Glass-epoxy laminates for high temperature use
Assignee: Westinghouse Electric Corp
•
Filing: 1975-04-24
•
Granted: 1976-11-02
•
Expires: 1995-04-24
Abstract
Abstract A laminate is made comprising a plurality of bonded layers of sheet material impregnated with a cured resinous composition, comprising a cured dispersion of an epoxy resin, NADIC methyl anhydride and benzophenonetetracarboxylic dianhydride.
Inventors
- 👤 Zal N. Sanjana
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-25 09:14
CPC Classifications
B; B29; B29C; B29C70/00; B29C70/003; B32; B32B; B32B5/00; B32B5/22; B32B5/24; B32B5/26; C; C08; C08G; C08G59/00; C08G59/18; C08G59/40; C08G59/42; C08G59/4223; B29K; B29K2309/00; B29K2309/08; B32B2260/00; B32B2260/02; B32B2260/021; B32B2260/023; B32B2260/04; B32B2260/046; B32B2262/00; B32B2262/10; B32B2262/101; B32B2307/00; B32B2307/50; B32B2307/546; Y; Y10; Y10T; Y10T428/00; Y10T428/31504; Y10T428/31511; Y10T428/31515; Y10T428/31518; Y10T428/31525
Claims Analysis
Total Claims: 7
Claim 1
Independent Claim
223 words
A method of making a laminate comprising at least one layer of sheet material containing a cured resin comprising the steps of: 1. admixing at a temperature of up to about 50° C: A. a mixture consisting essentially of: a. liquid epoxy resin, selected from the group consisting of a diglycidyl ether of bisphenol A having a viscosity range of about 2,500 cps. to about 20,000 cps. at 25° C and polyglycidyl ethers of a novolac having a viscosity range of about 1,500 cps. to about 20,000 cps. at 52° C to 55° C and mixtures thereof, and b. liquid NADIC methyl anhydride, with B. solid benzophenone-tetracarboxylic dianhydride, wherein the total anhydride plus dianhydride content is within the range of from about 0.60 to about 0.95 anhydride equivalents for each epoxy equivalent and the anhydride equivalent weight ratio of NADIC methyl anhydride: benzophenone-tetracarboxylic dianhydride is from about 0.50 to 0.90:1, to provide a homogeneous, stable dispersion of the solid dianhydride particles in the liquid without gellation, the dispersion containing about 98 percent to about 100 percent undissolved benzophenone-tetracarboxylic dianhydride; 2. adding organic solvent to the dispersion to give a solvent solution, 3. applying the solvent solution of the resinous admixture to a sheet material to coat or impregnate the material, and 4. curing the resin, to provide sheet material containing a solid resin.
Claim 2
Independent Claim
223 words
A method of making a laminate comprising at least one layer of sheet material containing a cured resin comprising the steps of: 1. admixing at a temperature of up to about 50° C: A. a mixture consisting essentially of: a. liquid epoxy resin, selected from the group consisting of a diglycidyl ether of bisphenol A having a viscosity range of about 2,500 cps. to about 20,000 cps. at 25° C and polyglycidyl ethers of a novolac having a viscosity range of about 1,500 cps. to about 20,000 cps. at 52° C to 55° C and mixtures thereof, and b. liquid NADIC methyl anhydride, with B. solid benzophenone-tetracarboxylic dianhydride, wherein the total anhydride plus dianhydride content is within the range of from about 0.60 to about 0.95 anhydride equivalents for each epoxy equivalent and the anhydride equivalent weight ratio of NADIC methyl anhydride: benzophenone-tetracarboxylic dianhydride is from about 0.50 to 0.90:1, to provide a homogeneous, stable dispersion of the solid dianhydride particles in the liquid without gellation, the dispersion containing about 98 percent to about 100 percent undissolved benzophenone-tetracarboxylic dianhydride; 2. adding organic solvent to the dispersion to give a solvent solution, 3. applying the solvent solution of the resinous admixture to a sheet material to coat or impregnate the material, and 4. curing the resin, to provide sheet material containing a solid resin.
Claim 3
Dependent Claim
46 words
The method of claim 10 wherein the cured resin constitutes about 20 to 40 weight percent of the laminate, the benzophenone-tetracarboxylic dianhydride has an average particle size of between about 20 to 150 microns and is shear mixed with the epoxy resin and NADIC methyl anhydride.
Claim 4
Dependent Claim
69 words
The method of claim 1 wherein an effective amount of catalyst is added between step (1) and step (3), the solvent is selected from the group consisting of acetone, benzene, toluene, naphtha, xylene and mixtures thereof, the solvent solution has a viscosity between about 500 to 2,000 cps. at 25° C, wherein admixing (A) and (B) in step (1) is at a temperature between about 20° to 50° C.
Claim 5
Dependent Claim
26 words
The method of claim 1 wherein the resin is cured by applying heat and pressure to the sheet material containing the solvent solution of the resin.
Claim 6
Dependent Claim
49 words
The method of claim 4, wherein a plurality of layers of sheet material containing applied solvent solution of the resinous admixture are stacked to give a laminate build up, and then heat and pressure consolidated to cure the resin to a thermoset state and provide a unitary, bonded laminate.
Claim 7
Dependent Claim
18 words
The method of claim 5 wherein the laminate is consolidated at a temperature of between about 170°-185° C.
References Cited (Backward Citations)
US2744845A
Cited
US2965610A
Cited
US3071496A
Cited
US3212958A
Cited
US3271230A
Cited
US3388185A
Cited
US3557246A
Cited
US3732332A
Cited
US3794555A
Cited
US3914512A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1979-11-02 | 1980-05-03 | 1980-11-02 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1983-11-02 | 1984-05-03 | 1984-11-02 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1987-11-02 | 1988-05-03 | 1988-11-02 | $7700.00 | Window Closed / Lapsed |