
Dependent Claim
18 words
The process of claim 1, wherein the weight ratio is between 85 : 15 and 55 : 45.
Claim 5
Dependent Claim
18 words
The process of claim 1 wherein the aqueous mixture has a pH of between about 3 and 4.
Claim 6
Dependent Claim
19 words
The process of claim 1 wherein said aqueous mixture contains a cross-linking agent which can react with said monomers.
Claim 7
Dependent Claim
14 words
The process of claim 1 wherein silica gel is used in an undried form.
Claim 8
Dependent Claim
35 words
The process of claim 1 wherein the polymerization of the aqueous mixture is carried out by dispersing the aqueous mixture as droplets and passing these droplets to a counter-current flow of a hot dry gas.
Claim 9
Dependent Claim
50 words
The process of claim 1 wherein the polymerization of the aqueous mixture is carried out by dispersing the aqueous mixture as droplets at the bottom of a column containing a liquid having a density higher than that of the beads, and recovering the beads at the surface of the liquid.
Claim 10
Dependent Claim
50 words
The process of claim 1 wherein the polymerization of the aqueous mixture is carried out by dispersing the aqueous mixture as droplets at the head of a column containing a liquid having a density lower than that of the beads, and recovering the bead at the bottom of the column.
Claim 11
Dependent Claim
32 words
The process of claim 1 wherein said beads are impregnated with one or more active catalytic agents or compounds which generate active catalytic agents upon subsequent thermal treatment of the impregnated beads.
Claim 12
Dependent Claim
9 words
Silico-alumina beads prepared by the process of claim 1.
Claim 13
Dependent Claim
9 words
Catalyst compositions prepared by the process of claim 10.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1979-11-23 | 1980-05-24 | 1980-11-23 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1983-11-23 | 1984-05-24 | 1984-11-23 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1987-11-23 | 1988-05-24 | 1988-11-23 | $7700.00 | Window Closed / Lapsed |