US3986653A
Expired / Lapsed
US
⏱️ 0.0 years remaining
Method for coating bonding tools and product
Assignee: Tribotech Inc
•
Filing: 1974-09-03
•
Granted: 1976-10-19
•
Expires: 1994-09-03
Abstract
Abstract A method for the electrodeposition of osmium, ruthenium or their alloys from alkali metal salts of the same in a nonaqueous solvent capable of permitting dissociation of the salt and having low surface tension (e.g., methanol or dimethyl formamide) or mixtures. A silicone layer chemically bonded to the surface of said electrodeposited layer. Also, a bonding tool having a tip coated by either of the above electrodeposited layer or the silicone layer, or both.
Inventors
- 👤 Denis K. Gilding
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-04 21:18
CPC Classifications
B; B23; B23K; B23K20/00; B23K20/002; B23K20/004; B23K20/005; C; C25; C25D; C25D3/00; C25D3/02; C25D3/50; C25D3/56; C25D3/567; B23K2101/00; B23K2101/36; H; H10; H10W; H10W72/00; H10W72/071; H10W72/0711; H10W72/07141; H10W72/075; H10W72/07531; H10W72/07532; H10W72/07533; H10W72/50; H10W72/551; H10W72/552; H10W72/5522; H10W72/5524
Claims Analysis
Total Claims: 33
Claim 1
Independent Claim
85 words
A method for the electrodeposition of the hard metal osmium, or alloys thereof comprising the steps of forming an electrolyte solution consisting essentially of a dissociated alkali metal salt of a complex of osmium as the anion in a nonaqueous organic solvent capable of dissolving said salt in ionized form and electrolytically depositing the hard metal from the solution onto a plating substrate comprising the cathode, said organic solvent consisting essentially of a major portion of aprotic solvent and a minor portion of lower alcohol.
Claim 2
Independent Claim
85 words
A method for the electrodeposition of the hard metal osmium, or alloys thereof comprising the steps of forming an electrolyte solution consisting essentially of a dissociated alkali metal salt of a complex of osmium as the anion in a nonaqueous organic solvent capable of dissolving said salt in ionized form and electrolytically depositing the hard metal from the solution onto a plating substrate comprising the cathode, said organic solvent consisting essentially of a major portion of aprotic solvent and a minor portion of lower alcohol.
Claim 3
Dependent Claim
48 words
A method as in claim 1 in which the substrate consists essentially of a metal-containing material selected from the group consisting of tungsten, tungsten carbide, tungsten steel, tool steel, rhenium, platinum, rhodium, molybdenum, titanium, hafnium, zirconium, tantalum, gold, silver, nickel, cobalt, copper, niobium, aluminum, alumina, and alloys thereof.
Claim 4
Dependent Claim
32 words
A method as in claim 1 in which the hard metal is deposited as an alloy with a compatible metal selected from the group consisting of rhodium, iridium, palladium, platinum and gold.
Claim 5
Dependent Claim
20 words
A method as in claim 1 in which the hard metal complex of the alkali metal salt is osmium pentoxide.
Claim 6
Dependent Claim
22 words
A method as in claim 1 in which the organic solvent is characterized by a surface tension substantially below that of water.
Claim 7
Dependent Claim
21 words
A method as in claim 1 in which the lower alcohols are selected from the group consisting of methanol and ethanol.
Claim 8
Dependent Claim
29 words
A method as in claim 1 in which the aprotic solvent is selected from the group consisting of dimethyl formamide, dimethyl sulphoxide, dimethyl acetamide, and combinations of the same.
Claim 9
Dependent Claim
23 words
A method as in claim 1 in which the alkali metal salt is selected from the group consisting of sodium, lithium and potassium.
Claim 10
Dependent Claim
27 words
A method as in claim 1 in which the alkali metal salt is formed by mixing the alkali metal with an ionizable salt of the hard metal.
Claim 11
Dependent Claim
42 words
A method as in claim 9 in which the alkali metal salt is formed in a portion of the organic solvent comprising a lower alcohol, and thereafter the remainder of the organic solvent comprising aprotic solvent is added prior to electrolytic deposition.
Claim 12
Dependent Claim
14 words
A method as in claim 9 in which the ionizable salt comprises osmium tetroxide.
Claim 13
Dependent Claim
16 words
A method as in claim 3 in which the alloy comprises said hard metal and platinum.
Claim 14
Dependent Claim
60 words
A method as in claim 1 in which the plating substrate is the surface of a microstructural bonding tool for holding a bonding wire against a surface to which the wire is to be bonded during application of energy thereto, which tool comprises an elongate tool body having a wire guide opening and a bonding surface at the end thereof.
Claim 15
Dependent Claim
23 words
A method as in claim 1 in which a silicone layer is deposited onto the surface of the electrolytically deposited hard metal substrate.
Claim 16
Dependent Claim
83 words
A method as in claim 14 in which the silicone layer is formed by treating the surface of the hard metal substrate to form pendant groups of the general formula --OM wherein M is hydrogen or a cation having a valence of one and contacting the treated surface with a silane of the general formula (R) n Si(X) 4 -n wherein n varies from 0 to 3, R is an aliphatic or aromatic group and X is a halogen group or alkoxy radical.
Claim 17
Dependent Claim
23 words
A method as in claim 15 in which the --OM groups are formed by electrolytically reacting the hard metal surface with a base.
Claim 18
Dependent Claim
25 words
A method as in claim 16 in which the base-reacted surface is washed with an acid to form hydroxyl groups before contact with the silane.
Claim 19
Dependent Claim
26 words
A method as in claim 15 in which the silane is selected from the group consisting of dimethyl dichlorosilane, dimethyl diethoxysilane, trimethyl chlorosilane, and trimethyl ethoxysilane.
Claim 20
Dependent Claim
50 words
An electrolytic solution for depositing the hard metal osmium onto a substrate, said solution consisting essentially of a dissociated alkali metal salt of an oxide complex of osmium in a nonaqueous organic solvent consisting essentially of a major portion of aprotic solvent and a minor portion of a lower alcohol.
Claim 21
Dependent Claim
50 words
An electrolytic solution for depositing the hard metal osmium onto a substrate, said solution consisting essentially of a dissociated alkali metal salt of an oxide complex of osmium in a nonaqueous organic solvent consisting essentially of a major portion of aprotic solvent and a minor portion of a lower alcohol.
Claim 22
Dependent Claim
36 words
An electrolytic solution as in claim 19 together with a dissociated alkali metal salt of a complex of a hard metal compatible alloying metal selected from the group consisting of rhodium, iridium, palladium, platinum and gold.
Claim 23
Dependent Claim
26 words
A solution as in claim 19 in which the hard metal is osmium and the hard metal ion of the alkali metal salt is osmium pentoxide.
Claim 24
Dependent Claim
23 words
A solution as in claim 19 in which the organic solvent is characterized by a surface tension substantially lower than that of water.
Claim 25
Dependent Claim
25 words
A solution as in claim 19 in which the organic solvent is selected from the group consisting of lower alcohols, aprotic solvents and mixtures thereof.
Claim 26
Dependent Claim
29 words
A solution as in claim 19 in which the aprotic solvent is selected from the group consisting of dimethyl formamide, dimethyl sulphoxide, dimethyl acetamide, and combinations of the same.
Claim 27
Dependent Claim
10 words
An electroplated substrate formed by the process of claim 1.
Claim 28
Dependent Claim
79 words
In a microstructural bonding tool for holding a bonding wire against a surface to which the wire is to be bonded during application of energy thereto, which tool comprises an elongate tool body having wire guide means and a bonding surface at the end thereof, a layer on said tool of electrodeposited hard metal selected from the group consisting of osmium, ruthenium or alloys of the same, said layer being characterized by a grain size less than 15 microinches.
Claim 29
Dependent Claim
79 words
In a microstructural bonding tool for holding a bonding wire against a surface to which the wire is to be bonded during application of energy thereto, which tool comprises an elongate tool body having wire guide means and a bonding surface at the end thereof, a layer on said tool of electrodeposited hard metal selected from the group consisting of osmium, ruthenium or alloys of the same, said layer being characterized by a grain size less than 15 microinches.
Claim 30
Dependent Claim
33 words
An article as in claim 26 in which the layer is an alloy of the hard metal with a compatible metal selected from the group consisting of rhodium, iridium, palladium, platinum and gold.
Claim 31
Dependent Claim
16 words
An article as in claim 26 in which the layer is an alloy in intimate dispersion.
Claim 32
Dependent Claim
14 words
An article as in claim 28 in which the layer is an osmium-platinum alloy.
Claim 33
Dependent Claim
20 words
An article as in claim 26 in which a silicone layer is bonded to the electrodeposited hard metal layer surface.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1979-10-19 | 1980-04-19 | 1980-10-19 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1983-10-19 | 1984-04-19 | 1984-10-19 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1987-10-19 | 1988-04-19 | 1988-10-19 | $7700.00 | Window Closed / Lapsed |