Production of powder metallurgical parts by formation of sintered preforms in thermally degradable molds
Assignee: United States Steel Corp
•
Filing: 1975-05-08
•
Granted: 1976-11-02
•
Expires: 1995-05-08
Abstract
Abstract Metal particles are intimately mixed with at least about 1.5 wt. percent of an organic binder. The mixture is poured into a thermally degradable mold and heated to above sintering temperature to form a preform useful for hot forging. The mold provides integrity for the packed particles until the organic compounds carbonize, which in turn effect sufficient bonding until the particles actually sinter together.
Inventors
- 👤 Roger L. Rueckl
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-03 01:29
CPC Classifications
B; B22; B22F; B22F3/00; B22F3/10; B22F1/00; B22F1/10
Claims Analysis
Total Claims: 9
Claim 1
Independent Claim
230 words
A method for the production of sintered powder metal preforms, which comprises, blending an essentially dry mixture of finely divided (a) metal particles and (b) organic binder particles to obtain a uniform distribution thereof, wherein a major portion of said finely divided particles are finer than minus 6 mesh, wherein said organic binder particles are from about 1.5 to 10.0 percent of the total mixture, packing a thermally degradable mold with said blended mixture, in a protective atmosphere, heating the packed mold to a temperature within the range 1200°-2400° F for a time sufficient to achieve sintering of said metal particles, thereby forming a sintered preform with sufficient green strength for further processing, said organic binder consisting essentially of compounds, which on heating to said sintering temperature, decompose (i) to a polycyclic structure with sufficient bonding strength to maintain the integrity of the packed structure until said metal particles sinter together, (ii) at a rate which is sufficiently slow to avoid disruption of the packed structure and containing less than 1.5% sucrose, said sucrose being below that which will maintain said integrity of the packed structure; said mold, (i) being so constructed that, on heating to said sintering temperature, it will degrade only after said organic binder has decomposed to form said polycyclic structure, and (ii) being formed of a material which degrades at a temperature below said sintering temperature.
Claim 2
Independent Claim
230 words
A method for the production of sintered powder metal preforms, which comprises, blending an essentially dry mixture of finely divided (a) metal particles and (b) organic binder particles to obtain a uniform distribution thereof, wherein a major portion of said finely divided particles are finer than minus 6 mesh, wherein said organic binder particles are from about 1.5 to 10.0 percent of the total mixture, packing a thermally degradable mold with said blended mixture, in a protective atmosphere, heating the packed mold to a temperature within the range 1200°-2400° F for a time sufficient to achieve sintering of said metal particles, thereby forming a sintered preform with sufficient green strength for further processing, said organic binder consisting essentially of compounds, which on heating to said sintering temperature, decompose (i) to a polycyclic structure with sufficient bonding strength to maintain the integrity of the packed structure until said metal particles sinter together, (ii) at a rate which is sufficiently slow to avoid disruption of the packed structure and containing less than 1.5% sucrose, said sucrose being below that which will maintain said integrity of the packed structure; said mold, (i) being so constructed that, on heating to said sintering temperature, it will degrade only after said organic binder has decomposed to form said polycyclic structure, and (ii) being formed of a material which degrades at a temperature below said sintering temperature.
Claim 3
Dependent Claim
23 words
The method of claim 1, wherein the particles in said mold are packed to a bulk density substantially in excess of "apparent density".
Claim 4
Dependent Claim
53 words
The method of claim 2, wherein said metal particles are composed of a ferrous alloy with a carbon reducible oxygen content substantially in excess of 200 ppm, and said organic binder is present in an amount sufficient to reduce said oxygen and increase the carbon content by a value greater than 0.04 percent.
Claim 5
Dependent Claim
30 words
The method of claim 3, wherein said binder is employed in amounts in excess of 2.0 wt. percent, and is selected from the group consisting of carbohydrates and thermosetting resins.
Claim 6
Dependent Claim
12 words
The method of claim 4, wherein said binder contains essentially no sucrose.
Claim 7
Dependent Claim
12 words
The method of claim 5, wherein said mold material is pressed paper.
Claim 8
Dependent Claim
26 words
The method of claim 6, wherein said sintering is conducted at temperatures in excess of about 1800° F for a period of at least 10 minutes.
Claim 9
Dependent Claim
23 words
The method of claim 7, wherein the resultant sintered preform is removed from the furnace and, without appreciable cooling thereof, is then forged.
References Cited (Backward Citations)
US2386544A
Cited
US3811878A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1979-11-02 | 1980-05-03 | 1980-11-02 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1983-11-02 | 1984-05-03 | 1984-11-02 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1987-11-02 | 1988-05-03 | 1988-11-02 | $7700.00 | Window Closed / Lapsed |