Method of encapsulating solid radioactive waste material for storage
Assignee: Energy Research and Development Administration ERDA
•
Filing: 1975-10-22
•
Granted: 1976-11-23
•
Expires: 1995-10-22
Abstract
Abstract High-level radioactive wastes are encapsulated in vitreous carbon for long-term storage by mixing the wastes as finely divided solids with a suitable resin, formed into an appropriate shape and cured. The cured resin is carbonized by heating under a vacuum to form vitreous carbon. The vitreous carbon shapes may be further protected for storage by encasement in a canister containing a low melting temperature matrix material such as aluminum to increase impact resistance and improve heat dissipation.
Inventors
- 👤 Lee Roy Bunnell
- 👤 J. Lambert Bates
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-02 10:38
CPC Classifications
G; G21; G21F; G21F9/00; G21F9/28; G21F9/30; G21F9/301; G21F9/302
Claims Analysis
Total Claims: 9
Claim 1
Independent Claim
123 words
A method of preparing solid high-level radioactive waste material for storage by encapsulating the material in vitreous carbon comprising: mixing powdered high-level radioactive material less 325 mesh with a curable resinous material selected from the group consisting of polyfurfuryl alcohol and phenolformaldehyde to form a resinous mixture containing up to 70 weight percent waste material; forming the resinous mixture into appropriate shapes for storage; curing the shaped resinous mixture; and heating the cured shapes to from 600° to 1000° C. under a vacuum or inert atmosphere at a rate of about 6° C. per hour for a period of time sufficient to carbonize the cured resinous material to vitreous carbon, thereby forming shapes of high-level radioactive material encapsulated in vitreous carbon for storage.
Claim 2
Independent Claim
123 words
A method of preparing solid high-level radioactive waste material for storage by encapsulating the material in vitreous carbon comprising: mixing powdered high-level radioactive material less 325 mesh with a curable resinous material selected from the group consisting of polyfurfuryl alcohol and phenolformaldehyde to form a resinous mixture containing up to 70 weight percent waste material; forming the resinous mixture into appropriate shapes for storage; curing the shaped resinous mixture; and heating the cured shapes to from 600° to 1000° C. under a vacuum or inert atmosphere at a rate of about 6° C. per hour for a period of time sufficient to carbonize the cured resinous material to vitreous carbon, thereby forming shapes of high-level radioactive material encapsulated in vitreous carbon for storage.
Claim 3
Dependent Claim
14 words
The method of claim 1 wherein the curable resinous material is a polyfurfuryl alcohol.
Claim 4
Dependent Claim
22 words
The method of claim 2 wherein the mixture is cured by heating the shapes for about 2 hours at about 70° C.
Claim 5
Dependent Claim
26 words
The method of claim 3 wherein the shapes into which the resinous material is formed are selected from the group consisting of rods, sheets and spheroids.
Claim 6
Dependent Claim
36 words
The method of claim 4 wherein the shape is a rod up to 1/4 inch in diameter, the rod is formed by extrusion and the resinous mixture contains up to about 70 weight percent waste material.
Claim 7
Dependent Claim
36 words
The method of claim 4 wherein the shape is a sheet up to 1/8 inch in thickness, the sheet is formed by casting and the resinous mixture contains up to about 50 weight percent waste material.
Claim 8
Dependent Claim
42 words
The method of claim 4 wherein the shape is spheroidal, the spheroids are formed and cured by injecting the resinous mixture dropwise into agitated vegetable oil at 100° C. and the resinous mixture contains up to about 50 weight percent waste material.
Claim 9
Dependent Claim
58 words
The method of claim 4 including the additional steps of: placing a plurality of vitreous carbon shapes into a metal canister in a regular spaced array, and filling the canister including the interstices between the carbon shapes with molten aluminum and permitting the aluminum to harden, thereby providing additional protection to the encapsulated high-level waste for long-term storage.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1979-11-23 | 1980-05-24 | 1980-11-23 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1983-11-23 | 1984-05-24 | 1984-11-23 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1987-11-23 | 1988-05-24 | 1988-11-23 | $7700.00 | Window Closed / Lapsed |