Carbon dioxide and excess water treatment of polymer stabilized with phosphite and glycine
Assignee: Phillips Petroleum Co
•
Filing: 1975-08-14
•
Granted: 1976-10-19
•
Expires: 1995-08-14
Abstract
Abstract The effluent from a lithium initiated polmerization, wherein a coupling agent is utilized to join two or more polymer molecules together, with the resulting generation of LiO--, LiS--, or ##EQU1## groups is treated with carbon dioxide and an excess of water and thereafter stabilized with an organic phosphite and a glycine in combination with a hindered phenol.
Inventors
- 👤 Alonzo G. Kitchen
- 👤 Frank J. Szalla
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-24 05:56
CPC Classifications
C; C08; C08F; C08F2/00; C08F2/38; C08F2/40; C08F2/42; C08K; C08K5/00; C08K5/49; C08K5/51; C08K5/52; C08K5/524; C08K5/526
Claims Analysis
Total Claims: 11
Claim 1
Independent Claim
225 words
A method comprising: adding carbon dioxide and water to a polymer containing effluent from a polymerization reaction wherein at least one monomer is contacted with an organolithium initiator and thereafter the resulting polymer molecules having an active lithium atom on one end are contacted with a coupling agent having at least two reactive groups, which coupling results in the generation of LiO--, LiS--, or LiNH-- groups attached either to said coupling agent or to a 1 to 20 carbon atom radical from said coupling agent, said carbon dioxide being present in an amount within the range of 0.8 to 2 times the stoichiometric amount based on said lithium with said water and carbon dioxide being present in a molar ratio within the range of 10:1 to 500:1 mols of water per mol of carbon dioxide, said polymer being stabilized with 0.2 to 5 weight percent based on the weight of said polymer of a mixture of a phosphite having the formula ##SPC2## and a glycine having the formula ##EQU2## wherein R is a C 14 , C 16 or C 18 alkyl radical and wherein said glycine is present in an amount within the range of 1 to 50 weight percent based on the weight of said phosphite, and 0.05 to 5 weight percent of a hindered phenol based on the weight of said polymer.
Claim 2
Independent Claim
225 words
A method comprising: adding carbon dioxide and water to a polymer containing effluent from a polymerization reaction wherein at least one monomer is contacted with an organolithium initiator and thereafter the resulting polymer molecules having an active lithium atom on one end are contacted with a coupling agent having at least two reactive groups, which coupling results in the generation of LiO--, LiS--, or LiNH-- groups attached either to said coupling agent or to a 1 to 20 carbon atom radical from said coupling agent, said carbon dioxide being present in an amount within the range of 0.8 to 2 times the stoichiometric amount based on said lithium with said water and carbon dioxide being present in a molar ratio within the range of 10:1 to 500:1 mols of water per mol of carbon dioxide, said polymer being stabilized with 0.2 to 5 weight percent based on the weight of said polymer of a mixture of a phosphite having the formula ##SPC2## and a glycine having the formula ##EQU2## wherein R is a C 14 , C 16 or C 18 alkyl radical and wherein said glycine is present in an amount within the range of 1 to 50 weight percent based on the weight of said phosphite, and 0.05 to 5 weight percent of a hindered phenol based on the weight of said polymer.
Claim 3
Dependent Claim
22 words
A method according to claim 1 wherein said ratio of water to carbon dioxide is within the range of 25:1 to 250:1.
Claim 4
Dependent Claim
12 words
A method according to claim 1 wherein said hindered phenol is 2,6-di-tert-butyl-4-methylphenol.
Claim 5
Dependent Claim
54 words
A method according to claim 3 wherein said mixture is present in an amount within the range of 0.5 to 2 weight percent based on the weight of said polymer and said 2,6-di-tert-butyl-4-methylphenol is present in an amount within the range of 0.1 to 1 weight percent based on the weight of said polymer.
Claim 6
Dependent Claim
30 words
A method according to claim 3 wherein said glycine is present in an amount within the range of 25 to 37 weight percent based on the weight of said phosphite.
Claim 7
Dependent Claim
16 words
A method according to claim 3 wherein said polymer is a polymer of butadiene and styrene.
Claim 8
Dependent Claim
43 words
A method according to claim 6 wherein said polymer is produced by the sequential addition of styrene and then butadiene, said styrene being present in an amount within the range of 70 to 95 weight percent so as to give a resinous polymer.
Claim 9
Dependent Claim
14 words
A method according to claim 1 wherein said phosphite is 2-t-butyl-α-(3-t-butyl-4-hydroxyphenyl)-p-cumenyl bis (p-nonylphenyl) phosphite.
Claim 10
Dependent Claim
12 words
A method according to claim 1 wherein said glycine is N-octadecyl-N'-(carboxymethyl)-trimethylene diglycine.
Claim 11
Dependent Claim
14 words
A method according to claim 9 wherein said phosphite is 2-t-butyl-α-(3-t-butyl-4-hydroxyphenyl)-p-cumenyl bis (p-nonylphenyl) phosphite.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1979-10-19 | 1980-04-19 | 1980-10-19 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1983-10-19 | 1984-04-19 | 1984-10-19 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1987-10-19 | 1988-04-19 | 1988-10-19 | $7700.00 | Window Closed / Lapsed |