Method of making a heat-recoverable article
Assignee: Fulmer Research Institute Ltd
•
Filing: 1974-09-30
•
Granted: 1976-11-02
•
Expires: 1994-09-30
Abstract
Abstract A method of making a heat-recoverable article which comprises cooling an article in a first shape from a first temperature to a lower temperature, said article being formed from an alloy comprising at least one phase in the form of a primary solid solution of a first metal with at least one other metallic element which increases the stability of a high temperature phase of the first metal, which solution on cooling from said first temperature retains the high temperature phase but which transforms into an essentially banded martensite phase on cold working and then plastically deforming the article into a second shape, the temperature and rate of cooling being such that, on reheating, the article at least partly resumes said first shape.
Inventors
- 👤 Greville B. Brook
- 👤 Roger F. Iles
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-24 10:59
CPC Classifications
C; C22; C22C; C22C5/00; C22C5/02; C22C5/04; C22C5/06; C22C5/10; C22C9/00; C22C9/01; C22C9/04; C22C9/05
Claims Analysis
Total Claims: 8
Claim 1
Independent Claim
152 words
A method of making a heat-recoverable article which comprises cooling an article in a first shape from a first temperature to a lower temperature, said article being formed from an alloy comprising at least one phase in the form of a primary solid solution of a first metal with at least one other metallic element which increases the stability of a high temperature phase of the first metal, which solution on cooling from said first temperature retains the high temperature phase but which transforms into an essentially banded martensite phase on cold working, and then deforming the article into a second shape by cold working, the temperatures and rate of cooling being such that, on reheating, the article at least partly resumes said first shape, said alloy comprising Fe-Mn, Fe-Mn-Co, Fe-Ni-Cr-Co, Fe-Mn-Cr-Co, Fe-Mn-Cr-Ni-Co, or another ternary or quaternary alloy containing Fe and at least one of the elements Mn, Ni and Cr.
Claim 2
Independent Claim
152 words
A method of making a heat-recoverable article which comprises cooling an article in a first shape from a first temperature to a lower temperature, said article being formed from an alloy comprising at least one phase in the form of a primary solid solution of a first metal with at least one other metallic element which increases the stability of a high temperature phase of the first metal, which solution on cooling from said first temperature retains the high temperature phase but which transforms into an essentially banded martensite phase on cold working, and then deforming the article into a second shape by cold working, the temperatures and rate of cooling being such that, on reheating, the article at least partly resumes said first shape, said alloy comprising Fe-Mn, Fe-Mn-Co, Fe-Ni-Cr-Co, Fe-Mn-Cr-Co, Fe-Mn-Cr-Ni-Co, or another ternary or quaternary alloy containing Fe and at least one of the elements Mn, Ni and Cr.
Claim 3
Dependent Claim
37 words
The method of claim 1 wherein said alloy contains up to about 2% copper, up to about 2% aluminum, up to about 5% molybdenum, up to about 4% titanium, up to about 1.5% niobium, or mixtures thereof.
Claim 4
Dependent Claim
12 words
The method of claim 1 wherein said cooling is effected by quenching.
Claim 5
Dependent Claim
21 words
The method of claim 1 wherein said article is cooled to a temperature above the M f temperature of said alloy.
Claim 6
Dependent Claim
21 words
The method of claim 1 wherein said article is cooled to a temperature above the M s temperature of said alloy.
Claim 7
Dependent Claim
19 words
The method of claim 1 wherein said article is deformed at above the M s temperature of said alloy.
Claim 8
Dependent Claim
19 words
The method of claim 1 wherein said article is deformed at above the M f temperature of said alloy.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1979-11-02 | 1980-05-03 | 1980-11-02 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1983-11-02 | 1984-05-03 | 1984-11-02 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1987-11-02 | 1988-05-03 | 1988-11-02 | $7700.00 | Window Closed / Lapsed |