Method of preparing polyvinyl alcohol fibers having improved properties
Assignee: Kuraray Co Ltd
•
Filing: 1973-04-11
•
Granted: 1976-10-19
•
Expires: 1993-04-11
Abstract
Abstract Disclosed is a method for preparing polyvinyl alcohol fibers which comprises spinning an aqueous solution of polyvinyl alcohol containing boric acid or a borate and from about 0.01-5 weight per cent based on said polyvinyl alcohol of an additive comprising an amino acid, an amine, salicylic acid and derivatives thereof or a derivative of pyridine into an alkaline coagulation bath, and subsequently treating the resultant spun fiber by roller drawing, neutralizing with acid, wet hot drawing, washing with water, drying and dry hot drawing.
Inventors
- 👤 Akio Mizobe
- 👤 Tomoo Saheki
- 👤 Shigekazu Kobayashi
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-04 22:41
CPC Classifications
D; D01; D01F; D01F6/00; D01F6/02; D01F6/14; C; C08; C08F; C08F8/00; D01F1/00; D01F1/02; D01F1/10
Claims Analysis
Total Claims: 9
Claim 1
Independent Claim
132 words
In a method for preparing a polyvinyl alcohol fiber which comprises: 1. wet-spinning an aqueous spinning solution of polyvinyl alcohol containing boric acid or a borate into an alkaline coagulating bath; 2. roller drawing the resulting fiber; 3. neutralizing the resulting drawn fiber; 4. wet hot drawing the fiber produced in Step (3); 5. washing the wet hot drawn fiber with water; and 6. dry hot drawing the water-washed fiber, the improvement comprising improving the spinnability of said spinning solution and producing a polyvinyl alcohol fiber having improved tenacity and initial modulus by wet-spinning an aqueous spinning solution which consists essentially of, in addition to said polyvinyl alcohol and said boric acid or borate, from 0.01 to 5 weight percent, based on the weight of said polyvinyl alcohol, of an amino acid.
Claim 2
Dependent Claim
132 words
In a method for preparing a polyvinyl alcohol fiber which comprises: 1. wet-spinning an aqueous spinning solution of polyvinyl alcohol containing boric acid or a borate into an alkaline coagulating bath; 2. roller drawing the resulting fiber; 3. neutralizing the resulting drawn fiber; 4. wet hot drawing the fiber produced in Step (3); 5. washing the wet hot drawn fiber with water; and 6. dry hot drawing the water-washed fiber, the improvement comprising improving the spinnability of said spinning solution and producing a polyvinyl alcohol fiber having improved tenacity and initial modulus by wet-spinning an aqueous spinning solution which consists essentially of, in addition to said polyvinyl alcohol and said boric acid or borate, from 0.01 to 5 weight percent, based on the weight of said polyvinyl alcohol, of an amino acid.
Claim 3
Dependent Claim
30 words
The method as defined by claim 1 wherein said polyvinyl alcohol has a degree of polymerization greater than 500 and a degree of saponification of greater than 95 mole percent.
Claim 4
Dependent Claim
61 words
The method as defined by claim 1 wherein the concentration, in said spinning solution, of said polyvinyl alcohol is from 10 to 30 percent by weight, wherein the concentration, in said spinning solution, of said boric acid or said borate is from 0.5 to 5 percent by weight, and wherein the pH of said spinning solution is from 3.5 to 7.
Claim 5
Dependent Claim
37 words
The method as defined by claim 3 wherein said alkaline coagulating bath comprises an aqueous solution containing from 5 to 200 g/l of caustic alkali and from 100 g/l to the saturating concentration of a dehydration salt.
Claim 6
Dependent Claim
42 words
The method as defined by claim 4 wherein said caustic alkali is selected from the group consisting of sodium hydroxide and potassium hydroxide, and wherein said dehydration salt is selected from the group consisting of sodium sulfate, ammonium sulfate and sodium carbonate.
Claim 7
Dependent Claim
15 words
The method as defined by claim 1, wherein said amino acid is an aminopolycarboxylic acid.
Claim 8
Dependent Claim
65 words
The method as defined by claim 6, wherein said aminopolycarboxylic acid is selected from the group consisting of ethylenediamine-tetraacetic acid and the sodium and potassium salts thereof, nitrilo-triacetic acid and the sodium and potassium salts thereof, trimethylene diamine-tetraacetic acid and the sodium and potassium salts thereof, methylamine-diacetic acid and the sodium and potassium salts thereof, and N-cyclohexylethylenediamine-triacetic acid and the sodium and potassium salts thereof.
Claim 9
Dependent Claim
36 words
The method as defined in claim 1 wherein said amino acid is present in said spinning solution in an amount of from 0.01 to 1.0 percent by weight based on the weight of said polyvinyl alcohol.
References Cited (Backward Citations)
US2345570A
Cited
US2878208A
Cited
US2962476A
Cited
US2888318A
Cited
US3063787A
Cited
US3660556A
Cited
US3776994A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1979-10-19 | 1980-04-19 | 1980-10-19 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1983-10-19 | 1984-04-19 | 1984-10-19 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1987-10-19 | 1988-04-19 | 1988-10-19 | $7700.00 | Window Closed / Lapsed |