Polyacrylonitrile fibers having a natural crimp and process for producing the same
Assignee: Akzo Belge SA
•
Filing: 1973-03-05
•
Granted: 1976-10-05
•
Expires: 1993-03-05
Abstract
Abstract A naturally crimped polyacrylonitrile fiber having an asymmetrical cross section, the cross section having at least two large oblong lobes, the angle between at least two of these lobes being less than 90 DEG , the fiber having an outer structure which has a relatively high density and has a variable thickness, this outer structure enclosing an inner structure which is porous and less dense than the outer structure.
Inventors
- 👤 Henri-Albert Mommaerts
- 👤 Andre-Edgard Dubois
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-02 09:09
CPC Classifications
D; D01; D01F; D01F6/00; D01F6/02; D01F6/18; D01F6/28; D01F6/38; D01F6/44; D01F6/54; Y; Y10; Y10T; Y10T428/00; Y10T428/29; Y10T428/2913; Y10T428/2922; Y10T428/2933; Y10T428/2935; Y10T428/2964; Y10T428/2967; Y10T428/2973; Y10T428/2975; Y10T428/2978
Claims Analysis
Total Claims: 5
Claim 1
Independent Claim
138 words
A method for producing crimped polyacrylonitrile fibers comprising spinning a polymer solution of polyacrylonitrile in a solvent for said polyacrylonitrile into a cold bath to form partially coagulated filaments of said polyacrylonitrile, said bath comprising 1,1,1-trichlorethane or a mixture of 1,1,1-trichlorethane with less than 25 percent by weight of a solvent for said polyacrylonitrile, the exposure of said polyacrylonitrile in said cold bath being for a period of less than two minutes; drawing said partially coagulated filaments above 200 percent in a hot bath, said hot bath having a temperature between 60°C and the boiling point of said bath, said hot bath comprising water or mixtures of water with less than 75 percent by weight of a solvent for said polyacrylonitrile; washing said drawn and coagulated filaments; and heat treating said filaments in a free state without tension.
Claim 2
Independent Claim
138 words
A method for producing crimped polyacrylonitrile fibers comprising spinning a polymer solution of polyacrylonitrile in a solvent for said polyacrylonitrile into a cold bath to form partially coagulated filaments of said polyacrylonitrile, said bath comprising 1,1,1-trichlorethane or a mixture of 1,1,1-trichlorethane with less than 25 percent by weight of a solvent for said polyacrylonitrile, the exposure of said polyacrylonitrile in said cold bath being for a period of less than two minutes; drawing said partially coagulated filaments above 200 percent in a hot bath, said hot bath having a temperature between 60°C and the boiling point of said bath, said hot bath comprising water or mixtures of water with less than 75 percent by weight of a solvent for said polyacrylonitrile; washing said drawn and coagulated filaments; and heat treating said filaments in a free state without tension.
Claim 3
Dependent Claim
60 words
The method of claim 1 wherein the temperature of said first bath is less than 25°C and wherein the composition of said bath comprises 1,1,1-trichlorethane or mixtures of 1,1,1-trichlorethane with less than 15 percent of said solvent for polyacrylonitrile; wherein said exposure time is less than 1 minute, the temperature of the hot bath being between 80°C and 100° C.
Claim 4
Dependent Claim
18 words
The method of claim 1 wherein said filament is initially dried at a temperature of less than 60°C.
Claim 5
Dependent Claim
21 words
The method of claim 1 wherein said solvent is selected from the group consisting of dimethylformamide, dimethylacetamide, dimethylsufoxide, and ethylene carbonate.
References Cited (Backward Citations)
GB711344A
Cited
US3052643A
Cited
FR1271610A
Cited
FR1334857A
Cited
GB1032992A
Cited
GB1064718A
Cited
GB1106581A
Cited
US3577499A
Cited
US3655857A
Cited
US3706828A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1979-10-05 | 1980-04-05 | 1980-10-05 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1983-10-05 | 1984-04-05 | 1984-10-05 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1987-10-05 | 1988-04-05 | 1988-10-05 | $7700.00 | Window Closed / Lapsed |