US3986901A
Expired / Lapsed
US
⏱️ 0.0 years remaining
Controlled catalyst for manufacturing magnetic alloy particles having selective coercivity
Assignee: International Business Machines Corp
•
Filing: 1975-04-30
•
Granted: 1976-10-19
•
Expires: 1995-04-30
Abstract
Abstract This invention provides techniques for producing unique cobalt-phosphorus (Co-P) particles. The Co-P particles produced by this technique are novel as to both size and morphology. Their size is uniformly less than about 300 A, with average sizes being about 150 A. This is substantially smaller than Co-P particles previously known or reported in the literature. Their morphology is unique, as shown by x-ray and electron diffraction, in that they are amorphous. All known prior art Co-P particles have been crystalline. In addition, these Co-P particles have the capability of being manufactured with selectively controlled magnetic coercivity. The new reaction system utilized to produce these unique materials provides a substantial departure from art known systems. The reaction system is notable for changes in materials and procedures previously considered important or indispensable to the production of magnetic Co-P and for its ability to control the coercivity of the particles produced over a broad range as an inverse function of the concentration of the palladium cation (Pd + + ) catalyst used. More specifically, the reaction system is extremely novel in terms of the fact that: (1) it is initiated at ambient rather than elevated temperatures; (2) excludes all complexing agents, both strong and weak, from the reaction system; (3) excludes magnetic fields of every form and magnitude during the reaction; and (4) can be utilized to provide Co-P particles of selected coercivity in the range of about 500 to 1500 oersteds as an inverse function of the Pd cation catalyst concentration utilized.
Inventors
- 👤 Franklin T. Plante
- 👤 Raymond F. Sankuer
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-27 11:20
CPC Classifications
H; H01; H01F; H01F1/00; H01F1/01; H01F1/03; H01F1/032; H01F1/04; H01F1/06; B; B22; B22F; B22F9/00; B22F9/002; B22F9/004; B22F9/16; B22F9/18; B22F9/24; B22F2998/00
Claims Analysis
Total Claims: 11
Claim 1
Independent Claim
163 words
A method for preparing finely divided amorphous magnetic cobalt-phosphorus alloy particles about 300 A or less in diameter with average size of about 150 A, said process comprising the steps of preparing an aqueous solution consisting essentially of reducible cobalt cations, hypophosphite anions as a reducing agent, a non-complexing base as a source of hydroxide anions to render the solution basic, and a source of reducible palladium cations to provide catalystic nucleating sites for cobalt-phosphorus particle formation; wherein the improvement comprises initiating an oxidation-reduction reaction to produce finely divided amorphous magnetic cobalt-phosphorus alloy particles about 300 A or less in diameter with an average size of about 150 A while excluding both strong and weak cobalt cation complexing agents from said solution substantially excluding magnetic fields of all types and magnitudes from affecting the solution during the reaction, and maintaining said solution at ambient temperatures in the range of about 15° C to about 35° C at the time the reaction is initiated.
Claim 2
Independent Claim
163 words
A method for preparing finely divided amorphous magnetic cobalt-phosphorus alloy particles about 300 A or less in diameter with average size of about 150 A, said process comprising the steps of preparing an aqueous solution consisting essentially of reducible cobalt cations, hypophosphite anions as a reducing agent, a non-complexing base as a source of hydroxide anions to render the solution basic, and a source of reducible palladium cations to provide catalystic nucleating sites for cobalt-phosphorus particle formation; wherein the improvement comprises initiating an oxidation-reduction reaction to produce finely divided amorphous magnetic cobalt-phosphorus alloy particles about 300 A or less in diameter with an average size of about 150 A while excluding both strong and weak cobalt cation complexing agents from said solution substantially excluding magnetic fields of all types and magnitudes from affecting the solution during the reaction, and maintaining said solution at ambient temperatures in the range of about 15° C to about 35° C at the time the reaction is initiated.
Claim 3
Dependent Claim
80 words
The method of claim 1 wherein the cobalt cation concentration is in the range of about 1.9 × 10 - 2 M. to 7.6 ×10 - 2 M., the concentration of hypophosphite anion is in the range of about 0.10M. to 0.40M., the palladium concentration is in the range of about 3.0 × 10 - 6 M. to 3.1 × 10 - 3 M., and the pH of the solution is in the range of about 7.1 to about 13.
Claim 4
Independent Claim
176 words
A method for preparing finely divided amorphous magnetic cobalt-phosphorus alloy particles having selected coercivity, said process comprising preparing an aqueous solution at ambient temperatures consisting essentially of reducible cobalt cations, hypophosphite anions as a reducing agent, a non-complexing base as a source of hydroxide anions to render the solution basic, and palladium cations to provide nucleating sites for cobalt-phosphorus particle formation; wherein the improvement comprises maintaining the solution at ambient temperatures in the range of about 15° C to about 35° C while excluding both strong and weak cobalt cation complexing agents and magnetic fields of every type and magnitude; selecting the concentration of palladium cations in the bath in the range of about 7.0 × 10 - 4 M. to 9.0 × 10 - 2 M.; and then initiating an oxidation-reduction reaction to produce finely divided magnetic cobalt-phosphorus alloy particles by reduction of the cobalt cations by the hypophosphite anions, the coercivity of said particles being inversely and functionally dependent on the palladium cation concentration of the solution at the time the reaction is initiated.
Claim 5
Independent Claim
176 words
A method for preparing finely divided amorphous magnetic cobalt-phosphorus alloy particles having selected coercivity, said process comprising preparing an aqueous solution at ambient temperatures consisting essentially of reducible cobalt cations, hypophosphite anions as a reducing agent, a non-complexing base as a source of hydroxide anions to render the solution basic, and palladium cations to provide nucleating sites for cobalt-phosphorus particle formation; wherein the improvement comprises maintaining the solution at ambient temperatures in the range of about 15° C to about 35° C while excluding both strong and weak cobalt cation complexing agents and magnetic fields of every type and magnitude; selecting the concentration of palladium cations in the bath in the range of about 7.0 × 10 - 4 M. to 9.0 × 10 - 2 M.; and then initiating an oxidation-reduction reaction to produce finely divided magnetic cobalt-phosphorus alloy particles by reduction of the cobalt cations by the hypophosphite anions, the coercivity of said particles being inversely and functionally dependent on the palladium cation concentration of the solution at the time the reaction is initiated.
Claim 6
Independent Claim
202 words
A method for preparing finely divided amorphous magnetic cobalt-phosphorus alloy particles having selected coercivity, said process comprising preparing an aqueous solution at ambient temperatures consisting essentially of reducible cobalt cations, hypophosphite anions as a reducing agent, a noncomplexing base as a source of hydroxide anions to render the solution basic, and palladium cations to provide nucleating sites for cobaltphosphorus particle formation; wherein the improvement comprises maintaining the solution at ambient temperatures in the range of about 15° C to about 35° C while excluding both strong and weak cobalt cation complexing agents and magnetic fields of every type and magnitude; selecting the concentration of palladium cations in the range of about 7.0 × 10 - 4 M. to 9.0 × 10 - 2 M.; and then initiating an oxidation-reduction reaction to produce finely divided magnetic cobaltphosphorus alloy particles by reduction of the cobalt cation by the hypophosphite anions, said particles having controlled coercivity in the range of about 500 to 1500 oersteds, said coercivity being inversely and functionally dependent on the palladium cation concentration in the catalyst solution at the time the reaction is initiated, substantially as set forth in curves A, B, C, D and E of FIGS. 1 and 2.
Claim 7
Independent Claim
202 words
A method for preparing finely divided amorphous magnetic cobalt-phosphorus alloy particles having selected coercivity, said process comprising preparing an aqueous solution at ambient temperatures consisting essentially of reducible cobalt cations, hypophosphite anions as a reducing agent, a noncomplexing base as a source of hydroxide anions to render the solution basic, and palladium cations to provide nucleating sites for cobaltphosphorus particle formation; wherein the improvement comprises maintaining the solution at ambient temperatures in the range of about 15° C to about 35° C while excluding both strong and weak cobalt cation complexing agents and magnetic fields of every type and magnitude; selecting the concentration of palladium cations in the range of about 7.0 × 10 - 4 M. to 9.0 × 10 - 2 M.; and then initiating an oxidation-reduction reaction to produce finely divided magnetic cobaltphosphorus alloy particles by reduction of the cobalt cation by the hypophosphite anions, said particles having controlled coercivity in the range of about 500 to 1500 oersteds, said coercivity being inversely and functionally dependent on the palladium cation concentration in the catalyst solution at the time the reaction is initiated, substantially as set forth in curves A, B, C, D and E of FIGS. 1 and 2.
Claim 8
Dependent Claim
53 words
A method for making a magnetic coating composition for use in the manufacture of magnetic recording media consisting of the steps of: bringing together particles produced in accordance with the process of claim 1 with an organic resin binder and solvent therefor; and then mixing said particles and resin to produce a mixture.
Claim 9
Dependent Claim
10 words
The method of claim 5 wherein said binder includes polyurethane.
Claim 10
Dependent Claim
9 words
The product produced by the process of claim 1.
Claim 11
Dependent Claim
9 words
The product produced by the process of claim 5.
References Cited (Backward Citations)
US3282723A
Cited
US3138476A
Cited
US3525635A
Cited
US3494760A
Cited
US3702263A
Cited
US3756866A
Cited
US3672867A
Cited
US3726664A
Cited
US3856513A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1979-10-19 | 1980-04-19 | 1980-10-19 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1983-10-19 | 1984-04-19 | 1984-10-19 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1987-10-19 | 1988-04-19 | 1988-10-19 | $7700.00 | Window Closed / Lapsed |