Process for producing molded structural foam article having a surface that reproducibly and faithfully replicates the surface of the mold
Assignee: Union Carbide Corp
•
Filing: 1975-05-22
•
Granted: 1976-10-26
•
Expires: 1995-05-22
Abstract
Abstract A process is disclosed for producing a structural foam article having a surface that reproducibly and faithfully replicates the surface of the mold within which the article was made. The process is an improvement in the "low pressure" process for producing structural foam, wherein the improvement resides in introducing the molten mixture of foamable thermoplastic material and blowing agent into the mold under such conditions that a no-slip boundary condition is maintained at an iNterface between the flowing thermoplastic and a predetermined portion of the interior surface of the mold, and by maintaining the temperature at said interface at or above a certain temperature (termed "replication temperature"), while the thermoplastic is flowing in the mold.
Inventors
- 👤 Richard G. Angell, Jr.
- 👤 Robert J. Anderson
- 👤 Kenneth E. Hobbs
- 👤 David E. James
- 👤 B. Duane Marsh
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-27 04:53
CPC Classifications
B; B29; B29C; B29C44/00; B29C44/02; B29C44/04; B29C44/0407; B29C44/34; B29C44/36; B29C44/38; B29C44/42; B29C44/421; Y; Y10; Y10S; Y10S264/00; Y10S264/05; Y10S264/14; Y10S264/83; Y10T; Y10T428/00; Y10T428/249921; Y10T428/249953; Y10T428/249987; Y10T428/249988; Y10T428/249989; Y10T428/31
Claims Analysis
Total Claims: 20
Claim 1
Independent Claim
201 words
In a process for injection molding foamed thermoplastic articles characterized by a foamed core, a relatively non-foamed exterior shell, and a surface that reproducibly and faithfully replicates a predetermined portion of the inner surface of the mold in which the article was made, wherein a mixture comprising molten foamable thermoplastic material and blowing agent is introduced under pressure into a mold cavity defined by the inner surface of the mold, the mold cavity being maintained at a pressure below the foaming pressure of said mixture, whereby said mixture flows and expands in said mold cavity, and said thermoplastic material is rigidified while it is in said mold cavity, the improvement comprising the steps of: a. maintaining said mixture in adhesive contact with said predetermined portion of said inner surface of the mold, thereby defining a polymer/mold interface as said mixture flows within said mold cavity; b. maintaining a no-slip boundary condition between said mixture and said inner surface of the mold at said interface, as said mixture flows within said mold cavity; and c. maintaining the temperature at said interface at a temperature of at least the replication temperature of said thermoplastic material, as said mixture flows within said mold cavity.
Claim 2
Dependent Claim
201 words
In a process for injection molding foamed thermoplastic articles characterized by a foamed core, a relatively non-foamed exterior shell, and a surface that reproducibly and faithfully replicates a predetermined portion of the inner surface of the mold in which the article was made, wherein a mixture comprising molten foamable thermoplastic material and blowing agent is introduced under pressure into a mold cavity defined by the inner surface of the mold, the mold cavity being maintained at a pressure below the foaming pressure of said mixture, whereby said mixture flows and expands in said mold cavity, and said thermoplastic material is rigidified while it is in said mold cavity, the improvement comprising the steps of: a. maintaining said mixture in adhesive contact with said predetermined portion of said inner surface of the mold, thereby defining a polymer/mold interface as said mixture flows within said mold cavity; b. maintaining a no-slip boundary condition between said mixture and said inner surface of the mold at said interface, as said mixture flows within said mold cavity; and c. maintaining the temperature at said interface at a temperature of at least the replication temperature of said thermoplastic material, as said mixture flows within said mold cavity.
Claim 3
Dependent Claim
82 words
Process of claim 1 wherein said no-slip boundary condition is maintained by introducing said mixture into said mold cavity at a rate such that, as said mixture flows within said mold, the forces resulting from the shearing stresses in said mixture at said interface are (a) less than the maximum value of the static frictional force between said mixture and said predetermined portion of said inner surface of the mold, and (b) less than the melt strength of said molten thermoplastic material.
Claim 4
Dependent Claim
45 words
Process of claim 1 wherein the temperature at said interface is maintained at or above said replication temperature by maintaining the temperature of at least the portion of said mold that includes said predetermined portion of said inner surface at or above said replication temperature.
Claim 5
Dependent Claim
45 words
Process of claim 2 wherein the temperature at said interface is maintained at or above said replication temperature by maintaining the temperature of at least the portion of said mold that includes said predetermined portion of said inner surface at or above said replication temperature.
Claim 6
Dependent Claim
103 words
Process of claim 1 wherein said mold includes a body portion having a relatively high heat capacity, wherein said predetermined portion of the inner surface of said mold comprises a member having a relatively low heat capacity, wherein said body portion and said member are separated by a heat insulating layer, wherein said body portion is maintained at a temperature below said replication temperature, and wherein said mixture is at a temperature above said replication temperature when it is introduced into said mold cavity, whereby said interface is maintained at or above said replication temperature while said mixture flows in said mold cavity.
Claim 7
Dependent Claim
38 words
Process of claim 1 wherein said thermoplastic material consists essentially of at least one member of the group consisting of olefin polymer, styrene polymer, polycarbonate, polyamide, polyaryl polyhydroxy ether, polysulfone, polyester, acrylic polymer, acetal polymer and mixtures thereof.
Claim 8
Dependent Claim
35 words
Process of claim 6 wherein said thermoplastic material consists essentially of at least one member of the group consisting of polystyrene, high density polyethylene, low density polyethylene, polypropylene, acrylonitrile-butadiene-styrene terpolymer, polysulfone, polycarbonate, and mixtures thereof.
Claim 9
Dependent Claim
44 words
Process of claim 1 wherein said blowing agent is selected from the group consisting of nitrogen, carbon dioxide, pentane, a C 1 to C 4 halogenated hydrocarbon, an azo compound, an N-nitroso compound, a sulfonyl hydrazide compound, a sulfonyl semicarbazide compound, and mixtures thereof.
Claim 10
Dependent Claim
22 words
The process of claim 8 wherein said blowing agent is selected from the group consisting of nitrogen, dichlorodifluoromethane, azodicarbonamide, and mixtures thereof.
Claim 11
Dependent Claim
218 words
In a process for injection molding foamed thermoplastic articles characterized by a foamed core, a relatively non-foamed exterior shell, and a surface that reproducibly and faithfully replicates a predetermined portion of the inner surface of the mold in which the article was made, wherein a mixture comprising molten foamable thermoplastic material and blowing agent is introduced under pressure into a mold cavity defined by the inner surface of the mold, the volume of said mixture introduced into said cavity being less than the volume of said cavity, the mold cavity being maintained at a pressure below the foaming pressure of said mixture, whereby said mixture flows and expands in said mold cavity, and said thermoplastic material is rigidified while it is in said mold cavity, the improvement comprising the steps of: a. maintaining said mixture in adhesive contact with said predetermined portion of said inner surface of the mold, thereby defining a polymer/mold interface as said mixture flows within said mold cavity; b. maintaining a no-slip boundary condition between said mixture and said inner surface of the mold at said interface, as said mixture flows within said mold cavity; and c. maintaining the temperature at said interface at a temperature of at least the replication temperature of said thermoplastic material, as said mixture flows within said mold cavity.
Claim 12
Dependent Claim
218 words
In a process for injection molding foamed thermoplastic articles characterized by a foamed core, a relatively non-foamed exterior shell, and a surface that reproducibly and faithfully replicates a predetermined portion of the inner surface of the mold in which the article was made, wherein a mixture comprising molten foamable thermoplastic material and blowing agent is introduced under pressure into a mold cavity defined by the inner surface of the mold, the volume of said mixture introduced into said cavity being less than the volume of said cavity, the mold cavity being maintained at a pressure below the foaming pressure of said mixture, whereby said mixture flows and expands in said mold cavity, and said thermoplastic material is rigidified while it is in said mold cavity, the improvement comprising the steps of: a. maintaining said mixture in adhesive contact with said predetermined portion of said inner surface of the mold, thereby defining a polymer/mold interface as said mixture flows within said mold cavity; b. maintaining a no-slip boundary condition between said mixture and said inner surface of the mold at said interface, as said mixture flows within said mold cavity; and c. maintaining the temperature at said interface at a temperature of at least the replication temperature of said thermoplastic material, as said mixture flows within said mold cavity.
Claim 13
Dependent Claim
82 words
Process of claim 10 wherein said no-slip boundary condition is maintained by introducing said mixture into said mold cavity at a rate such that, as said mixture flows within said mold, the forces resulting from the shearing stresses in said mixture at said interface are (a) less than the maximum value of the static frictional force between said mixture and said predetermined portion of said inner surface of the mold, and (b) less than the melt strength of said molten thermoplastic material.
Claim 14
Dependent Claim
45 words
Process of claim 10 wherein the temperature at said interface is maintained at or above said replication temperature by maintaining the temperature of at least the portion of said mold that includes said predetermined portion of said inner surface at or above said replication temperature.
Claim 15
Dependent Claim
45 words
Process of claim 11 wherein the temperature at said interface is maintained at or above said replication temperature by maintaining the temperature of at least the portion of said mold that includes said predetermined portion of said inner surface at or above said replication temperature.
Claim 16
Dependent Claim
103 words
Process of claim 10 wherein said mold includes a body portion having a relatively high heat capacity, wherein said predetermined portion of the inner surface of said mold comprises a member having a relatively low heat capacity, wherein said body portion and said member are separated by a heat insulating layer, wherein said body portion is maintained at a temperature below said replication temperatures, and wherein said mixture is at a temperature above said replication temperature when it is introduced into said mold cavity, whereby said interface is maintained at or above said replication temperature while said mixture flows in said mold cavity.
Claim 17
Dependent Claim
38 words
Process of claim 10 wherein said thermoplastic material consists essentially of at least one member of the group consisting of olefin polymer, styrene polymer, polycarbonate, polyamide, polyaryl polyhydroxy ether, polysulfone, polyester, acrylic polymer, acetal polymer, and mixtures thereof.
Claim 18
Dependent Claim
35 words
Process of claim 15 wherein said thermoplastic material consists essentially of at least one member of the group consisting of polystyrene, high density polyethylene, low density polyethylene, polypropylene, acrylonitrile-butadiene-styrene terpolymer, polysulfone, polycarbonate, and mixtures thereof.
Claim 19
Dependent Claim
44 words
Process of claim 10 wherein said blowing agent is selected from the group consisting of nitrogen, carbon dioxide, pentane, a C 1 to C 4 halogenated hydrocarbon, an azo compound, an N-nitroso compound, a sulfonyl hydrazide compound, a sulfonyl semicarbazide compound, and mixtures thereof.
Claim 20
Dependent Claim
22 words
The process of claim 17 wherein said blowing agent is selected from the group consisting of nitrogen, dichlorodifluoromethane, azodicarbonamide, and mixtures thereof.
References Cited (Backward Citations)
US2928130A
Cited
US3162703A
Cited
US3268636A
Cited
US3382535A
Cited
US3436446A
Cited
US3531553A
Cited
US3544518A
Cited
US3773873A
Cited
US3734449A
Cited
US3671168A
Cited
US3776989A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1979-10-26 | 1980-04-26 | 1980-10-26 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1983-10-26 | 1984-04-26 | 1984-10-26 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1987-10-26 | 1988-04-26 | 1988-10-26 | $7700.00 | Window Closed / Lapsed |