Abstract
Abstract Solar cells showing improved efficiency, amounting to about 14 percent for overall solar power conversion, are obtained by annealing InP/CdS solar cells in a slightly reducing atmosphere for about 15 minutes in a temperature range preferably from about 550° centrigrade to about 600° centigrade. In an annealing temperature range from 400° centigrade to 625° centigrade, an inversely dependent adjustment of annealing time is found desirable. The atmosphere preferably comprises mainly a substantially inert component and typically comprises an H 2 + N 2 mixture, such as forming gas (15% H 2 + 85% N 2 ).
Inventors
- 👤 Klaus Jurgen Bachmann
- 👤 Ernest Buehler
- 👤 Joseph Leo Shay
- 👤 Sigurd Wagner
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-27 09:51
CPC Classifications
H; H10; H10P; H10P95/00; Y; Y10; Y10S; Y10S148/00; Y10S148/003; Y10S148/072; Y10S148/079; Y10S148/12
Claims Analysis
Total Claims: 12
Claim 1
Independent Claim
62 words
A process comprising the steps of fabricating a device having a heterojunction between semiconductive regions of InP and CdS, annealing said device for a selected time at a selected temperature in a non-oxidizing substantially inert atmosphere, said selected temperature being in the range from about 400° centigrade to about 625° centigrade, and completing connections to said device for a desired photovoltaic response.
Claim 2
Dependent Claim
62 words
A process comprising the steps of fabricating a device having a heterojunction between semiconductive regions of InP and CdS, annealing said device for a selected time at a selected temperature in a non-oxidizing substantially inert atmosphere, said selected temperature being in the range from about 400° centigrade to about 625° centigrade, and completing connections to said device for a desired photovoltaic response.
Claim 3
Dependent Claim
30 words
A process according to claim 1 in which the selected time is in the range from 10 minutes to several hours, the shorter times corresponding to the higher annealing temperatures.
Claim 4
Dependent Claim
14 words
A process according to claim 1 in which the selected time approximates 15 minutes.
Claim 5
Dependent Claim
23 words
A process according to claim 3 in which the selected temperature is in the range from about 550° centigrade to about 600° centigrade.
Claim 6
Dependent Claim
27 words
A process according to claim 1 in which the atmosphere includes a mixture of a first substantially inert component and a second component consisting essentially of hydrogen.
Claim 7
Dependent Claim
13 words
A process according to claim 5 in which the first component is nitrogen.
Claim 8
Dependent Claim
13 words
A process according to claim 1 in which the atmosphere comprises forming gas.
Claim 9
Dependent Claim
130 words
A process for improving the performance of a heterojunction photovoltaic device, comprising the steps of fabricating a device to include a heterojunction between regions of InP and CdS, said device to be without an ohmic contact to the CdS, placing the device in an apparatus which can be temperature controlled and through which a gas ambient can be flowed, controlling the temperature of said apparatus and said device to be in the range between approximately 400° centigrade and approximately 600° centigrade, flowing non-oxidizing gas atmosphere of an otherwise substantially inert nature through said apparatus over said device, and removing said device from said apparatus after the continuation of said controlling and flowing steps for about 10 minutes to several hours in inverse dependance upon the temperature of said controlling step.
Claim 10
Dependent Claim
130 words
A process for improving the performance of a heterojunction photovoltaic device, comprising the steps of fabricating a device to include a heterojunction between regions of InP and CdS, said device to be without an ohmic contact to the CdS, placing the device in an apparatus which can be temperature controlled and through which a gas ambient can be flowed, controlling the temperature of said apparatus and said device to be in the range between approximately 400° centigrade and approximately 600° centigrade, flowing non-oxidizing gas atmosphere of an otherwise substantially inert nature through said apparatus over said device, and removing said device from said apparatus after the continuation of said controlling and flowing steps for about 10 minutes to several hours in inverse dependance upon the temperature of said controlling step.
Claim 11
Dependent Claim
38 words
A process according to claim 8 in which the controlling step controls the temperature to be between about 550° centigrade and about 600° centigrade, and in which the device is removed after about 15 minutes in said apparatus.
Claim 12
Dependent Claim
20 words
A process according to claim 8 including an additional subsequent step of supplying an ohmic contact to the CdS region.
References Cited (Backward Citations)
US3492167A
Cited
US3888697A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1979-10-26 | 1980-04-26 | 1980-10-26 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1983-10-26 | 1984-04-26 | 1984-10-26 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1987-10-26 | 1988-04-26 | 1988-10-26 | $7700.00 | Window Closed / Lapsed |